Chlorinated polyvinyl chloride waterproof coiled material and preparation method thereof

A technology of chlorinated polyvinyl chloride and waterproof membrane, which is applied in the field of waterproof material preparation, can solve the problems of poor elongation at break, no flame retardancy, poor aging resistance, etc., and achieve large friction coefficient and strong deformation adaptability , the effect of a wide range of temperature adaptation

Inactive Publication Date: 2012-12-12
天津市耀新科技发展有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, it has flame retardancy, but the traditional polymer waterproof roll cannot meet the requirements of the current construction due to defects such as lack of flame retardancy, poor aging resistance, and poor elongation at break.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chlorinated polyvinyl chloride waterproof coiled material and preparation method thereof
  • Chlorinated polyvinyl chloride waterproof coiled material and preparation method thereof
  • Chlorinated polyvinyl chloride waterproof coiled material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Recipe and preparation method:

[0022] 1. Formulation:

[0023]

[0024] 2. Preparation method:

[0025] (1) Measure all the raw materials according to the formula ratio and put them into the high-speed mixer for mixing evenly, then put them into the hopper of the twin-screw extruder, and follow the instructions in the accompanying drawings figure 1 The technical process for the preparation of chlorinated polyethylene waterproofing membrane is extrusion granulation.

[0026] (2) Put the prepared chlorinated polyvinyl chloride waterproof membrane pellets into the barrel of the extruder calendering unit for extrusion and calendering to make chlorinated polyvinyl chloride waterproof membrane.

[0027] The main properties of the prepared chlorinated polyethylene waterproof coiled material of the present invention:

[0028] serial number project index 1 Tensile strength MPa 18.76 2 Elongation at break%≥ 629 3 Dimensional cha...

Embodiment 2

[0031] Recipe:

[0032]

[0033] Preparation method is identical with embodiment 1

Embodiment 3

[0035] Recipe:

[0036]

[0037] Preparation method is identical with embodiment 1

[0038] Performance Comparison Table

[0039] performance Example 1 Example 2 Example 3 Tensile strength MPa 18.76 16.63 17.67 Elongation at break% 629 587 613

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chlorinated polyvinyl chloride waterproof coiled material and a preparation method thereof. The material is composed of a base material of chlorinated polyvinyl chloride, and added materials of a plasticizing agent, a toughening agent, a filling agent, and other additives. An extrusion calendar molding method is adopted, and the chlorinated polyvinyl chloride waterproof coiled material is produced. The chlorinated polyvinyl chloride waterproof coiled material provided by the invention has various excellent comprehensive economic and technical performance indicators such as excellent water resistance, excellent flame retardance, anti-leakage performance, weatherability, high tensile strength, high elongation, aging resistance, high deformation adaptability, wide temperature adaptation range, high adhesive strength, long service life, easy construction, low cost, and the like. The material can be used in waterproofing works of architectural roofing, bridge deck concrete, subways, and roads.

Description

technical field [0001] The invention belongs to the field of waterproof material preparation, and in particular relates to a chlorinated polyvinyl chloride waterproof coiled material and a preparation method thereof. Background technique [0002] Chlorinated polyvinyl chloride, referred to as CPVC, is obtained by chlorination and modification of polyvinyl chloride (PVC) resin. The product is white or light yellow tasteless, odorless, non-toxic loose particles or powder. After the PVC resin is chlorinated, the irregularity of the molecular chain arrangement increases and the polarity increases, which increases the solubility and chemical stability of the resin, thereby improving the heat resistance of the material and resistance to acids, alkalis, salts, oxidants, etc. corrosion performance. Improve the mechanical properties of the heat distortion temperature of the resin, the chlorine content increased from 56.7% to 63-69%, the Vicat softening temperature increased from 72-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/28C08L9/06C08L9/02C08K13/02C08K5/12C08K3/26
Inventor 刘耀俭孙燕峰
Owner 天津市耀新科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap