Concrete curing compound and preparation method thereof

A technology of concrete curing agent and dispersing agent, applied in the field of building material additives, can solve the problems of poor practicability, slow film-forming speed and low water retention rate, and achieve the effects of long curing time, fast film-forming speed and high water retention rate

Inactive Publication Date: 2015-01-21
HEBEI ZHUSHENG BUILDING MATERIALS SCI & TECH DEV
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention proposes a concrete curing agent and its preparation method, which solves the problems of slow film-forming speed, poor practicability and low water retention rate of concrete curing agents in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A concrete curing agent, which is made of the following raw materials in weight ratio: 8 kg of paraffin wax, 5 kg of nano-scale calcium carbonate, 1 kg of film-forming aid, 1 kg of sorbitan monofatty acid ester, and 1 kg of triethanolamine , 0.2 kg of dispersant and 85 kg of water.

[0027] Wherein the particle size of nano-scale calcium carbonate is 0.1nm-100nm; the film-forming aid is ethylene glycol or ethylene glycol butyl ether; the dispersant is polyhydroxy acid salt, sulfamate or naphthalene sulfonate.

[0028] The above-mentioned nano-scale calcium carbonate filler can block the capillary channels of concrete and hinder the volatilization of water. Film-forming aids have the characteristics of high adhesion, waterproof, wear-resistant, high temperature resistance and anti-sticking.

[0029] The preparation method of above-mentioned concrete curing agent, its concrete steps are as follows:

[0030] (1) Add paraffin, sorbitan monofatty acid ester and triethanola...

Embodiment 2

[0035] A concrete curing agent, which is made of the following raw materials in weight ratio: 12 kilograms of paraffin wax, 20 kilograms of nano-scale calcium carbonate, 7 kilograms of film-forming aids, 3 kilograms of sorbitan monofatty acid ester, and 3 kilograms of triethanolamine , 1 kg of dispersant and 100 kg of water.

[0036] Wherein the particle size of nano-scale calcium carbonate is 0.1nm-100nm; the film-forming aid is ethylene glycol or ethylene glycol butyl ether; the dispersant is polyhydroxy acid salt, sulfamate or naphthalene sulfonate.

[0037] The above-mentioned nano-scale calcium carbonate filler can block the capillary channels of concrete and hinder the volatilization of water. Film-forming aids have the characteristics of high adhesion, waterproof, wear-resistant, high temperature resistance and anti-sticking.

[0038] The preparation method of above-mentioned concrete curing agent, its concrete steps are as follows:

[0039] (1) Add paraffin, sorbitan...

Embodiment 3

[0044] A concrete curing agent, which is made of the following raw materials in weight ratio: 10 kilograms of paraffin wax, 12.5 kilograms of nano-scale calcium carbonate, 4 kilograms of film-forming aids, 2 kilograms of sorbitan monofatty acid ester, and 2 kilograms of triethanolamine , 0.6 kg of dispersant and 92.5 kg of water.

[0045] Wherein the particle size of nano-scale calcium carbonate is 0.1nm-100nm; the film-forming aid is ethylene glycol or ethylene glycol butyl ether; the dispersant is polyhydroxy acid salt, sulfamate or naphthalene sulfonate.

[0046] The above-mentioned nano-scale calcium carbonate filler can block the capillary channels of concrete and hinder the volatilization of water. Film-forming aids have the characteristics of high adhesion, waterproof, wear-resistant, high temperature resistance and anti-sticking.

[0047] The preparation method of above-mentioned concrete curing agent, its concrete steps are as follows:

[0048] (1) Add paraffin, sor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a concrete curing compound. The concrete curing compound is prepared from the following raw materials in parts by weight: 8-12 parts of paraffin, 5-20 parts of nano-sized calcium carbonate, 1-7 parts of a coalescing agent, 1-3 parts of sorbitan fatty acid ester, 1-3 parts of triethanolamine, 0.2-1 part of a dispersing agent and 85-100 parts of water. The concrete curing compound has the beneficial effects that the concrete curing compound provided by the invention is high in film-forming speed, high in water-retention rate, long in curing time and convenient to construct, can be normally used under the condition of relatively low external environment temperature; the water-retention rate can reach over 90%; and the concrete curing compound can be directly used without dilution, can be sprayed, brushed and rolled, and is high in compressive strength rate, non-toxic, tasteless, non-inflammable, and free of corrosivity on concrete.

Description

technical field [0001] The invention relates to the technical field of building material additives, in particular to a concrete curing agent and a preparation method thereof. Background technique [0002] Concrete needs a lot of water in the hydration process, and the lack of water will delay or even stop the hydration process. There is a certain amount of water in the concrete mixture, and the mixing water is even greater than the water required for cement hydration. However, due to the There are a large number of capillary channels in the concrete, and the water is easy to lose. At the same time, the evaporation of water and the water absorption of the base layer also make the water in the concrete lose quickly. Therefore, to ensure the smooth progress of the concrete hydration process, it must be moisturized and maintained. [0003] Concrete curing agent, also known as concrete curing liquid, is a kind of coating material. When it is sprayed on the concrete surface, it ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B40/04
Inventor 田艳光
Owner HEBEI ZHUSHENG BUILDING MATERIALS SCI & TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com