Steel for low temperature and high tenacity structure use and its production method

A technology of structural steel and a manufacturing method, applied in the field of structural steel, can solve problems such as high cost and complex processing technology, and achieve the effect of reducing manufacturing cost

Inactive Publication Date: 2008-06-04
BAOSHAN IRON & STEEL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In short, the composition and processing technology of the existing low-temperature high-toughness structural steel are complex and costly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel for low temperature and high tenacity structure use and its production method
  • Steel for low temperature and high tenacity structure use and its production method
  • Steel for low temperature and high tenacity structure use and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] Examples see figure 1 ,Table 2.

[0038] The steel type designed by the present invention does not need to add elements such as above precious Ni, Cr or Mo, only needs to slightly increase very cheap Si (extremely cheap. Solid solution strengthening, reduces bainite transformation point, and makes bainite C The curve moves to the right, inhibits the decomposition of supercooled austenite, increases the volume fraction of retained austenite and stabilizes austenite, promotes the formation of carbon-rich austenite film between ferrite in bainite, and improves toughness), Mn (Cheap. Strongly reduce bainite point, weakly reduce martensite point, improve hardenability and strength) and trace amounts of Nb and Ti (Nb and Ti are microalloying elements, which can control the growth of grains by precipitation Large, improve strength) and other elements and a certain controlled rolling and controlled cooling process (TMCP), can meet the requirements of better strength and toughn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a low-temperature high ductility constructional steel, wherein the chemical constituents include (by weight percent): C 0.04-0.08, Si 0.60-0.80, Mn 1.65-2.15, Nb 0.055-0.075, Ti 0.010-0.020, AlT 0.025-0.045, P<=0.012, S<=0.003, O<=0.0015, N 0.008-0.012, balancing Fe and unavoidable foreign substance. The preparation method comprises the steps of smelting, refining, casting, billet reheating, rolling, fast cooling, and finishing.

Description

technical field [0001] The invention belongs to the field of structural steel, in particular to a low-temperature high-toughness structural steel and a manufacturing method thereof. Background technique [0002] As the demand for long-distance transportation such as petroleum gas and natural gas continues to increase, the manufacture of liquefaction devices and storage equipment requires more and more low-temperature-resistant, high-strength, and high-toughness steels. In addition to high strength (yield strength ≥ 390MPa), it must also have good low temperature toughness. According to general standards, the designed operating temperature is lower than -110°C, even reaching -165°C. [0003] Table 1 is the contrast of the present invention with the specific regulations of the Det Norske Veritas (DNV) ship classification specification to low temperature and ultra-low temperature ductile steel mechanical properties and design working temperature (not including NV9Ni steel, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/14C21D6/00C21D7/13
Inventor 王巍
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.