Preparation method of TiO2/porous g-C3N4 composite material

A composite material, g-c3n4 technology, applied in the field of preparation of TiO2/porous g-C3N4 composite material, can solve the problems of weak separation ability of photogenerated carriers, poor photocatalytic activity, limited wide application, etc., to avoid homogeneous phase Precipitation, improving photocatalytic activity, and solving the effect of low quantum efficiency

Inactive Publication Date: 2014-12-17
ZHEJIANG UNIV
View PDF1 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

g-C 3 N 4 It is an organic polymer semiconductor with an energy gap of about 2.7eV. It is simple to prepare and has good chemical stability, but the pure phase g-C 3 N 4 The low specific surface area, weak separation ability of photogenerated carriers, and poor photocatalytic activity limit the wide application of this material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of TiO2/porous g-C3N4 composite material
  • Preparation method of TiO2/porous g-C3N4 composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] TiO 2 / Porous g-C 3 N 4 The preparation method of nanocomposite material, comprises the following steps:

[0020] Step A: Under stirring conditions, H 2 SO 4 The aqueous solution was added dropwise to the melamine aqueous solution to form a white suspension; the precipitate was obtained after stirring at 80°C for 2 hours; the precipitate was filtered, washed three times with distilled water and absolute ethanol, and dried at 60°C for 24 hours to obtain melamine sulfate; put into a corundum boat, followed by sintering in a tube furnace; after cooling to room temperature, the obtained yellow polymer product was ground a little to powdery particles to obtain g-C 3 N 4 particles;

[0021] Among them, H 2 SO 4 The molar concentration of aqueous solution is 0.02mol / L~2mol / L, the molar concentration of melamine aqueous solution is 0.02mol / L~2mol / L, the amount of control reactant makes H 2 SO 4 The molar ratio to melamine is 5:1~0.5:1; the protective atmosphere for s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of semiconductor materials and aims at providing a preparation method of a TiO2 / porous g-C3N4 composite material. The preparation method of the TiO2 / porous g-C3N4 composite material comprises the following steps: dropwise adding H2SO4 aqueous solution into melamine aqueous solution to form a white suspension solution; stirring at the temperature of 80 DEG C for 2 hours to obtain sediment; filtering the sediment and respectively washing the sediment for three times by using distilled water and absolute ethyl alcohol, drying the washed sediment at the temperature of 60 DEG C for 24 hours to obtain melamine sulphate; adding the melamine sulphate into a corundum boat, subsequently sintering the melamine sulphate in a tubular furnace, cooling the melamine sulphate to room temperature and grinding an obtained yellow polymerization product into powder particles to obtain g-C3N4 particles. The preparation method of the TiO2 / porous g-C3N4 composite material has the beneficial effects that the g-C3N4 polymerization temperature is effectively reduced; by virtue of the protonation of the melamine, the polymerization energy of melamine is reduced; the melamine can polymerize at relatively low temperature to generate graphite-like g-C3N4.

Description

technical field [0001] The present invention relates to the field of semiconductor materials, in particular to TiO 2 / Porous g-C 3 N 4 Methods of preparation of composite materials. Background technique [0002] Graphite-like carbon nitride (g-C 3 N 4 ) has shown good application prospects in the fields of solar energy utilization and environmental protection because of its special physical and chemical properties. g-C 3 N 4 It is an organic polymer semiconductor with an energy gap of about 2.7eV. It is simple to prepare and has good chemical stability, but the pure phase g-C 3 N 4 The low specific surface area, weak separation ability of photogenerated charge carriers, and poor photocatalytic activity limit the wide application of this material. At present, there are many methods to improve g-C 3 N 4 The structure and morphology of the base material can be used to improve its photocatalytic performance, such as element doping, porous and nanostructure structure,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24B01J35/04
Inventor 沈建超申乾宏杨辉冯宇蔡奇风
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products