Manufacturing technique for duplex metal compound crusher hammerhead

A compound crusher and production process technology, which is applied in the field of wear-resistant metal materials, can solve the problems of low hardness, easy breakage of the hammer head, and short service life, and achieve the effect of good hardness, not easy to fall off, and improved service life

Active Publication Date: 2014-08-20
盐城支点机械制造有限公司
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a production process for the hammer head of a bimetallic composite crusher, so as to overcome the defects of the prior art that the hammer head is easy to break, and its strength and hardness are too low so that its service life is very short.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing technique for duplex metal compound crusher hammerhead

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Smelting: smelting contains 3.1% C, 0.7% Si, 1.0% Manganese, 22% Cr, 1.0% Ca, 1.0% B, and P 0.05% high-chromium cast iron alloy liquid containing 0.05% S content, and pour the high-chromium cast iron alloy liquid into a wear-resistant layer. The ironing temperature is 1500 ° C, and the pouring temperature is 1480 ° C. Before pouring, the rare earth is crushed to the particle size Small pieces smaller than 15mm are dried at 280°C and wrapped with iron sheets and placed at the bottom of the ladle, and the molten steel is modified by the method of flushing into the ladle; the above contents are all percentages by weight;

[0022] (2) wear-resistant layer mold: the wear-resistant layer obtained in step (1) is polished;

[0023] (3) Casting hammer handle: cast the hammer head according to the shape of the hammer handle and grind it;

[0024] (4) Smelting molten steel containing 0.35% C, 0.8% Mn, 0.37% Si, 0.03% P and 0.03% S;

[0025] (5) Casting the lost foam of the h...

Embodiment 2

[0030] (1) Smelting: smelting contains 2.5% C, 0.3% Si, 0.6% Manganese, 18% Cr, 0.6% Ca, 0.8% B, and P content of 0.04%, S content of 0.04%, the high chromium cast iron alloy liquid, and pour the high chromium cast iron alloy liquid into a wear-resistant layer, the iron temperature is 1450 ℃, the pouring temperature is 1480 ℃, and the rare earth is broken to The small pieces with a particle size of less than 15mm are dried at 280°C and wrapped with tinfoil paper and placed at the bottom of the ladle, and the molten steel is modified by the method of pouring into the ladle; the above contents are all percentages by weight;

[0031] (2) wear-resistant layer mold: the wear-resistant layer obtained in step (1) is polished;

[0032] (3) Casting hammer handle: cast the hammer head according to the shape of the hammer handle and grind it;

[0033] (4) Smelting molten steel containing 0.27% C, 0.5% Mn, 0.2% Si, 0.02% P and 0.02% S;

[0034] (5) Casting the lost foam of the hammer he...

Embodiment 3

[0039] (1) Smelting: smelting contains 2.8% C, 0.5% Si, 0.8% Manganese, 20% Cr, 0.8% Ca, 0.9% B, and P 0.03% high-chromium cast iron alloy liquid containing 0.03% S content, and the high-chromium cast iron alloy liquid is poured into a wear-resistant layer. The ironing temperature is 1470 ° C, and the pouring temperature is 1480 ° C. Before pouring, the rare earth is broken to the particle size Small pieces smaller than 15mm are dried at 280°C and wrapped with iron sheets and placed at the bottom of the ladle, and the molten steel is modified by the method of flushing into the ladle; the above contents are all percentages by weight;

[0040] (2) wear-resistant layer mold: the wear-resistant layer obtained in step (1) is polished;

[0041] (3) Casting hammer handle: cast the hammer head according to the shape of the hammer handle and grind it;

[0042] (4) Melting molten steel containing 0.30% C, 0.7% Mn, 0.30% Si, 0.01% P and 0.01% S;

[0043](5) Casting the lost foam of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of wear-resistant metal materials and discloses a manufacturing technique for a duplex metal compound crusher hammerhead. The manufacturing technique for the duplex metal compound crusher hammerhead comprises the steps of smelting, wearing layer casting, hammer handle casting, hammerhead evanescent mode casting, pouring, cooling, heat treatment and the like. According to the manufacturing technique for the duplex metal compound crusher hammerhead, a wearing layer is welded at the front end of the hammerhead, the abrasive resistance of the crusher hammerhead is improved, the service life of the hammerhead is prolonged, and the requirements of impact resistance on the hammerhead by a crusher are met. The manufacturing technique for the duplex metal compound crusher hammerhead is simple, a hammer handle is closely connected with the hammerhead, the hammerhead is not prone to falling off when used, and the hammerhead is good in hardness, high in intensity and good in toughness.

Description

technical field [0001] The invention relates to the technical field of wear-resistant metal materials, in particular to a production process of a double-metal composite crusher hammer. Background technique [0002] Hammer crusher is a production equipment widely used in industrial sectors such as building materials, metallurgy, and chemical fertilizers, and the hammer head is a wearable part that consumes a lot. The working surface of the hammer head is in contact with the material, resulting in high stress wear. Since the crushed materials are generally hard objects such as rocks and metal ores, the wear of the parts is relatively serious. Through the analysis of the microscopic morphology of the hammer head surface, the wear process of the hammer head is the result of the combined action of deformation and erosion wear. This is due to the high-speed operation of the surface of the hammer head, and the inertia of the hammer head strikes and crushes the material. In the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D19/08C22C37/10C22C38/04
Inventor 包玮
Owner 盐城支点机械制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com