A kind of high cti value, high gwit value environmental protection flame retardant glass fiber reinforced pp/ppo alloy material and preparation method thereof

An alloy material and an environmentally friendly technology are applied in the field of environmentally friendly flame retardant glass fiber reinforced PP/PPO alloy materials and their preparation to achieve the effects of improving smoothness, improving processing fluidity and preventing decomposition

Inactive Publication Date: 2015-08-05
SHANGHAI SUNNY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, there is no report on the environmentally friendly flame-retardant glass fiber reinforced PP / PPO alloy material with high CTI value and high GWIT value and excellent comprehensive performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high cti value, high gwit value environmental protection flame retardant glass fiber reinforced pp/ppo alloy material and preparation method thereof
  • A kind of high cti value, high gwit value environmental protection flame retardant glass fiber reinforced pp/ppo alloy material and preparation method thereof
  • A kind of high cti value, high gwit value environmental protection flame retardant glass fiber reinforced pp/ppo alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Example 1 Preparation of PP / PPO alloy material of the present invention (1)

[0061] Weigh raw materials by weight percentage: PP 25%, PPO (intrinsic viscosity: 1.0dl / g) 25.1%, compound flame retardant 12%, antimony trioxide 4%, alkali-free glass treated with silane coupling agent Fiber 30%, maleic anhydride grafted SEBS 3%, antioxidant 1330 0.4%, iron oxide 0.5%; put the weighed raw materials into a high mixer and mix for 5 minutes, and discharge; extrude with a twin-screw extruder For granulation, the processing temperature is 220-240°C, the screw speed is 35HZ, and the specific processing conditions are shown in the table below.

[0062]

Embodiment 2

[0063] Example 2 Preparation of PP / PPO alloy material of the present invention (2)

[0064] Weigh raw materials by weight percentage: PP 25%, PPO (intrinsic viscosity: 1.0dl / g) 23%, compound flame retardant 12%, antimony trioxide 4%, alkali-free glass treated with silane coupling agent Fiber 30%, maleic anhydride grafted SEBS 5%, antioxidant 1330 0.4%, iron oxide 0.6%; put the weighed raw materials into a high mixer and mix for 2 minutes, and discharge; extrude with a twin-screw extruder For granulation, the processing temperature is 220-240°C, the screw speed is 35HZ, and the specific processing conditions are shown in the table below.

[0065]

Embodiment 3

[0066] Example 3 Preparation of PP / PPO alloy material of the present invention (3)

[0067] Weigh raw materials by weight percentage: PP 23%, PPO (intrinsic viscosity: 1.0dl / g) 22%, compound flame retardant 20%, antimony trioxide 4.3%, alkali-free glass treated with silane coupling agent Fiber 20%, maleic anhydride grafted SEBS 10%, antioxidant 1330 0.1%, iron oxide 0.6%; put the weighed raw materials into a high mixer and mix for 2 minutes, and discharge; extrude with a twin-screw extruder For granulation, the processing temperature is 220-240°C, the screw speed is 30HZ, and the specific processing conditions are shown in the table below.

[0068]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-CTI (Creepage Tracking Index) high-GWIT (Glow-Wire Ignition Temperature) environmental-friendly flame-retardant glass fiber reinforced PP / PPO (Polypropylene / Polyphenylene Oxide) alloy material which is prepared from the following raw materials in percentage by weight: 23%-41% of PP, 22%-41% of PPO, 6%-20% of compound flame retardant, 3%-15% of antimony trioxide, 20%-30% of glass fibers, 2%-10% of compatilizer, 0.1%-1% of antioxidant and 0.1%-1% of oxide, wherein the compound flame retardant contains the following materials in percentage by weight: 50% of BPS (Brominated Polystyrene), 25% of magnesium hypophosphite and 25% of talcum powder. The invention also provides a preparation method of the high-CTI high-GWIT environmental-friendly flame-retardant glass fiber reinforced PP / PPO alloy material. The high-CTI value high-GWIT value environmental-friendly flame-retardant glass fiber reinforced PP / PPO alloy material provided by the invention has the advantages that the GWIT value is increased by 50-100 DEG C by adoption of a novel flame-retardant compounding system, so that the material can pass 850 DEG C glow-wire test; the GWIT value is also obviously increased through the addition of the glass fibers; in addiiton, impact property and ageing-resistant property are improved, processing fluidity and smoothness are increased and friction factor is lowered.

Description

Technical field [0001] The present invention involves an environmentally friendly flame retardant glass fiber enhancement PP / PPO alloy material and its preparation methods. Specifically, it is a high CTI value, high GWIT value environmental flame retardant glass fiber enhancement PP / PPO alloy material and their preparation methodsEssence Background technique [0002] PPO, a Chinese name polyzhenylene, is one of the world's five major general engineering plastics. It has the advantages of high rigidity, high heat resistance, difficulty, high strength, excellent electrical performance, abrasion resistance, non -toxic, pollution resistance and other.In addition, PPO is one of the varieties with the least consumption of engineering plastic intermediaries and the smallest dielectric loss. It is almost not affected by temperature and humidity. It can be used in the field of low, medium and high -frequency electric fields.The temperature is -170 ° C.PPO's relative density (PPO / PA simila...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L71/12C08L25/06C08K13/06C08K9/06C08K7/14C08K3/22C08K3/32C08K3/34B29C47/92B29C48/92
CPCB29B9/14B29B9/12B29B9/06B29C47/92B29B7/72B29B7/46C08L23/12B29C47/0011B29B7/90C09K21/14B29B7/7461B29C48/04B29C48/40C08K3/34C08K7/14C08L51/006C08L71/02
Inventor 郭建鹏王尹杰孟诚铭
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com