UV-curable resin composition for transparent colored coated steel sheet and steel sheet utilizing the same

A technology for curing resins and compositions, applied in epoxy resin coatings, coatings, optics, etc., can solve problems such as rust resistance, weak bendability, and inability to provide transparency for steel products, and achieve the effect of improving productivity

Active Publication Date: 2011-11-30
POSCO CO LTD
View PDF8 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] However, the above-mentioned prior art uses inorganic antirust pigments to improve corrosion resistance, so there is a problem that not only cannot provide transparency to steel products, but also are inferior in rust resistance and bendability for preventing corrosion. weak

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0095] By mixing modified epoxy acrylate oligomer [CN 150 / 80, Sartomer, USA] 35g, urethane acrylate oligomer [UA-5221, HS Chemtron, Korea] 15g, tetrahydrofuryl methyl acrylate (THFA) [SR285 , Sartomer, U.S.], hexanediol diacrylate (HDDA) [Miramer M200, Miwon, Korea] 10g, photoinitiator [Darocur 1173, Ciba Chemicals, Switzerland] 8g, defoamer [TEGO Airex 920, Evonik , Germany] 0.5g, leveling agent [TEGO Rad 2250, Evonik, Germany] 0.5g and adhesion promoter 1g to prepare the coating composition. The compositions of the components used are shown in Table 1 below.

Embodiment 2

[0097]By mixing modified epoxy acrylate oligomer [CN 150 / 80, Sartomer, U.S.] 34g, urethane acrylate oligomer [CN 966J75, Sartomer, U.S.] 16g, isobornyl acrylate (IBOA) [SR506, Sartomer , U.S.] 30g, tripropylene glycol diacrylate (TPGDA) [Miramer M220, Miwon Corporation, Korea] 10g, photoinitiator [Darocur 1173, Ciba Chemicals, Switzerland] 8g, defoamer [TEGO Airex 920, Evonik , Germany] 0.5g, leveling agent [TEGO Rad 2250, Evonik, Germany] 0.5g and adhesion promoter 1g to prepare the coating composition. The compositions of the components used are shown in Table 1 below.

Embodiment 3

[0099] Modified by mixing epoxy acrylate oligomer [3020-A80, AGI, Taiwan] 35g, urethane acrylate oligomer [UA-5221, HS Chemtron, Korea] 15g, tetrahydrofurfuryl acrylate (THFA) [SR285, Sartomer, the U.S.] 30g, tetrahydrofuryl methyl acrylate (THFA) [SR285, Sartomer, the U.S.] 30g, hexanediol diacrylate (HDDA) [Miramer M200, Miwon, Korea] 11g, photoinitiator [Darocur 1173, Ciba Chemicals, Switzerland] 6g, defoamer [TEGO Airex 920, Evonik, Germany] 0.5g, leveling agent [TEGO Glide 440, Evonik, Germany] 0.5g and adhesion promoter 1g to prepare the coating composition. The compositions of the components used are shown in Table 1 below.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
wavelengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention relates to an ultraviolet curable resin composition comprising: 25 to 45 wt% modified epoxy acrylate oligomer; and 10 to 25 wt% urethane acrylate oligomer. The present invention can provide a metal sheet which is transparent, and which has corrosion resistance, impact resistance, scratch resistance, adhesion, anti-corrosion, and bendability (workability) by forming a coating film on the surface of metal materials such as steel materials, specifically steel sheets, using the ultraviolet curable resin composition of the present invention.

Description

technical field [0001] The present invention relates to an ultraviolet curable resin composition and a steel plate using the composition, and particularly relates to forming a coating film on the surface of a steel plate by utilizing an ultraviolet curable resin composition that is not only transparent but also provides adhesion, rust resistance and flexibility. It improves productivity, and can provide an ultraviolet curable resin composition for an environmentally friendly steel sheet without using a solvent, and a steel sheet using the composition. Background technique [0002] Generally, for steel materials such as steel sheets, a coating film is formed on the surface in order to protect the surface, prevent corrosion, and improve the appearance of the material. [0003] Typical methods for forming a coating film on steel materials such as steel sheets include a pre-coated metal (PCM, Pre-Coated Metal) method in which a resin composition such as paint is directly applied...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D175/04
CPCC09D151/08G03F7/027C09D163/10C08F283/008C08L63/10C09D175/16Y10T428/24975Y10T428/259Y10T428/31529C08L75/14C09D175/04
Inventor 金辰泰金相坤李在隆金正守权纹栽边昌世
Owner POSCO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com