Oil enhanced fog seal material for asphalt pavement and preparation method and construction method of oil enhanced fog seal material

A technology of fog seal layer material and asphalt pavement, which is applied in building insulation materials, roads, roads, etc., and can solve the problem that the adhesion between the original fog seal layer and the original pavement stone material cannot achieve the expected effect and reduce the anti-skid ability of the asphalt pavement surface layer , the reduction of the anti-seepage capacity of the pavement, etc., to achieve the effect of improving the anti-seepage capacity of the pavement, delaying ultraviolet aging, and improving the firmness of the pavement

Inactive Publication Date: 2014-12-03
CHANGAN UNIV
View PDF8 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the relatively simple preventive maintenance method of fog seal layer commonly used at present, its biggest disadvantage is that the anti-seepage effect is not ideal, and the adhesion between the original fog seal layer and the original pavement stone material cannot achieve the expected effect. Detachment will occur, exposing the stone material of the original pavement, and the anti-seepage ability of the pavement will be reduced, thereby reducing the skid resistance of the surface layer of the asphalt pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil enhanced fog seal material for asphalt pavement and preparation method and construction method of oil enhanced fog seal material
  • Oil enhanced fog seal material for asphalt pavement and preparation method and construction method of oil enhanced fog seal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Take the preparation of an oily enhanced fog seal material for asphalt pavement as an example for illustration.

[0057] (1) Weigh each component:

[0058] The sub-layer emulsion material for waterproof penetration includes the following components in parts by weight: 50 parts of 90# asphalt, 20 parts of D-80 kerosene solvent oil, 1 part of Lei Fengnuo, 2 parts of modified latex, and 2 parts of styrene butadiene particles.

[0059] The anti-slip and wear-resistant upper sub-layer emulsion material includes the following components in parts by weight: 50 parts of 90# asphalt, 20 parts of D-80 kerosene solvent oil, 1 part of Lei Fengnuo, 5 parts of modified latex, and 2 parts of styrene butadiene particles , 2 parts of phenyl salicylate.

[0060] (2) The preparation method of oily mist seal layer emulsion material:

[0061] The preparation method of the waterproof permeable lower sub-layer emulsion material: first heat and melt the petroleum asphalt, then mix it with so...

Embodiment 2

[0070] Take the preparation of an oily enhanced fog seal material for asphalt pavement as an example for illustration.

[0071] (1) Weigh each component:

[0072] The sub-layer emulsion material for waterproof penetration includes the following components in parts by weight: 70 parts of 70# asphalt, 60 parts of S-100 kerosene solvent oil, 10 parts of Lei Fengnuo, 8 parts of silane coupling agent KH7928, and 8 parts of modified rubber powder.

[0073] The anti-slip and wear-resistant upper sub-layer emulsion material includes the following components in parts by weight: 70 parts of 70# asphalt, 60 parts of S-100 kerosene solvent oil, 10 parts of Lei Fengnuo, silane coupling agent KH7928 parts, 4 parts of modified rubber powder, Benzophenone - 31 parts.

[0074] (2) The preparation method of oily mist seal layer emulsion material:

[0075] The preparation method of the waterproof permeable lower sub-layer emulsion material: first heat and melt the petroleum asphalt, then mix i...

Embodiment 3

[0084] Take the preparation of an oily enhanced fog seal material for asphalt pavement as an example for illustration.

[0085] (1) Weigh each component:

[0086] The sub-layer emulsion material for waterproof penetration includes the following components in parts by weight: 60 parts of 90# asphalt, 40 parts of S-100 solvent oil, 8 parts of Lei Fengnuo, 10 parts of silane coupling agent KH5500, and 6 parts of rock asphalt.

[0087] The anti-slip and wear-resistant upper sub-layer emulsion material includes the following components in parts by weight: 60 parts of 90# asphalt, 40 parts of S-100 solvent oil, 5 parts of Lei Feng Nuo, 15 parts of silane coupling agent KH55015, 3 parts of rock asphalt, salicylic acid 2 parts of phenyl ester.

[0088] (2) The preparation method of oily mist seal layer emulsion material:

[0089] The preparation method of the waterproof permeable lower sub-layer emulsion material: first heat and melt the petroleum asphalt, then mix it with solvent o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of road maintenance and discloses an oil enhanced fog seal material for asphalt pavement and a preparation method and a construction method of the oil enhanced fog seal material. The fog seal material comprises a waterproof permeable lower sublayer and a non-slip wear-resistant upper sublayer, wherein the upper sublayer and the lower sublayer are respectively composed of emulsion materials and sand on the layers; the emulsion material on the lower sublayer contains petroleum asphalt, solvent oil, an oil penetrating agent, a tackifier and an additive; and the emulsion material on the upper sublayer contains petroleum asphalt, solvent oil, an oil penetrating agent, a tackifier, an additive and an ultraviolet aging-resistant agent. The construction method of the fog seal material refers to a layered spreading method, namely mixing the emulsion material and sand on the lower sublayer and then spreading the mixture on the asphalt pavement so as to form the waterproof permeable lower sublayer, spraying the emulsion material on the upper sublayer on the waterproof permeable lower sublayer after drying, and spreading the sand so as to form the non-slip wear-resistant upper sublayer. The fog seal material disclosed by the invention is used for preventive maintenance of roads, and the water resistance, skid resistance, firmness and ultraviolet aging resistance of the pavement can be improved.

Description

technical field [0001] The invention relates to the technical field of highway maintenance, in particular to an oily enhanced fog seal material for asphalt pavement, a preparation method and a construction method. Background technique [0002] After several years of normal use of the asphalt pavement, the pavement will experience slight fatigue cracks and loss of fine aggregates, and its anti-seepage performance will deteriorate, and pavement water will enter the asphalt mixture through cracks or fine aggregate damage. accelerated road damage. [0003] Fog seal is currently the most effective preventive maintenance measure for asphalt pavement. This technology spreads the fog seal material on the asphalt pavement in the form of a mist to form a thin layer of seal to seal tiny cracks and surfaces. Voids, restore and protect the oxidized asphalt pavement, play a role in waterproofing and inhibiting looseness, and at the same time improve and enhance the image of the pavement....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01C7/32C08L95/00C08K13/02C08K3/00C08K5/134C08K5/132
Inventor 李炜光杨婉怡靳美倩郑敏楠耿九光
Owner CHANGAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com