A kind of preparation method of one-component poss/addition type silicone resin nanocomposite material

A technology of nanocomposite materials and silicone resins, which is applied in the field of preparation of single-component POSS/addition silicone resin nanocomposites, which can solve the problems of low effective crosslink density, silicone resin mechanical strength stretching, weak impact, and organic silicon molecules. Interaction force is small and other problems, to achieve excellent thermal stability, system transparency, mechanical and high temperature performance improvement effect

Active Publication Date: 2016-09-21
JIANGXI PROVINCE HANGYU NEW MATERIAL CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the small intermolecular force of silicone and the low effective crosslinking density, the mechanical strength (bending, stretching, impact, etc.) of the silicone resin is weak, and it needs to be reinforced by other means.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Take 30 grams of methyltrimethoxysilane and 55.1 grams of ethyl orthosilicate, and inject them into three-necked flasks with stirring and condensing equipment. Set the temperature of the water bath to 50°C, adjust the pH of the system to 3 with concentrated hydrochloric acid, slowly drop 25.8 g of deionized water into the three-necked flask under stirring, and complete the drop within 1 hour. After reacting for 3 hours, a white solid product was obtained, and the reaction was stopped. The white solid was filtered out using a Buchner funnel, washed with tetrahydrofuran five times, and finally the treated white solid was placed in a vacuum oven and dried at 100°C for 24 hours to obtain The white solid powder is polyhedral oligomeric silsesquioxane.

[0025] Take 60 grams of methyltrimethoxysilane and 17.5 grams of dimethyldimethoxysilane and slowly drop them into a three-necked flask with 150 grams of absolute ethanol and 67.4 grams of deionized water in advance with a co...

Embodiment 2

[0028] Take 30 grams of methyltriethoxysilane and 27.8 grams of ethyl orthosilicate, and inject them into three-necked flasks with stirring and condensing equipment. Set the temperature of the water bath to 50°C, adjust the pH of the system to 3 with concentrated hydrochloric acid, slowly drop 13.1 g of deionized water into the three-necked flask under stirring, and complete the drop within 1 hour. After reacting for 3 hours, a white solid product was obtained, and the reaction was stopped. The white solid was filtered out using a Buchner funnel, washed with tetrahydrofuran five times, and finally the treated white solid was placed in a vacuum oven and dried at 100°C for 24 hours to obtain The white solid powder is polyhedral oligomeric silsesquioxane.

[0029] Take 60 grams of methyltriethoxysilane and 10.9 grams of dimethyldiethoxysilane and slowly drop them into a three-necked flask with 150 grams of absolute ethanol and 34 grams of deionized water in advance with a constan...

Embodiment 3

[0032]Take 30 grams of phenyltrimethoxysilane and 37.8 grams of ethyl orthosilicate, and inject them into three-necked flasks equipped with stirring and condensing equipment. Set the temperature of the water bath to 50°C, adjust the pH of the system to 3 with concentrated hydrochloric acid, slowly drop 17.7 g of deionized water into the three-necked flask under stirring, and complete the drop within 1 hour. After reacting for 3 hours, a white solid product was obtained, and the reaction was stopped. The white solid was filtered out using a Buchner funnel, washed with tetrahydrofuran five times, and finally the treated white solid was placed in a vacuum oven and dried at 100°C for 24 hours to obtain The white solid powder is polyhedral oligomeric silsesquioxane.

[0033] Take 60 grams of phenyltrimethoxysilane and 14.8 grams of dimethyldiethoxysilane and slowly drop them into a three-necked flask with 90 grams of absolute ethanol and 46.3 grams of deionized water in advance wit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method for a single-component POSS / addition type silicon resin nanocomposite. The method comprises the following steps: double-bond-contained polyhedral oligomeric silsesquioxane (POSS) is synthesized, a silanol mixed solution containing different functional groups is prepared, and the double-bond-contained polyhedral oligomeric silsesquioxane (POSS) reacts with the silanol mixed solution to generate the target product namely single-component POSS / addition type silicon resin nanocomposite. The method comprises the following steps: (1), synthesizing the double-bond-contained polyhedral oligomeric silsesquioxane (POSS); (2) synthesizing silanol; (3), adding the double-bond-contained polyhedral oligomeric silsesquioxane (POSS) with different content, which is obtained through the step (1), into the silanol mixed solution obtained through the step (2), and reacting continuously for a period of time, so that a POSS / silicon resin nanocomposite prepolymer is obtained, then adding an end-capping agent, reducing pressure for removing low-molecular-weight by-products and absolute ethyl alcohol, and adding a cross-linking agent, a catalyst and an inhibitor auxiliary, so that the single-component POSS / addition type silicon resin nanocomposite is obtained.

Description

technical field [0001] The invention relates to a preparation method of a single-component POSS / addition type silicone resin nanocomposite material, which belongs to the technical field of high molecular photoelectric new materials. Background technique [0002] Polymer-based nanocomposites combine the advantages of each component, not only have excellent mechanical properties, but also have good thermal stability, toughness and optical properties. In addition, the controllable content of inorganic substances in polymer-based nanocomposites, light weight, and easy processing can effectively improve the physical and mechanical properties of polymers. [0003] Polyhedral oligomeric silsesquioxanes (POSS) are a class of polyhedral oligomeric silsesquioxanes (RSiO 1.5 ) n Structural substances have been a research hotspot in recent years. The R substituents in the molecular structure are hydrogen, alkyl, alkenyl, aryl, arylene and their derivative groups. According to differe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G77/20C08G77/06C08L83/07
Inventor 董晓娜陈衍华游胜勇谌开红金贞玉
Owner JIANGXI PROVINCE HANGYU NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com