A kind of preparation technology of composite foam cement

A composite foamed cement and preparation process technology, applied in ceramic products, applications, household appliances, etc., can solve the problems of not having the conditions for widespread use in the market, not being suitable for large-scale production, not having market competitiveness, etc. The wall thickness is balanced and controllable, the bubble diameter is small, uniform and controllable, and the effect of a high degree of automation

Active Publication Date: 2015-11-11
HUBEI KAILIFENG GREEN BUILDING MATERIALS DEV CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, this "mechanical foaming" composite foaming cement preparation method requires a large number of turnover mold boxes when processing insulation boards; a large area of ​​turnover space is required; a large amount of transshipment labor is required; the finished product has a long turnover period and is noisy when dry cutting , dusty; From the perspective of modern enterprise standards, it is not suitable for large-scale production, low production capacity, high unit cost, does not have market competitiveness, and does not have the conditions to be widely used in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation technology of composite foam cement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1) Premixing: 63kg cement, 25kg fly ash ceramsite, 4kg micro silica fume, 0.55kg water reducer, 1.5kg aluminum sulfate, 0.01kg fiber, 0.60kg graphite, 0.58kg sodium sulfate, 0.58kg cellulose, 2.0kg of heavy calcium, 1.6g of phase change powder, dry mixed evenly to make a premix and store it in a storage tank for use;

[0038] 2) Foaming: Put the premix in step 1) and hot water at 40°C into the mixing tank and stir for 5 minutes (the hot water at 40°C accounts for 30% of the mass of the premix), and then pour them into the mixing tank in turn Add 0.68kg polyacrylamide, 0.01kg lithium carbonate, 0.035kg rubber powder, 0.75kg calcium stearate, 0.75kg801 rubber powder, 0.45kg sodium silicate, 0.55kg zinc stearate emulsion, 8.3kg mass concentration is 12.5% Oxidizing agent, continue stirring 5 minutes and make slurry;

[0039] 3) Pre-coagulation: inject the slurry in step 2) into the mold box of the pre-coagulation pit, and at the same time, supply 83°C hot water to the pre...

Embodiment 2

[0042] 1) Premixing: 80kg cement, 20kg fly ash ceramsite, 2kg micro silica fume, 1.25kg water reducer, 0.9kg aluminum sulfate, 0.03kg fiber, 0.75kg graphite, 1.0kg sodium sulfate, 0.75kg cellulose, 1.0kg of heavy calcium, 3.0g of phase change powder, after dry mixing evenly, make a premix and store it in a storage tank for use;

[0043] 2) Foaming: Put the premix in step 1) and hot water at 65°C into the mixing tank and stir for 5 minutes (the hot water at 65°C accounts for 22% of the mass of the premix), and then pour it into the mixing tank in turn Add 1.1kg polyacrylamide, 0.015kg lithium carbonate, 0.0125kg rubber powder, 1.5kg calcium stearate, 1.5kg801 rubber powder, 0.5kg sodium silicate, 1.0kg zinc stearate emulsion, 10.5kg mass concentration is 12.5% Oxidizing agent, continue stirring 5 minutes and make slurry;

[0044] 3) Pre-coagulation: inject the slurry in step 2) into the mold box of the pre-coagulation cellar, and at the same time, supply 100°C hot water to the...

Embodiment 3

[0047] 1) Premixing: Mix 75kg polystyrene with 20kg cement, 22.5kg fly ash ceramsite, 2.3kg microsilica, 0.88kg water reducer, 0.94kg aluminum sulfate, 0.022kg fiber, 0.69kg graphite, 0.83kg sulfuric acid Sodium, 0.92kg of cellulose, 1.85kg of heavy calcium, and 3.54g of phase change powder, which are uniformly dry-mixed to make a premix and stored in a storage tank for use;

[0048] 2) Foaming: put the premix in step 1) and hot water at 55°C into the mixing tank and stir for 5 minutes (the hot water at 55°C accounts for 7% of the mass of the premix), and then pour them into the mixing tank in turn Add 1.28kg polyacrylamide, 0.028kg lithium carbonate, 0.026kg rubber powder, 1.85kg calcium stearate, 1.5kg801 rubber powder, 0.78kg sodium silicate, 1.7kg zinc stearate emulsion, 14.5kg mass concentration is 12.5% Oxidizing agent, continue stirring 5 minutes and make slurry;

[0049] 3) Pre-coagulation: inject the slurry in step 2) into the mold box of the pre-coagulation pit, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a process for preparing composite foamed cement. The process comprises the following steps: premixing, namely, uniformly mixing a gel material, lightweight aggregate and a multifunctional additive, subsequently preparing the above components into premix, and storing the premix in a storage tank for later use; foaming, namely, feeding the premixed premix and hot water into a stirring tank, stirring for 5 minutes, sequentially adding a composite modifier and an oxidant into the stirring tank, and continuously stirring for 5 minutes, thereby obtaining slurry; pre-coagulating, namely, filling the foamed slurry into a mold box of a pre-coagulating kiln, simultaneously supplying hot water into the pre-coagulating kiln continuously so as to foam and expand the slurry inside the mold box, thereby preparing the composite foamed cement, and standing the composite foamed cement in the mold box for 6-8 minutes, thereby forming a composite foamed cement initial set object; and demolding and cutting, namely, demolding and cutting the pre-coagulated composite foamed cement initial set object into a plate material, thereby preparing the formed composite foamed cement. The composite foamed cement prepared by using the process is high in mechanical strength, free of foaming, high in foaming strength, rapid to coagulate and dry, short in demolding time and free of maintenance period, can save the space, the energy, the labor and the time, and can be cut in a wet manner.

Description

technical field [0001] The invention relates to a preparation method of composite foamed cement, and belongs to the field of preparation of novel materials. Background technique [0002] Composite foamed cement is a member of the concrete family. As the name implies, concrete is foamed or foamed, so it is also called foamed cement, lightweight concrete, etc. It is a waste-reducing, environmentally friendly, energy-saving, low-cost Carbon, economical, practical and non-combustible new building energy-saving materials with a fire rating of A. In recent years, both at home and abroad have attached great importance to the research and development of composite foamed cement, making it more and more widely used in the field of construction. At present, composite foamed cement is more and more widely used in building insulation materials in my country because of its good thermal insulation and fireproof characteristics, mainly including: roof insulation layer cast-in-situ, floor i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B28/00C04B26/04C04B24/26
Inventor 王义红卢叶张林江
Owner HUBEI KAILIFENG GREEN BUILDING MATERIALS DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap