High-CTI (Creepage Tracking Index) high-GWIT (Glow-Wire Ignition Temperature) environmental-friendly flame-retardant glass fiber reinforced PP/PA612 (Polypropylene/Polyamide 612) alloy material and preparation method thereof

A PA612, alloy material technology, applied in the field of PP/PA612 alloy material and its preparation, to achieve the effects of short residence time, lower friction coefficient, and prevention of decomposition

Inactive Publication Date: 2013-02-27
SHANGHAI SUNNY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no report on the environmentally friendly flame-retardant glass fiber reinforced PP / PA612 alloy material with high CTI value and high GWIT value and excellent comprehensive performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-CTI (Creepage Tracking Index) high-GWIT (Glow-Wire Ignition Temperature) environmental-friendly flame-retardant glass fiber reinforced PP/PA612 (Polypropylene/Polyamide 612) alloy material and preparation method thereof
  • High-CTI (Creepage Tracking Index) high-GWIT (Glow-Wire Ignition Temperature) environmental-friendly flame-retardant glass fiber reinforced PP/PA612 (Polypropylene/Polyamide 612) alloy material and preparation method thereof
  • High-CTI (Creepage Tracking Index) high-GWIT (Glow-Wire Ignition Temperature) environmental-friendly flame-retardant glass fiber reinforced PP/PA612 (Polypropylene/Polyamide 612) alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Example 1 Preparation of PP / PA612 alloy material of the present invention (1)

[0059] Weigh the raw materials by weight percentage: PP 25%, PA612 (intrinsic viscosity of 2.8dl / g) 25.1%, compound flame retardant 12%, antimony trioxide 4%, alkali-free glass treated with silane coupling agent Fiber 30%, maleic anhydride grafted PP 3%, antioxidant 1330 0.4%, iron oxide 0.5%; put the weighed raw materials into a high-mixer, mix for 5 minutes, and discharge; use a twin-screw extruder to extrude The granulation is produced, the processing temperature is 220-240°C, and the screw rotation is 35HZ. The specific processing conditions are shown in the table below.

[0060]

Embodiment 2

[0061] Example 2 Preparation of PP / PA612 alloy material of the present invention (2)

[0062] Weigh the raw materials by weight percentage: PP 25%, PA612 (intrinsic viscosity of 2.8dl / g) 23%, compound flame retardant 12%, antimony trioxide 4%, alkali-free glass treated with silane coupling agent Fiber 30%, maleic anhydride grafted PP 5%, antioxidant 1330 0.4%, iron oxide 0.6%; put the weighed raw materials into a high-mixer, mix for 2 minutes, and discharge; use a twin-screw extruder to extrude The granulation is produced, the processing temperature is 220-240°C, and the screw rotation is 35HZ. The specific processing conditions are shown in the table below.

[0063]

Embodiment 3

[0064] Example 3 Preparation of PP / PA612 alloy material of the present invention (3)

[0065] Weigh the raw materials by weight percentage: PP 23%, PA612 (intrinsic viscosity 2.8dl / g) 22%, compound flame retardant 20%, antimony trioxide 4.3%, alkali-free glass treated with silane coupling agent Fiber 20%, maleic anhydride grafted PP 10%, antioxidant 1330 0.1%, iron oxide 0.6%; put the weighed raw materials into a high-mixer, mix for 2 minutes, and discharge; use a twin-screw extruder to extrude The granulation is produced, the processing temperature is 220-240°C, and the screw rotation is 30HZ. The specific processing conditions are shown in the table below.

[0066]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-CTI (Creepage Tracking Index) high-GWIT (Glow-Wire Ignition Temperature) environmental-friendly flame-retardant glass fiber reinforced PP / PA612 (Polypropylene / Polyamide 612) alloy material which is prepared from the following raw materials in percentage by weight: 23%-41% of PP, 22%-41% of PA612, 6%-20% of compound flame retardant, 3%-15% of antimony trioxide, 20%-30% of glass fibers, 2%-10% of compatilizer, 0.1%-1% of antioxidant and 0.1%-1% of oxide, wherein the compound flame retardant contains the following materials in percentage by weight: 50% of BPS (Brominated Polystyrene), 25% of magnesium hypophosphite and 25% of talcum powder. The invention also provides a preparation method of the high-CTI high-GWIT environmental-friendly flame-retardant glass fiber reinforced PP / PA612 alloy material. The high-CTI high-GWIT environmental-friendly flame-retardant glass fiber reinforced PP / PA612 alloy material provided by the invention has the advantages that the GWIT value is increased by 50-100 DEG C due to adoption of a novel flame-retardant compounding system, so that the material can pass 850 DEG C glow-wire test; the GWIT value is also obviously increased through the addition of the glass fibers; moreover, and impact property and ageing-resistant property are improved, processing fluidity and smoothness are increased and friction factor is lowered.

Description

technical field [0001] The invention relates to a PP / PA612 alloy material and a preparation method thereof, in particular to an environmentally friendly flame-retardant glass fiber reinforced PP / PA612 alloy material with a high CTI value and a high GWIT value and a preparation method thereof. Background technique [0002] Nylon (Nylon), Chinese name polyamide, English name polyamide, referred to as PA, is the general term for thermoplastic resins containing repeated amide groups—[NHCO]—on the main chain of the molecule, and its naming is determined by the specific number of carbon atoms in the synthetic monomer , such as PA-6, PA-66, PA-1010, PA-610. PA has high crystallinity and obvious melting point; high surface hardness, wear resistance, small friction coefficient, self-lubrication and noise reduction; good low temperature performance and certain heat resistance (can be used below 100°C); non-toxic , Odorless, no mildew, self-extinguishing, good weather resistance, but ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L77/06C08L25/06C08K13/06C08K9/06C08K7/14C08K3/22C08K3/32C08K3/34B29C47/92B29C48/92
CPCB29B7/46B29B7/72B29B7/7461B29B7/90B29B9/06B29B9/12B29B9/14B29C48/04B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895C08K3/2279C08K3/32C08K3/346C08K5/13C08K7/14C08K9/06C08K2003/2265C08K2003/326C08L23/12C08L25/18C08L51/06C08L77/06C08L91/00C09K21/14
Inventor 郭建鹏孟诚铭
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com