Method and device for modifying surface of polymer material

A polymer material and surface modification technology, applied in the field of polymer material surface modification, can solve the problems of unsatisfactory grafting effect on the surface of polymer materials, uncontrollable reaction temperature, and incapable of continuous production, etc. The effect of shortening the reaction time and improving the graft ratio

Active Publication Date: 2010-09-15
CHINESE TEXTILE ACAD
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the prior art, there are defects such as incapable of continuous production, uncontrollable reaction temperature, or unsatisfactory grafting effect on the surface of polymer materials in the method of using plasma initiation technology to modify the surface of polymer materials. In view of the above defects, the present invention is proposed The surface grafting method of polymer materials has the advantages of controllable graft polymerization temperature, short reaction time, ideal grafting effect and continuous processing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for modifying surface of polymer material
  • Method and device for modifying surface of polymer material
  • Method and device for modifying surface of polymer material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Plasma Initiated Vapor Phase Grafting of Acrylic Acid (AAc) on Polypropylene (PP) Films

[0049] Working conditions: argon, frequency 13.56MHz, power 100W.

[0050] Place the polypropylene film in the plasma processor, evacuate the system pressure to 50Pa, and the flow rate of the working gas argon is 800cm 3 / min, treated under the above conditions for 10min, the polypropylene film after plasma treatment was placed in the air at normal temperature and pressure for 50min to generate peroxide.

[0051] The polypropylene film placed in the air is placed in a reaction chamber with a pressure of 500Pa and a temperature of 60°C, and the liquid acrylic monomer (molecular weight 72.06g / mol; under normal temperature and pressure, density 1.05g / cm 3 ; under normal pressure, boiling point 141°C) preheated to 70°C in advance, the preheated liquid monomer enters the above reaction chamber and immediately vaporizes, the flow rate of the gaseous monomer is controlled at 2000cm 3 / m...

Embodiment 2

[0053] Plasma Initiated Vapor Phase Grafting of Acrylic Acid (AAc) on Polypropylene (PP) Films

[0054] Working conditions: argon, frequency 40KHz, power 600W.

[0055] Place the polypropylene film in the plasma processor, evacuate the system pressure to 50Pa, and the flow rate of the working gas argon is 100cm 3 / min, under the above conditions for 10min, the plasma treatment ends.

[0056] The polypropylene film after plasma treatment is placed in a reaction chamber with a pressure of 50 Pa and a temperature of 50°C. The liquid acrylic monomer is preheated to 70°C in advance. The flow rate of the body is controlled at 500cm 3 / min, the grafting reaction time is 15min, after the reaction is completed, the gaseous monomer supply is stopped first, the vacuum is continued for 1min, the atmosphere is connected, the reaction chamber returns to normal pressure, and the modified polypropylene film is taken out.

Embodiment 3-6

[0058] The technological process of embodiment 3-6 and part technological parameter are with embodiment 1, and different technological parameter is as described in the following table:

[0059] Process conditions

[0060] Description: PP means polypropylene; PBT means polybutylene terephthalate; PTFE means polytetrafluoroethylene; PE polyethylene; PPS polyphenylene sulfide; AAc means acrylic acid; HEMA means methacrylic acid-2-hydroxyethyl ester; GMA means glycidyl methacrylate; MAAc methacrylic acid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Boiling pointaaaaaaaaaa
Densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for modifying the surface of a polymer material, which comprises the following steps of: performing surface plasma treatment on the polymer material; and putting the treated polymer material into a gaseous phase grafting reaction device preheated to between 50 and 150 DEG C, and then introducing gaseous or atomized monomers into the device to perform gaseous phase grafting reaction with the surface of the treated polymer material. A device for the reaction comprises a plasma grafting device, and the plasma grafting device comprises a polymer material surface plasma treatment device and a plasma-treated polymer material surface gaseous phase grafting reaction device. The device is characterized in that a temperature control system is arranged in the plasma grafting device. The device and the method for grafting polymerization have the advantages of controllable temperature, short polymerization reaction time, ideal grafting effect, continuous treatment in the industry and the like.

Description

technical field [0001] The present invention relates to a method for surface modification of polymer materials, more specifically, to a method for surface modification of polymer materials using plasma-induced graft polymerization, the polymerization process is a gas phase grafting process, and also relates to A device used during the surface modification of polymers. Background technique [0002] Plasma technology has been widely used in the field of surface modification of various materials. It is usually divided into atmospheric pressure plasma technology and low pressure plasma technology. These two technologies have their own advantages in practical applications: the former can be used under atmospheric pressure conditions It can work under the ground without a closed cabin, and can realize continuous production with low cost; the latter is easy to control, uses a wide range of working gases, easy to adjust the treatment mode, and has uniform treatment effects. However...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J7/16
Inventor 任婉婷李鑫
Owner CHINESE TEXTILE ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com