A production method of electroslag remelting of high-strength and high-plasticity twip steel

A technology of electroslag remelting and production method, which is applied in the field of metallurgy to achieve the effects of preventing cracks, reducing aluminum burning loss, improving solidification structure and segregation status

Active Publication Date: 2016-01-20
UNIV OF SCI & TECH BEIJING
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the TWIP steel electroslag process technology has not been reported in the relevant literature. The determination of the mold slag composition, the burning loss control of easily oxidized elements and volatile elements, and the control of the loose center of the electroslag final stage are the key issues in the development of this technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production method of electroslag remelting of high-strength and high-plasticity twip steel
  • A production method of electroslag remelting of high-strength and high-plasticity twip steel
  • A production method of electroslag remelting of high-strength and high-plasticity twip steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0047] The target composition of smelted TWIP steel is shown in Table 1.

[0048] Table 1 TWIP steel chemical composition control requirements, %

[0049] element C Si mn P S Al chemical composition ≤0.04 2.55～3.05 24.00～26.00 ≤0.025 ≤0.005 2.90～3.50

[0050] 1) Preparation of electrode ingot

[0051] According to the target composition requirements, the chemical composition control of the electrode ingot before electroslag remelting is shown in Table 2.

[0052] Table 2 Chemical composition control of TWIP steel electrode ingot, %

[0053]

[0054] Determine the size of the electrode ingot according to the size of the target product. This example plans to produce about 14 tons of TWIP steel by electroslag remelting, so two 7.3t electrode ingots are prepared, and then continuously smelted by electroslag remelting to obtain TWIP steel electroslag ingots with a weight of about 14 tons. Among them, the size of the electrode ingot is φ580 / 62...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a production method of high-strength high-plasticity TWIP (Twinning Induced Plasticity) steel, and belongs to the technical field of metallurgy. The TWIP steel comprises 0.03%-0.08% of C, 2.0%-3.0% of Si, 20%-30% of Mn, 2.5%-3.5% of Al, the balance of Fe and a small amount of other alloying elements. The TWIP steel is smelted by adopting a slag system comprising 60-70% of CaF2, 20-30% of Al2O3 and 5-15% of CaO; a right amount of manganese metal or electrolytic manganese and aluminium powder are added to slag so as to solve the problems of easy oxidization and burning loss of volatile elements in the TWIP steel. Argon is used for protecting remelting at a flow rate of 20-40Nm<3> / h, so that the burning loss of aluminium is reduced; the refinement is carried out at a low melting rate, and the melting rate is controlled at 700-950kg steel / hour. In a feeding period, electric currents gradually decline, and the feeding time is greater than 1.5 hours. The production method has the advantages that by adopting the electroslag remelting method, cracks are prevented from occurring in a TWIP solidification process, the solidification structure and the segregation condition of the TWIP steel can be improved, and meanwhile, the cleanliness of the TWIP steel can also be obviously improved.

Description

technical field [0001] The invention belongs to the field of metallurgy technology, and relates to a production and control method of high-strength and high-plasticity TWIP (twin-induced plasticity) steel, which can obtain TWIP steel with qualified components, excellent internal metallurgical quality and excellent mechanical properties. Background technique [0002] TWIP steel is a kind of twinning induced plasticity steel (Twinning induced plasticity), which is an ideal structural material for safety, weight reduction and energy saving in automobiles, which integrates high strength, high plasticity and high strain hardening performance. [0003] Single-phase austenitic high manganese steel was patented by R.A. Hadfield as early as 1883. Later, Grassel's research showed that increasing the content of Mn and adjusting the content of Al and Si in the Fe-Mn-Al-Si alloy can obtain a steel structure with a single austenite structure, and the product of its tensile strength and el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B9/18
Inventor 刘建华庄昌凌江海涛郭军儒
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More