Barium-strontium scale inhibitor

A technology of scale inhibitors and strontium scale inhibitors, which is applied in the field of barium strontium scale inhibitors, can solve the problems of cumbersome preparation methods, use restrictions, environmental pollution, etc., achieve excellent scale inhibition effects, completely clarify water bodies, and save use costs

Inactive Publication Date: 2014-05-07
YANGTZE UNIVERSITY
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN101012090A discloses a barium strontium scale inhibitor, but because it is a phosphonic acid copolymer, it is easy to cause pollution to the environment and its use is limited
Chinese patent CN1491908A discloses a barium strontium scale inhibitor, which is composed of sodium tripolyphosphate, ethylenediaminetetraacetic acid and other substances. The preparation method is cumbersome and the cost is high when used.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Barium-strontium scale inhibitor
  • Barium-strontium scale inhibitor
  • Barium-strontium scale inhibitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] (1) Preparation of terpolymer

[0022] ①Add 0.5mol maleic anhydride and 1.0-4.5mol distilled water into a four-necked flask equipped with an electric stirrer, two dropping funnels and a reflux condenser, stir to dissolve and heat to 60-75°C.

[0023] ②Put 0.1~0.3mol of acrylic acid or methacrylic acid and 0.25~0.5mol of acrylate mixture, 0.01~0.03mol of potassium persulfate solution into two dropping funnels, and drop these two solutions into the flask at the same time under stirring , and the dropwise addition was completed within 0.5 to 1.5 hours.

[0024] ③Continue heating the mixed reactant in ② to 80-95°C, then react at constant temperature for 3-6 hours, cool to room temperature to obtain a light yellow transparent liquid, and adjust the pH=7 with 50% sodium hydroxide solution to obtain the required ternary copolymer.

[0025] (2) Structural characterization of the terpolymer

[0026] Adopt KBr tablet method to carry out infrared spectrum analysis to the terpol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
scale inhibition rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to a barium-strontium scale inhibitor, belongs to the technical field of industrial water treatment agent designing and is especially suitable for water containing barium-strontium scale and calcium-barium-strontium composite scale in the oil field. A terpolymer and poly(sodium epoxysuccinate) are compounded according to a mass percent ratio of 1: 0.1-5.0 to form the barium-strontium scale inhibitor. Maleic anhydride is added with acrylic acid or methacrylic acid and acrylic acid ester and the mixture undergoes a copolymerization reaction under the action of potassium persulphate as an initiator to produce the terpolymer. A hydrolysate of maleic anhydride and sodium hydroxide is added with sodium tungstate as a catalyst and hydrogen peroxide as an oxidizing agent, the mixture undergoes a reaction to produce sodium epoxysuccinate, the sodium epoxysuccinate is added with a sodium-calcium compound alkali as an initiator and the mixture undergoes a polymerization reaction to produce the poly(sodium epoxysuccinate). The barium-strontium scale inhibitor does not contain phosphorus, has a small use amount and good effects, can be effectively used for preventing barium-strontium scale, calcium scale and calcium-barium-strontium composite scale in the oil field, has excellent barium-strontium scale inhibition performances, has a low cost, can be prepared by a simple method and is environmentally friendly.

Description

Technical field: [0001] The invention relates to a barium-strontium scale inhibitor, which belongs to the technical field of industrial water treatment agent design, and is especially suitable for water bodies containing barium-strontium scale and calcium-barium-strontium composite scale in oil fields. Background technique: [0002] Fouling is a widespread phenomenon and is a thermodynamically spontaneous process. Scaling in oilfields will bring many problems to production. Scaling in oil layers and areas near wells will block oil and gas channels, reduce oil layer permeability, and reduce oil well fluid production. Scaling in water injection systems will increase water injection pressure and increase energy consumption. Reduced production capacity; scaling on the surface of pipes and equipment can cause subscale corrosion or even perforation. With the deepening of oilfield development, the content of barium and strontium ions in formation water and oilfield produced water ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F5/10C08F222/06C08F220/06C08F222/10C08G65/22
Inventor 唐善法朱洲熊炜熊玉娟田磊邹玮
Owner YANGTZE UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com