High-dielectric-constant X8R type MLCC medium material and preparing method thereof

A technology of high dielectric constant and dielectric material, applied in high dielectric constant X8R type MLCC dielectric material and its preparation, medium and low temperature sintering high dielectric constant X8R type MLCC dielectric material and its preparation field, can solve the problem of high loss, Achieve the effects of reducing the capacity temperature change rate, increasing the Curie temperature, and increasing the insulation resistivity

Active Publication Date: 2014-01-01
FUJIAN TORCH ELECTRON TECH CO LTD
View PDF4 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although Na 0.5 Bi 0.5 TiO 3 The Curie point is higher, and the modified barium titanate does increase the Curie temperature of barium titanate, but due to Na 0.5 Bi 0.5 TiO 3 The loss itself is high, so reduce Na 0.5 Bi 0.5 TiO 3 -The loss of BT-based composite dielectric materials has become a new problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-dielectric-constant X8R type MLCC medium material and preparing method thereof
  • High-dielectric-constant X8R type MLCC medium material and preparing method thereof
  • High-dielectric-constant X8R type MLCC medium material and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] The present invention will be further described below through specific embodiments.

[0037] A preparation method of high dielectric constant X8R type MLCC dielectric material:

[0038] (1) Nb 2 o 5 Proportion with ZnO according to the Zn / Nb atomic molar ratio of 1:1, weigh, mix, sieve and calcinate at 800-900°C, ball mill and dry to obtain ZnNb 2 o 5 ;

[0039] (2) According to the chemical formula MBi 4 Ti 4 o 15 , M is one or more of Sr, Ca and Ba, for TiO 2 、 Bi 2 o 3 , SrCO 3 、BaCO 3 with CaCO 3 Carry out proportioning, make MBi 4 Ti 4 o 15 ;

[0040] (3) Proportion by weight as follows: 35-42 parts of Bi 2 o 3 , 8-14 parts of ZnO, 8-12 parts of CaCO 3 , 20-25 parts of H 3 BO 3 , 4 to 8 parts of SiO 2 and 7-11 Li 2 CO 3 , carrying out proportioning, weighing, mixing, sieving, melting at 1000-1100°C, water quenching, grinding and sieving to obtain fluxing glass powder;

[0041] (4) Combining ZnO with SiO 2 According to the Zn / Si atomic molar ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-dielectric-constant X8R type MLCC medium material. 100 parts, by weight, of barium titanate are used as base materials which are added with, by weight, 0.5-1.5 parts of niobium zinc compound, 1.5-2.5 parts of MBi4Ti4O15, 0.3-0.75 part of zirconic oxide, 3-4 parts of flux glass powder, 1-2 parts of silicon zinc compound, 0-0.2 part of manganic carbonate and 0-0.2 part of one or more of oxides of Er, Yb, Dy, Ho and Nd. M is one or more of Sr, Ca and Ba. According to the high-dielectric-constant X8R type MLCC medium material, a proper amount of niobium zinc compounds are added to easily form a core-shell structure. The core-shell structure can facilitate stability of the medium temperature of a medium material and reduce the temperature coefficient of capacitance of the material.

Description

technical field [0001] The invention belongs to the field of ceramic functions, and relates to a high dielectric constant X8R type MLCC dielectric material and a preparation method thereof, in particular to a medium-low temperature sintered high dielectric constant X8R type MLCC dielectric material and a preparation method thereof. Background technique [0002] MLCC is the English abbreviation of chip multilayer ceramic capacitors (Multi-layer ceramic capacitors). According to temperature characteristics, material, production process. MLCC can be divided into the following types: NPO, COG, Y5V, Z5U, X7R, X5R, etc. NPO and COG have stable temperature characteristics, small capacitance and high price; Y5V and Z5U have large temperature characteristics, large capacitance and low price; X7R and X5R are between the above two. [0003] In recent years, X7R (operating temperature range -55 ° C ~ 125 ° C, capacity temperature change rate within ± 15%) MLCC materials have been exte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/468C04B35/622
Inventor 黄祥贤吴金剑张子山谢显斌宋运雄
Owner FUJIAN TORCH ELECTRON TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap