Pearlescent pigment with environment cleaning capacity

A clean and pearlescent technology, which is applied in the treatment of inorganic pigments, fibrous fillers, cosmetics, etc., can solve the problems affecting the stability of the coating film, the effect cannot be displayed, and it is difficult to maintain the color quality of pearlescent coatings, so as to improve the photocatalytic activity. and antibacterial effect

Inactive Publication Date: 2014-05-21
浙江瑞成新材料股份有限公司 +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But, natural mica has its defect as the matrix material of pearlescent pigment: (1) though the mica flake that (1) grinds and grades by wet grinding method can obtain less thickness and larger diameter-to-thickness ratio (general requirement is greater than 50), but Usually there is a wide range of thickness distribution (0.2-1 micron), so it is easy to affect the stability of the coating, and it is not easy to make pearlescent pigments with uniform hue; The formed layers and edge gradients cause light to scatter and reduce the pearlescent effect; (3) natural mica contains colored impurity ions such as iron ions, and requires very complicated and time-consuming steps to remove these impurity ions
[0007] In the past, when pearlescent pigments were prepared into coatings to have other functions, other effective agents such as antibacterial agents or antifouling agents were often added to increase the functions of the coatings. However, the more additives were added, the interaction between the additives The greater the factor, the less effective the performance will be. This kind of mixing method will cause the pearlescent pigment to fail to express its characteristics and it is difficult to maintain the color quality of the pearlescent coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pearlescent pigment with environment cleaning capacity
  • Pearlescent pigment with environment cleaning capacity
  • Pearlescent pigment with environment cleaning capacity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1: present embodiment provides a kind of pearlescent pigment, and its structure is:

[0035] (1) as Figure 1 As shown, on the surface of the sheet substrate 1, a plurality of columnar Ti 2 O 3 The nanorod 2, the sheet substrate 1 can be natural mica sheet, synthetic mica sheet, glass sheet, sheet aluminum powder, sheet expanded perlite, aluminum oxide, silicon dioxide, etc., the sheet substrate 1 The particle size can be 2-800 microns, and the thickness can be 0.1-10 microns. In the present invention, an aqueous solution of titanium trichloride hydrochloric acid is slowly added dropwise to the solution containing sheet substrate 1 to hydrolyze titanium trichloride into trioxide Dititanium is adsorbed on the sheet substrate 1 to form a Ti 2 O 3 Nanorod 2, where Ti 2 O 3 Nanorods 2 can control Ti according to reaction rate, reaction time and pH value 2 O 3 The height of nanorod 2, to form the pearlescent pigment of different colors, just utilize Ti 2 O...

Embodiment 2

[0036] Embodiment 2: the present embodiment provides a kind of pearlescent pigment coated with metal, and its structure is:

[0037] (1) as Figure II Shown, continue the follow-up step of embodiment 1, further provide another kind of pearlescent pigment. (2) Utilize Ti on the pearlescent pigment of embodiment 1 2 O 3 Reducibility, after redox reaction with metal salt, Ti 2 O 3 oxidized to TiO 2 , metal particles 4 are reduced and deposited on TiO 2 1 on the nanorod 3 and the sheet substrate; wherein the metal salt can be metal salts such as chloroauric acid, chloroplatinic acid, ruthenium chloride, palladium chloride, rhodium chloride, ferric chloride, copper nitrate and palladium acetate any one or a combination of two or more. Next, according to the use of different metal particles 4 deposited on the TiO 2 On the nanorods 3 and the sheet substrate 1, pearlescent pigments coated with different metals can be obtained. For example, after redox reaction is carried out w...

Embodiment 3

[0038] Embodiment 3: present embodiment provides a kind of pearlescent pigment, and its structure is:

[0039] (1) Use commercially available pearlescent pigments (YB103, YB205, YB219, YB300, YB504, etc.) 2 O 3 The nanorods grow by reaction, and the Ti is controlled according to the time of adding the titanium trichloride solution 2 O 3 The growth height of the nanorods, after reacting for 8 to 12 hours, the pH value is controlled at 1.5-2.5, Ti 2 O 3 The growth height of the nanorod is 60-80 nanometers, and it has a length of 30-60 nanometers and a width of 30-60 nanometers, and a plurality of Ti rods arranged at intervals. 2 O 3 Nanorods will form a rough surface on their surface, and have a total roughness Rz(DIN) between 60-80, and Ti 2 O 3 Coated pearlescent pigments, and the pearlescent pigments form multiple Ti on the surface 2 O 3 The nanostructure of nanorods has a lotus effect, which produces anti-fouling and dust-proof effects.

[0040] Then, (2) using the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pearlescent coating with environment cleaning capacity. The pearlescent coating is characterized by comprising a sheet substrate and film forming resin, and multiple spaced titanium dioxide nanorods are formed on the sheet substrate, therefore, a nano-structure surface with roughness can be formed by use of the titanium dioxide nanorods on the pearlescent coating, and then multiple metal particles are deposited on each titanium dioxide nanorod and the sheet substrate.

Description

technical field [0001] The invention belongs to the field of pearlescent pigments, and relates to a metal-coated powder pigment, in particular to a metal-coated pearlescent pigment with environmental cleaning power. Background technique [0002] Pearlescent pigments are pigments that give pearly luster to products. It is a transparent or translucent flake as the core, and uses a special chemical process to coat one or more layers of titanium dioxide and other metal oxides on its surface. When When the light hits the interface of the pearlescent pigment, reflected light and refracted light will be produced, part of the light is transmitted and then reflected, and they interfere with each other to produce a three-dimensional pearlescent color. At present, most of the base materials are mica flakes, which are covered with a high-refraction titanium dioxide coating. When white light shines on this type of pigment, it is partially reflected by the titanium dioxide layer, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/36C09C3/06C09C1/40A61K8/89A61K8/87A61K8/86A61K8/85A61K8/81A61K8/29A61K8/19A61Q1/10A61Q1/08A61Q1/06A61Q1/04A61Q3/02A61P31/02
Inventor 张海滨郭永城李善云黄兆忠徐步方穆彬郭秋容吴兴伟
Owner 浙江瑞成新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com