Preparation method for environment-friendly anti-flaming anti-static polyethylene pipeline

A flame retardant, antistatic, polyethylene technology, used in pipes, rigid pipes, mechanical equipment, etc., can solve the problems of moisture absorption, poor, and difficult to obtain the flame retardant effect of closed-cell carbon layer.

Inactive Publication Date: 2013-05-01
CHONGQING XINGTELONG IND CO LTD
View PDF9 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these flame retardants have the disadvantages of moisture absorption, closed-pore carbon layer is not easy to obtain during combustion and decomposition process, and the flame retardant effect is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for environment-friendly anti-flaming anti-static polyethylene pipeline

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Prepare environmentally friendly flame-retardant and antistatic polyethylene pipes according to the following steps

[0039] 1) Accurately weigh each component according to the following component distribution ratio, and then fully dry;

[0040] 97 parts by weight of high-density polyethylene resin,

[0041] Mg(OH) 2 39 parts by weight,

[0042] 35 parts by weight of phenoxy polyphosphazene elastomer,

[0043] Nanoscale calcium carbonate 37 parts by weight,

[0044] 6 parts by weight of nano-scale carbon black,

[0045] Silane coupling agent KH-570 5 parts by weight,

[0046] 1 part by weight of pentaerythritol stearic acid amine,

[0047] Antioxidant 736 0.8 parts by weight,

[0048] Antioxidant 168 0.6 parts by weight,

[0049] Its preparation method is as follows:

[0050] 2) First take 30 parts by weight of high-density polyethylene resin, 12 parts by weight of phenoxy polyphosphazene elastomer, 0.4 parts by weight of pentaerythritol stearic acid...

Embodiment 2

[0057] Prepare environmentally friendly flame-retardant and antistatic polyethylene pipes according to the following steps

[0058] 1) Accurately weigh each component according to the following component distribution ratio, and then fully dry;

[0059] 99 parts by weight of high-density polyethylene resin,

[0060] Mg(OH) 2 35 parts by weight,

[0061] 39 parts by weight of phenoxy polyphosphazene elastomer,

[0062] 38 parts by weight of nano calcium carbonate,

[0063] 7 parts by weight of nano-scale carbon black,

[0064] Silane coupling agent KH-570 6 parts by weight,

[0065] 1.2 parts by weight of pentaerythritol stearic acid amine,

[0066] Antioxidant 736 0.9 parts by weight,

[0067] Antioxidant 168 0.8 parts by weight,

[0068] Its preparation method is as follows:

[0069] 2) First take 40 parts by weight of high-density polyethylene resin, 17 parts by weight of phenoxy polyphosphazene elastomer, 0.5 parts by weight of pentaerythritol stearic aci...

Embodiment 3

[0076] Prepare environmentally friendly flame-retardant and antistatic polyethylene pipes according to the following steps

[0077] 1) Accurately weigh each component according to the following component distribution ratio, and then fully dry;

[0078] 103 parts by weight of high-density polyethylene resin,

[0079] Mg(OH) 2 31 parts by weight,

[0080] 42 parts by weight of phenoxy polyphosphazene elastomer,

[0081] Nanoscale calcium carbonate 40 parts by weight,

[0082] 8 parts by weight of nano-scale carbon black,

[0083] Silane coupling agent KH-570 7 parts by weight,

[0084] 1.3 parts by weight of pentaerythritol amine stearate,

[0085] Antioxidant 736 1 part by weight,

[0086] Antioxidant 168 0.9 parts by weight,

[0087] Its preparation method is as follows:

[0088] 2) First take 50 parts by weight of high-density polyethylene resin, 20 parts by weight of phenoxy polyphosphazene elastomer, 0.6 parts by weight of pentaerythritol stearic acid am...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for an environment-friendly anti-flaming anti-static polyethylene pipeline. The preparation method comprises the following steps: selecting the following components: high-density polyethylene resin, Mg(OH)2, 35-42 weight parts of phenoxy polyphosphazene elastomer, nanoscale calcium carbonate, nanoscale carbon black, silane coupling agent KH-570, pentaerythritol stearic acid amide, antioxygen 736 and antioxygen 168; preparing polyethylene master batch, mixing through a high-speed mixer, and extruding and pelletizing through a double-screw extruder; and preparing into the pipeline through the steps of extruding through a molding machine, sizing, dragging, cooling-shaping and cutting. The anti-flaming anti-static polyethylene pipeline prepared according to the method provided by the invention has the advantages that the fire retardant is high in anti-flaming efficiency, the additive amount is small, no molten drop is generated during combustion and fuming volume is small, no harmful gas is generated, and the pipeline is anti-flaming while the comprehensive mechanical property is excellent.

Description

technical field [0001] The invention relates to a preparation method of an environmentally friendly flame-retardant and antistatic polyethylene pipe, in particular to a preparation method of an environmentally friendly flame-retardant and antistatic polyethylene pipe used for transporting flammable gases such as coal gas. Background technique [0002] Polyethylene pipe is one of the most common pipes. It has the advantages of low temperature impact resistance, chemical corrosion resistance and wear resistance. It is used in water supply, drainage, heating, gas supply, agricultural irrigation, water conservancy projects and various industrial installations. be widely used. Polyethylene (PE for short) refers to a polymer formed by free radical polymerization of ethylene monomers. It is one of the most productive general-purpose plastics. Electrically insulating and chemically resistant thermoplastic. Moreover, it is easy to form and process, and is widely used in wire and ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L85/02C08K13/02C08K3/22C08K3/26C08K3/04C08K5/20B29C47/92F16L9/12B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 刘芝英
Owner CHONGQING XINGTELONG IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com