Method for compounding natural protein fiber powder on surfaces of polymer filaments

A protein fiber and surface composite technology, which is applied in the direction of plant fiber, fiber type, fiber treatment, etc., can solve the problems of single choice of matrix material, poor temperature resistance of natural protein fiber powder, low content of natural protein fiber powder, etc.

Active Publication Date: 2014-02-05
JIANGSU YIMAO FILTER MEDIA CO LTD
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above-mentioned existing problems, the object of the present invention is to overcome the above-mentioned defects, and provide a method that can effectively solve the problem of poor temperature resistance of natural protein fiber powder, natural protein fiber powder is coated by matrix, low content of natural protein fiber powder and The method for compounding the natural protein fiber powder on the polymer filament surface of problems such as matrix material selection comparatively singleness, for satisfying the solution of the object of the present invention is:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] A Preparation of blend solution

[0033] According to the following mass percentage:

[0034] Natural protein fiber powder 1-16%

[0035] Protein Compatible Polymer 1-12%

[0036] Polar solvents 72-98%

[0037] Wool fiber powder or cashmere fiber powder or silk fiber powder or down fiber powder or rabbit hair fiber powder or camel hair fiber powder or human hair fiber powder or mohair fiber powder or yak fiber powder with an average particle size of ≤2 μm One of the wool fiber powders is put into soft water or 8% acetic acid aqueous solution or dimethylformamide or dimethylacetamide or dimethyl sulfoxide or 1,4-dioxane, and ultrasonically disperses 1- After 3 hours, add one of polyurethane or polyvinyl alcohol or polyacrylonitrile or gelatin or chitosan with a number average molecular weight of 8000-100000, and use mechanical stirring to make the protein phase at a temperature of 25-98 ° C. Allow the polymer to dissolve, and after dissolving for 3-5 hours, obtain a ...

Embodiment 1

[0046] A Put 1 g of wool fiber powder with an average particle size of 2 μm into 98 g of dimethylformamide, and after ultrasonic dispersion for 1 h, add 1 g of polyurethane with a number average molecular weight of 8000, and use Mechanical stirring makes polyurethane dissolve, after dissolving 3h, obtain blend solution through static vacuum degassing, the viscosity of blend solution is 100 mPa s, and static vacuum degassing temperature is 25 DEG C;

[0047] B Warm up the blended solution prepared in step A to 25°C under ultrasonic vibration, pass the polyester with a denier of 1 denier and 1 root through the blended solution and the thickness control mold at a speed of 50 m / min The diameter of the upper hole is 25 μm, and the length of the hole is a guide wire hole of 5 mm to obtain a polyester with a thickness of 10 μm on the surface of the composite blend solution, and the distance of the polyester through the blend solution is 2 cm;

[0048] C is after the terylene of the s...

Embodiment 2

[0051] A Put 2 g of cashmere fiber powder with an average particle size of 1.5 μm into 97 g of demineralized water, and after ultrasonic dispersion for 2 hours, add 1 g of polyvinyl alcohol with a number-average molecular weight of 10,000. Stir to make the polyvinyl alcohol dissolve, after dissolving for 4h, obtain the blended solution through static vacuum degassing, the viscosity of the blended solution is 250 mPa s, and the static vacuum degassing temperature is 30 °C;

[0052] B The blending solution prepared in step A is heated up to 85°C under ultrasonic vibration, and the denier is 10 deniers, and the polyamide fibers with 4 roots pass through the blending solution and the thickness control mold at a speed of 80 m / min The diameter of the upper hole is 50 μm, and the length of the hole is 10 mm. The nylon fiber with a surface composite blend solution thickness of 12 μm is obtained, and the distance of the nylon fiber through the blend solution is 4 cm;

[0053] C is afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for compounding natural protein fiber powder on surfaces of polymer filaments, belonging to the technical field of new textile materials. The method comprises the steps of preparation of a blended solution, formation of polymer filaments with surfaces compounded with the blended solution and control of thickness, phase inversion primary formation of the polymer filaments with surfaces compounded with the blended solution and thermosetting formation of the polymer filaments with surfaces compounded with the blended solution, thus obtaining the polymer filaments with surfaces compounded with natural protein fiber powder. The polymer filaments with surfaces compounded with natural protein fiber powder have the characteristics of good strength, elasticity, hand feeling, surfaces rich in natural protein fibre powder, uniform distribution and the like, so that the polymer filaments have the characteristics of natural protein fibers and wide use values. The preparation method is simple to operate, dispenses with special equipment and achieves industrial production easily.

Description

technical field [0001] The invention relates to a method for compounding natural protein fiber powder on the surface of polymer filaments, belonging to the technical field of new textile materials. Background technique [0002] Natural protein fibers include silk, wool, cashmere, down, hair, rabbit fur, mohair, etc., which are renewable natural materials with excellent performance. At present, natural protein fibers are widely used in people's daily life. Except for clothing and bedding, most of them are simply processed and used as feed or degraded by fermentation. At the same time, the leftovers and waste fibers of natural protein fibers cannot Realize reasonable reuse, resulting in huge waste of resources. Therefore, it is of great significance to study new methods and new ways to realize the regeneration and efficient utilization of natural protein fiber resources. [0003] At present, there are two main methods to regenerate and spin natural protein fibers into protei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/15D06M15/564D06M15/333D06M15/31D06M15/03D06M101/32D06M101/24D06M101/06D06M101/20
Inventor 刘欣徐卫林程远佳吴勇敏郭蕾陈凤翔
Owner JIANGSU YIMAO FILTER MEDIA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com