Method for regulating luminescence characteristic of rare earth noctilucent fiber

A technology of luminous fiber and luminescent properties, which is applied in the field of textile technology and optics, can solve the problems of high burning temperature, limited range of pigment selection, and high heat resistance requirements of inorganic transparent pigments, and achieve low heat resistance and easy operation , the effect of easy adjustment of the level

Inactive Publication Date: 2013-04-10
JIANGNAN UNIV
View PDF10 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation of colored light-storage luminescent base material here is to add inorganic pigments in the preparation process of luminescent base material, and its burning temperature is as high as 900~1000°C, which requires high heat resistance of inorganic transparent color materials, which limits the process to a certain extent. Selection range of pigments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for regulating luminescence characteristic of rare earth noctilucent fiber
  • Method for regulating luminescence characteristic of rare earth noctilucent fiber
  • Method for regulating luminescence characteristic of rare earth noctilucent fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Take 5 parts of rare earth strontium aluminate long afterglow luminous material, 94.85 parts of PET polymer chips, add 0.15 parts of cobalt violet (PV-514), mix at 900r / min, melt and granulate at 265°C, dry at 105°C, Melt spinning at 290°C to obtain rare earth luminous fiber with adjusted luminous properties. The luminous wavelength of the tested fiber is 512nm, and the afterglow initial test brightness is 0.876Lx. The emission spectrum and afterglow curve are as attached figure 1 , 2 shown.

Embodiment 2

[0020] Take 5 parts of rare earth strontium aluminate long afterglow luminous material, 94.85 parts of PET polymer chips, add 0.15 parts of cobalt chromium blue (PBl-536), mix at 900r / min, then melt and granulate at 265°C, and dry at 105°C , Melt spinning at 290°C to obtain rare earth luminous fiber with adjusted luminous properties. The luminous wavelength of the tested fiber is 514nm, and the afterglow initial test brightness is 0.985Lx. The emission spectrum and afterglow curve are as attached image 3 , 4 shown.

Embodiment 3

[0022] Take 8 parts of alkaline earth silicate long-lasting luminescent material, 90 parts of PET polymer slices, add 0.01 part of inorganic composite pigment cobalt green, mix at 700r / min, then melt and granulate at 285°C, dry at 100°C, and then dry at 300°C Melt spinning to obtain rare earth luminous fiber with adjusted luminous properties.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thermal resistanceaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for regulating the luminescence characteristic of a rare earth noctilucent fiber, and belongs to the fields of textile technology and optical technology. During the manufacturing process of the rare earth noctilucent fiber, an inorganic compound pigment in a definite proportion is added, so that the luminescence characteristic of the rare earth noctilucent fiber is changed. Therefore, the fiber can present rich and colorful colors in the daytime and also can emit rich and colorful light at night. The pigment is added during the preparation process of a spinning solution or a spinning masterbatch, so that the requirement for the heat-resisting performance of the pigment is lower relatively. According to the invention, the luminescence characteristic of the rare earth noctilucent fiber is regulated by changing the adding category and the adding proportion of the pigment. The method also has the advantages of easiness in process control and easiness in regulation level control.

Description

technical field [0001] The invention relates to a method for adjusting the luminescence characteristics of rare earth luminous fibers, and belongs to the fields of textile technology and optical technology. Background technique [0002] Rare earth luminous fiber is a kind of functional fiber that glows at night made of rare earth luminescent materials. As long as the fiber absorbs visible light for 10 minutes, it can continue to glow for more than 10 hours in a dark environment. It is non-toxic, non-polluting, and environmentally friendly, and is widely used in construction and decoration, transportation, night operations and other fields. [0003] In order to achieve a specific color, the usual practice is to dye the fiber, which to a certain extent has caused pollution to the environment; or add a colored light-storage type luminous base material to achieve colored and colored light effects. The preparation of colored light-storage luminescent base material here is to add...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F1/04D01F1/10D01F6/92C09K11/64C09K11/59
Inventor 葛明桥张技术
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap