A low-smoke flame-retardant cable material for locomotives and its preparation method

A low-smoke flame-retardant and cable material technology, applied in the direction of insulating cables, cables, circuits, etc., to achieve the effects of improved resilience performance, superior mechanical properties, and strong water resistance

Active Publication Date: 2016-03-02
蚌埠尚维知识产权运营有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is difficult to prepare halogen-free flame-retardant materials with high temperature resistance (150°C), high strength (≥13.79MPa), high elongation (≥300%), and high flame retardancy (VW-1) for the above halogen-free flame-retardant materials. Wire and Cable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A low-smoke flame-retardant cable material for locomotives, which is composed of the following raw materials in parts by weight:

[0017] Neoprene M-40105, cis-1,4-polyisoprene rubber 10-15, nitrile rubber 12, triethylene glycol diisocaprylate 15-25, vulcanizing agent DCBP3, titanate coupling agent TMC-TTS2, barium sulfate powder 35, anti-aging agent AW2, 2-mercaptobenzimidazole 2, chlorinated paraffin 8, accelerator DM2, silane coupling agent KH5501-2, crosslinking agent TAC1, nano bauxite 25 , propylene glycol adipate polyester 3, zinc borate hydrate 4, epoxy butyl oleate 4-6, vulcanizing agent DCBP0.8, modified sepiolite 3, bispentamethylenethiuram hexasulfide 6;

[0018] The preparation method of described modified sepiolite is: soak sepiolite with 15% hydrochloric acid for 4 hours, wash with deionized water, then soak with 12% sodium hydroxide solution for 4 hours, then wash with deionized water until neutral , drying; put the dried sepiolite into water, then add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
elongationaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-smoke flame retardant cable material for locomotive and a preparation method thereof. The low-smoke flame retardant cable material consists of the following raw materials in parts by weight: 95-105 parts of chloroprene rubber M-40, 10-15 parts of cis-1,4-polyisoprene rubber, 15-20 parts of nitrile butadiene rubber, 15-25 parts of triethylene glycol di-isooctoate, 2-3 parts of diphenylamine, 1-2 parts of titanate coupling agent TMC-TTS, 30-35 parts of barium sulfate powder, 1-2 parts of anti-aging agent AW, 1-2 parts of 2-thiol benzimidazole, 5-8 parts of chlorinated paraffin, 1-2 parts of accelerant DM, 1-2 parts of silane coupling agent KH550, 0.8-1 part of crosslinking agent TAC, 15-25 parts of nano bauxite, 1-3 parts of polypropylene glycol adipate, 2-4 parts of hydrated zinc borate, 4-6 parts of epoxy butyl oleate, 0.8-1 part of vulcanizing agent DCBP, 2-3 parts of modified sepiolite and 4-6 parts of dipentamethylenethiuram hexasulfide. Through the invention, the produced low-smoke flame retardant cable material for locomotive has excellent physical performance, stable size and low shrinkage; and the tensile strength, the tear strength and the resilience force of the product are greatly improved.

Description

technical field [0001] The invention mainly relates to a rubber sheath material and a preparation method thereof, in particular to a low-smoke flame-retardant cable material for locomotives and a preparation method thereof. Background technique [0002] In 2002, the European Union formulated the "Electronic Waste Disposal Law" with two directives, one of which is the "Directive on Prohibiting the Use of Certain Hazardous Substances in Electrical and Electronic Equipment" (ROHS). The ROHS Directive requires that electrical and electronic products put on the EU market after July 1, 2006 must not contain six harmful substances including lead, mercury, cadmium, hexavalent chromium, polybrominated biphenyls and polybrominated diphenyl ethers. Correspondingly, at the beginning of 2004, the Ministry of Information Industry of the People’s Republic of China formulated the Measures for the Prevention and Control of Pollution by Electronic Information Products (referred to as the Meas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L11/00C08L9/00C08L9/02C08K13/06C08K9/04C08K9/02C08K3/34C08K5/11C08K3/30C08K3/38C08K5/40H01B7/295
Inventor 姜睿
Owner 蚌埠尚维知识产权运营有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap