Welding agent for braze, braze method and printing substrate

A brazing method and flux technology, which is applied in the field of flux, brazing method and printed substrate, can solve the problems of solder joint strength insulation resistance reduction, brazing and printed substrate reliability damage, short circuit, etc., to achieve good brazing performance, Improves stability, prevents drastic reduction in effects

Active Publication Date: 2009-12-23
HARIMA CHEM INC
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, when the flux containing a predetermined amount of metal salt as described above is stored for a long period of time, problems such as a significant decrease in the joint strength of the solder and the insulation resistance of the soldered area occur compared with the flux immediately after production.
If the insulation resistance of the soldering area is reduced, for example, a short circuit is likely to occur in the soldering area, which will damage the reliability of soldering and printed circuit boards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding agent for braze, braze method and printing substrate

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1～8 and comparative example 1～7

[0046] [Choice of Copper Salt and Active Agent]

[0047] As the metal salt, the following are selected.

[0048] A:(C 17 h 35 COO) 2 Cu

[0049] B:(C 7 h 15 COO) 2 Cu

[0050] C:(C 21 h 43 COO) 2 Cu

[0051] D:(C 17 h 35 COO) 2 Pb

[0052] As the active agent, the following substances were selected.

[0053] E: C 7 h 15 COOH

[0054] F: C 17 h 35 COOH

[0055] G: C 21 h 43 COOH

[0056] H:(CH 3 ) 2 CHNH 2 ·HCl

[0057] Here, the order of acidity is H>E>F>G.

[0058] [Preparation of Rosin Flux]

[0059] WW grade Toichiru rosin 70 parts by weight

[0060] 25 parts by weight of hexyl carbitol

[0061] 5 parts by weight of hydrogenated castor oil

[0062] Mix the materials according to the above formula, heat to 120°C to melt, cool to room temperature, and prepare viscous flux.

[0063] [Preparation of acrylic flux]

[0064] Acrylic resin (Pararoid B-48N manufactured by Romde Haus Co., Ltd.) 50 parts by weight of hexyl carbitol 45 parts by weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

PROBLEM TO BE SOLVED: To provide a flux for soldering in which the preservation stability of the flux is increased, a soldering method using the same and a printed board. SOLUTION: The flux contains a resin having film forming ability, an activator and a solvent and is used when soldering is performed on the printed board to which electroless nickel plating is applied. The flux contains organic acid metallic salt of 0.1-20 wt.% to the total amount of the flux and, the activator is the same organic acid as an organic acid which comprises the organic acid metallic salt or an organic acid which is lower than it in acidity. Thus, the stability of the organic acid metallic salt is increased and high joining strength is maintained for a long term. COPYRIGHT: (C)2006,JPO&NCIPI

Description

technical field [0001] The present invention relates to a soldering flux used when soldering various electronic components to a printed circuit board, in particular to a flux, a soldering method and a printing process used for soldering on a copper pad of a printed circuit board subjected to electroless nickel plating. substrate. Background technique [0002] Conventionally, when soldering an electronic component to a printed circuit board, tin-lead alloy solder or lead-free solder is used for soldering on copper lands formed on the printed circuit board. In order to prevent oxidation of copper, electroless nickel plating is often performed on the surface of the above-mentioned pad. [0003] However, since hypophosphite is used as a reducing agent when electroless nickel plating is performed on the above-mentioned pads, a trace amount of phosphide remains in the nickel plating layer. [0004] Therefore, when a solder alloy is used for brazing on an electroless nickel-plate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/36B23K1/00H05K3/34
CPCB23K35/0244B23K35/24B23K35/36B23K2101/42
Inventor 池田一辉入江久夫岛俊典穴田隆昭石川俊辅
Owner HARIMA CHEM INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com