Energy storage type self-luminous nano coating material

A technology of nano-coatings and self-luminous materials, applied in the field of coatings, can solve the problems of need to improve practical life and simple functions, and achieve the effects of improved coating performance and long service life

Active Publication Date: 2015-01-07
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing energy-storage self-luminous nano-coatings have simple functions, and the practical life needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An energy storage type self-luminous nano coating, comprising the following components in parts by weight: 35 parts of open-cell expanded perlite, 65 parts of calcium titanate, 35 parts of rosin, 18 parts of glass microspheres, 15 parts of chitin, chitosan 18 parts of sugar, 30 parts of nano-titanium dioxide, 18 parts of nano-zinc oxide, 13 parts of nano-silicon oxide, 35 parts of styrene-acrylic emulsion (with a particle size of 0.15 μm) and 18 parts of nano-rare-earth self-luminous material.

[0021] Its preparation method is as follows: mix open-cell expanded perlite, calcium titanate, rosin, chitin and chitosan in the formula amount into a mixer, and stir at 35°C for 1 hour to obtain A mixed liquid; mix the formula amount of glass Microbeads, nano-titanium dioxide, nano-zinc oxide, nano-silicon oxide, styrene-acrylic emulsion and nano-rare-earth self-luminous materials are mixed and added to the mixer, stirred at room temperature for 1 hour to obtain B liquid, and th...

Embodiment 2

[0023] An energy storage type self-luminous nano coating, comprising the following components in parts by weight: 30 parts of open-cell expanded perlite, 60 parts of talcum powder, 20 parts of silica powder, 30 parts of maleic rosin ester, and 20 parts of glass microspheres , 10 parts of chitin, 20 parts of chitosan, 20 parts of nano-titanium dioxide, 20 parts of nano-zinc oxide, 10 parts of nano-silicon oxide, 40 parts of vinegar-acrylic emulsion (particle size is 0.2 μm) and 15 parts of nano-rare earth self-luminous material share.

[0024] Its preparation method is as follows: mix open-cell expanded perlite, talc powder, silica powder, maleic anhydride rosin ester, chitin and chitosan into a mixer, stir at 30°C for 0.5h, and obtain A mixed Liquid; mix glass microspheres, nano-titanium dioxide, nano-zinc oxide, nano-silicon oxide, vinegar-acrylic emulsion and nano-rare-earth self-luminous materials into the mixer, stir at room temperature for 0.5h, and obtain B liquid. The ...

Embodiment 3

[0026] An energy storage type self-luminous nano coating, comprising the following components in parts by weight: 40 parts of open-cell expanded perlite, 30 parts of talcum powder, 20 parts of silica powder, 40 parts of turpentine, 15 parts of glass microspheres, and 20 parts of chitin 15 parts of chitosan, 40 parts of nano-titanium dioxide, 15 parts of nano-zinc oxide, 15 parts of nano-silicon oxide, 40 parts of tert-acetic acid emulsion (particle size is 0.4 μm) and 20 parts of nano-rare earth self-luminous material.

[0027] Its preparation method is as follows: mix open-cell expanded perlite, talc powder, silica powder, maleic anhydride rosin ester, chitin and chitosan in the formula amount and add them to the mixer, stir at 40°C for 0.8h, and obtain A mixed Liquid; mix glass microspheres, nano-titanium dioxide, nano-zinc oxide, nano-silicon oxide, vinegar tert-emulsion and nano-rare-earth self-luminous materials into the mixer, and stir at room temperature for 0.8h to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an energy storage type self-luminous nano coating material. The energy storage type self-luminous nano coating material comprises the following ingredients in parts by weight: 30-40 parts of perforated expanded perlite, 50-80 parts of filler, 30-40 parts of resin, 15-20 parts of glass micro-beads, 10-20 parts of chitin, 15-20 parts of chitosan, 20-40 parts of nano titanium white, 15-20 parts of nano zinc oxide, 10-15 parts of nano-silica, 30-40 parts of acrylic emulsion and 15-20 parts of nano rare-earth self-luminous material. The invention further discloses a preparation method of the nano coating material. Through the compounding of the raw materials of the energy storage type self-luminous nano coating material, the energy storage type self-luminous nano coating material disclosed by the invention is wear-resistant, is long in service life and has a bacterium resisting effect, and nano-materials or nano-structured ingredients are introduced into an organic coating material, so that organic and inorganic matched compositing or hybridization is realized. The advantages of organic polymers and inorganic-structured ingredients are integrated, so that the properties of the coating material are obviously improved.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to an energy storage type self-luminous nano coating. Background technique [0002] The development of new energy sources and energy conservation have become the common needs of people in the world today. With the maturity of optoelectronic technology, many countries have turned their research focus to how to realize the light-light conversion of materials, that is, to store light and then emit light. The existing energy-storage self-luminous nano-coatings have simple functions, and the practical life needs to be improved. Contents of the invention [0003] Purpose of the invention: In order to overcome the deficiencies of the prior art, the present invention provides an energy storage type self-luminous nano coating. [0004] Technical solution: In order to solve the above technical problems, the present invention proposes an energy storage type self-luminous nano c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D105/08C09D201/00C09D7/12C09D5/22C09D5/14
CPCC09D125/14C08K2201/011C08L2205/025C08L2205/035C09D5/14C09D5/22C09D7/61C09D7/70C09D131/04C09D133/04
Inventor 潘峥嵘
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com