Molten iron dephosphorization agent manufactured by using converter dry-method dust-removal ash as raw material

A technology of converter dry dust removal and water dephosphorization agent is applied in the direction of improving process efficiency, which can solve the problems of low lime slag formation rate, difficulty in lime slag formation, and low processing temperature, and achieve high CaO activity and slag basicity. And the effect of stable dephosphorization effect and fast slag formation

Inactive Publication Date: 2011-04-13
CENT IRON & STEEL RES INST
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the thermodynamic advantages of dephosphorization pretreatment in the molten iron stage are obvious, but due to the relatively low treatment temperature, lime slagging is relatively difficult and the rate of lime slagging is low. In order to achieve a certain slag alkalinity, lime consumption will be relatively high. Realize the smelting target of dephosphorization pretreatment final slag alkalinity of 2.0~2.5 and molten iron [P] less than 0.03% after dephosphorization pretreatment, lime consumption generally reaches 25kg / t~35kg / t, ore consumption 20kg / t~30kg / t, fluorite consumption is 3kg / t~5kg / t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Molten iron dephosphorization agent manufactured by using converter dry-method dust-removal ash as raw material
  • Molten iron dephosphorization agent manufactured by using converter dry-method dust-removal ash as raw material
  • Molten iron dephosphorization agent manufactured by using converter dry-method dust-removal ash as raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] According to the composition scope of the dephosphorization agent of the present invention, the production and practical application tests of the dephosphorization agent were carried out. Dephosphorization agent raw material converter ash accounted for 45% of the total mass, active lime powder accounted for 45%, fluorite powder accounted for 10%. A comparative test of conventional slagging agents was carried out.

[0029] Table 1 Dephosphorization agent composition / %

[0030] CaO

Fe 2 o 3

FeO

CaF 2

SiO 2

al 2 o 3

MgO

50.88

21.36

14.09

8.50

4.28

1.21

3.72

[0031] Put 200kg of pig iron into a 500kg intermediate frequency induction furnace. The induction furnace has the function of simulating top-blowing and bottom-blowing compound blowing. After the start of the test, the gun was lowered to blow oxygen, and steel scrap and pre-mixed slag were added...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a molten iron dephosphorization agent manufactured by using converter dry-method dust-removal ash as a raw material, which belongs to the technical field of steel making and molten iron pretreatment and is applicable to converter molten iron dephosphorization treatment. The dephosphorization agent comprises the following chemical components in percentage by weight: 45 to 65 percent of CaO, 15 to 35 percent of iron oxides (Fe2O3+FeO), 5 to 15 percent of CaF2 and 2 to 6 percent of SiO2, wherein the ratio of CaO to Fe2O3+FeO+CaF2 ranges from 1.0 to 3.0, and the ratio of CaO to SiO2 ranges from 9 to 16; and the hemispherical fusion temperature of the dephosphorization agent is not more than 1,200 DEG C. The raw material of the dephosphorization agent comprises 20 to 60 percent of converter dry-method dust-removal ash, 20 to 60 percent of active lime powder and 5 to 20 percent of fluorite powder. The dephosphorization agent has the advantages that: after the converter molten iron dephosphorization pretreatment is performed by using the dephosphorization agent, the P content can be kept below 0.030 percent; the converter dry-method dust-removal ash is recycled in a steel making process; and the cost of the converter dephosphorization pretreatment is reduced considerably.

Description

technical field [0001] The invention belongs to the technical field of steelmaking and molten iron pretreatment, and in particular relates to a molten iron dephosphorization agent using converter dry dust removal as raw material. Background technique [0002] The continuous development and progress of the society has led to an increasing demand for high-quality clean steel. Since the traditional ladle, torpedo tank car powder spraying dephosphorization process + converter slag-less refining process cannot meet the process requirements for large-scale, low-cost production of clean steel, converter dephosphorization The process flow of phosphorus pretreatment + less slag refining process to produce clean steel has been promoted and applied. The process flow of clean steel produced by converter dephosphorization pretreatment + less slag refining process is characterized by utilizing the characteristics of high-efficiency smelting of converters to realize mass production of clea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/064
CPCY02P10/20
Inventor 刘浏李峻佟溥翘吴伟郑丛杰高建军金振坚
Owner CENT IRON & STEEL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products