Polyacrylic acid type calcium nitrite corrosion inhibitor and preparation method thereof

A technology of calcium nitrite and polyacrylic acid, applied in the field of inorganic rust inhibitor, can solve the problems of low rust inhibition efficiency, nitrite loss, low rust inhibition efficiency, etc. Good anti-rust effect

Active Publication Date: 2012-03-28
SHENZHEN UNIV
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it is also with the continuation of use that some shortcomings exposed by calcium nitrite during use have caused people to reflect on the choice of this type of rust inhibitor.
[0009] According to the construction process of calcium nitrite, it is a direct-incorporated rust inhibitor. Combined with some physical and chemical properties of calcium nitrite itself, this construction process leads to the main problems in its use: 1. It is easy to be oxidized ; Because the valence of nitrogen element has not reached the maximum value, the chemical properties of nitrite ion are relatively active, and...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyacrylic acid type calcium nitrite corrosion inhibitor and preparation method thereof
  • Polyacrylic acid type calcium nitrite corrosion inhibitor and preparation method thereof
  • Polyacrylic acid type calcium nitrite corrosion inhibitor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] The equipment adopts extrusion spheronizer (Shenzhen Xinyite Technology Co., Ltd., LTAES 380 type)

[0061] 1. Capsule core preparation: According to the weight ratio of the V capsule core in Table 1, firstly mix calcium nitrite and microcrystalline cellulose fully, add Tween 80 after mixing, knead evenly and then add in portions Pure water, so that pure water can exist evenly in the mixture.

[0062] 2. Extrusion and thinning: Turn on the extrusion spheronizer, start the extrusion mode of the equipment, feed materials at the feeding port, and start the cooling water circulation mode of the equipment to prevent the excessive temperature of the extrusion cylinder from affecting the discharge.

[0063] 3. Discharging and rounding: Use a tray to hold the extruded rice strip-shaped capsule core material, pour it into the roller in the equipment, start the rounding mode of the equipment, adjust the rotation rate of the rounding (the speed is controlled at 700-1100r / min), and...

Embodiment 2

[0069] 1. Capsule core preparation: according to the weight ratio of No. III capsule core in Table 1,

[0070] 2. Coating solution preparation: select the weight ratio of No. III coating in Table 2, and weigh the coating material according to the weight ratio of the capsule core to the dry matter of the coating material as 1:1.

[0071] Other processing steps, parameter and equipment are with embodiment 1.

Embodiment 3

[0073] 1. Capsule core preparation: according to the weight ratio of No. I capsule core in Table 1,

[0074] 2. Coating solution preparation: select the weight ratio of the V coating in Table 2, and weigh the coating material according to the weight ratio of the capsule core to the dry matter of the coating material as 1:4.

[0075] Other processing steps, parameter and equipment are with embodiment 1.

[0076] 2. The particle size range of polyacrylic acid calcium nitrite corrosion inhibitor capsules:

[0077] The particle size of the polypropylene calcium nitrite microcapsules prepared by this method changes from 350 μm (corresponding capsule core material: the mass ratio of coating dry material=1: 0.25) to 1000 μm (corresponding capsule core material: coating dry material The mass ratio of = 1: 4)

[0078] 4. Microscopic morphology of polyacrylic acid calcium nitrite corrosion inhibitor capsules

[0079] The shape of the microcapsules was photographed with an optical mic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyacrylic acid type calcium nitrite corrosion inhibitor and a preparation method thereof. The polyacrylic acid calcium nitrite corrosion inhibitor has a capsule form, the capsule comprises a core and a coating, the core comprises calcium nitrite, a microcrystalline cellulose and tween 80, and the coating comprises a polyacrylic resin, talc, and hydroxypropyl methyl cellulose. The polyacrylic resin wrapped calcium nitrite corrosion inhibitor of the invention has a good stability, and the release rate of the microcapsule can be controllably optimized by changing the mass ratio between the core material and the coating material, so defects of easy loss and easy oxidation of the calcium nitrite corrosion inhibitor are effectively solved; and the polyacrylic acid type calcium nitrite corrosion inhibitor of the invention has the advantages of long valid period, good corrosion inhibition effect, and environmental protection.

Description

[technical field] [0001] The invention relates to an inorganic rust inhibitor, in particular to a polyacrylic acid calcium nitrite corrosion inhibitor and a preparation method thereof. [Background technique] [0002] The most widely used inorganic rust inhibitor in engineering today is mainly calcium nitrite. American Grace Company has done a lot of research on calcium nitrite since the 1970s, because it has no obvious negative impact on concrete, and it has become the mainstream rust inhibitor in the American and Japanese markets for a while. [0003] Calcium nitrite is a direct mixing type rust inhibitor. When in use, directly mix calcium nitrite into the concrete structure and stir evenly. Scholars at home and abroad have basically the same views on its mechanism of action. The chemical expression of its protective effect is as follows: [0004] Fe 2+ +OH - +NO - 2 =NO+γ-FeOOH (1) [0005] 2Fe 2+ +2OH - +2NO - 2 =2NO+Fe 2 o 3 +H 2 O (2) [0006] For the ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F11/00
Inventor 董必钦邢锋丁铸刘伟
Owner SHENZHEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap