A technology of electromagnetic shielding and latex paint, applied in the field of latex paint, can solve the problems of high cost of fillers and restrictions on the promotion and use of latex paint, and achieve the effect of simple process, good electromagnetic shielding and low cost

Active Publication Date: 2016-08-24
山东新佳涂料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The commonly used latex paints with electromagnetic shielding properties use metal fillers such as silver and copper. Due to the high cost of fillers, the promotion and use of latex paints with electromagnetic shielding properties is greatly limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of latex paint with electromagnetic shielding performance
  • A kind of latex paint with electromagnetic shielding performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The proportion of raw materials in this embodiment is as follows: epoxy resin: 30 parts; calcium borate: 21 parts; carbon powder: 2.5 parts; polyvinyl alcohol: 0.3 parts; n-butanol: 0.3 parts; Titanium dioxide: 13 parts; water: 30.4 parts.

[0024] The main components of industrial waste calcium borate are boric anhydride and calcium oxide. Boric anhydride, calcium oxide and carbon powder will generate calcium hexaboride and carbon monoxide at high temperature. The synthesis of calcium hexaboride is very sensitive to temperature changes, and the synthesis temperature The range is relatively narrow, and it cannot be synthesized above or below a certain temperature range. After testing, the chemical reaction is the best when the sintering temperature is 1950K and the holding time is 30min.

[0025] Epoxy resin is a kind of polymer material with poor conductivity, and it has almost no shielding effect on electromagnetic waves. The present invention forms a conductive netw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a latex paint with electromagnetic shielding performance, which is characterized in that the formula is as follows: epoxy resin: 29-31 parts; calcium borate: 20-22 parts; carbon powder: 2-3 parts; polyvinyl alcohol: 0.3 n-butanol: 0.3 parts; silane coupling agent: 2.5 parts; nano titanium dioxide: 12-14 parts; water: 30-31 parts. The latex paint prepared by the invention has the advantages of good electromagnetic shielding, low cost and simple process.

Description

technical field [0001] The invention relates to the field of building materials, in particular to an emulsion paint with electromagnetic shielding performance. Background technique [0002] With the rapid development of electronic information technology, electromagnetic wave radiation pollution has become a major public hazard in today's society, and its impact on economic construction, national defense security and social life is becoming more and more serious. Electromagnetic shielding technology is an effective means to deal with electromagnetic radiation pollution. Various electromagnetic shielding materials, especially electromagnetic wave shielding latex paint, have become new materials for electromagnetic environmental pollution protection due to their high cost performance and good applicability. Research and application a hotspot. The commonly used latex paints with electromagnetic shielding properties use metal fillers such as silver and copper. Due to the high co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/02C09D7/12
Inventor 叶长青
Owner 山东新佳涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap