Core-sheel structure M(1-x)Y2S4:Ax/ZnS quantum dot and its prepn process

A technology of Y2S4 and quantum dots, which is applied in the direction of chemical instruments and methods, luminescent materials, etc., can solve the problems affecting the quantum yield, and achieve the effect of safe and easy-to-obtain raw materials, good stability, and low price

Inactive Publication Date: 2007-06-06
TIANJIN UNIVERSITY OF TECHNOLOGY
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, due to the large number of defects on the surface of quantum dots that are usually prepared, the quantum yield is affected.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] with Ca 0.9 Y 2 S 4 :Er 0.1 / ZnS core / shell structure quantum dots are taken as an example, 0.0045mol calcium chloride is dissolved in 10ml aqueous solution, add 40ml concentration and be the sodium hexametaphosphate aqueous solution of 0.15g / ml, stir, make stock solution A;

[0029] 2) Dissolve 0.01mol yttrium nitrate in 30ml aqueous solution, and ultrasonically disperse for 30min to prepare stock solution B;

[0030] 3) Dissolve 0.0005mol of erbium acetate in 10ml of aqueous solution, and ultrasonically disperse for 30min to obtain stock solution C;

[0031] 4) Dissolve 0.02 mol of sodium sulfide in 10 ml of ethanol solution, and ultrasonically disperse for 30 min to obtain stock solution D;

[0032] 5) Dissolve 0.01mol of zinc acetate in 20ml of aqueous solution and disperse ultrasonically for 30min to obtain stock solution E;

[0033] 6) Dissolve 0.01mol of sodium sulfide in 20ml of aqueous solution, and disperse it ultrasonically for 30min to obtain stock solu...

Embodiment 2

[0037] with Ca 0.95 Y 2 S 4 :Eu 0.05 / ZnS core / shell structure quantum dots are taken as an example, 0.00475mol calcium chloride is dissolved in 10ml aqueous solution, add 46ml concentration and be the sodium hexametaphosphate aqueous solution of 0.15g / ml, stir, make stock solution A;

[0038] 2) Dissolve 0.01mol yttrium nitrate in 30ml aqueous solution, ultrasonically disperse for 30min, and prepare stock solution B;

[0039] 3) Dissolve 0.00025 mol of europium acetate in 10 ml of aqueous solution, and ultrasonically disperse for 30 minutes to obtain stock solution C;

[0040]4) Dissolve 0.02 mol of sodium sulfide in 10 ml of ethanol solution, and ultrasonically disperse for 30 min to obtain stock solution D;

[0041] 5) Dissolve 0.01mol of zinc acetate in 20ml of aqueous solution and disperse ultrasonically for 30min to obtain stock solution E;

[0042] 6) Dissolve 0.01mol of sodium sulfide in 20ml of aqueous solution, and disperse it ultrasonically for 30min to obtain ...

Embodiment 3

[0046] with Ba 0.95 Y 2 S 4 :Pr 0.05 / ZnS core / shell structure quantum dots are taken as an example, 0.00475mol barium chloride is dissolved in 10ml aqueous solution, add 60ml concentration and be the sodium hexametaphosphate aqueous solution of 0.15g / ml, stir, make stock solution A;

[0047] 2) Dissolve 0.01mol yttrium nitrate in 30ml aqueous solution, and ultrasonically disperse for 30min to prepare stock solution B;

[0048] 3) Dissolve 0.00025 mol of praseodymium acetate in 10 ml of aqueous solution, and disperse it ultrasonically for 30 minutes to obtain stock solution C;

[0049] 4) Dissolve 0.02 mol of sodium sulfide in 10 ml of ethanol solution, and ultrasonically disperse for 30 min to obtain stock solution D;

[0050] 5) Dissolve 0.01mol of zinc acetate in 20ml of aqueous solution and disperse ultrasonically for 30min to obtain stock solution E;

[0051] 6) Dissolve 0.01mol of sodium sulfide in 20ml of aqueous solution, and disperse it ultrasonically for 30min t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses one kind of core-shell structure quantum dot with ZnS shell, and features its chemical expression of M(1-x)Y2S4 to Ax / ZnS, where, M is Bioavailability or Ca, A is one or two of Mn, Cu, Ag, Al, Pr, Eu, Er, Tm, Ce, Yb and Nd, x is 0.001-0.5. The present invention also provides the preparation process of the quantum dot. The preparation process has safe material, low material cost, simple and safe operation and relaxed equipment requirement, and is suitable for large scale preparation in lab. The prepared quantum dot has high dispersivity, high fluorescence strength and high stability, and may be used as fluorescent labeling material for biological detection and analysis and as light emitting material for display devices.

Description

【Technical field】 [0001] The present invention relates to nano semiconductor material, especially a kind of M (1-x) Y 2 S 4 :A x / ZnS core / shell structure quantum dot and its preparation method. 【Background technique】 [0002] Quantum dots are quasi-zero-dimensional nano-semiconductor materials, which are composed of a small number of atoms or atomic groups, and usually have a three-dimensional scale of 1 to 10 nm. Due to the influence of size quantum effect and dielectric confinement effect, semiconductor nanocrystals show unique physical and chemical properties such as fluorescence characteristics. This makes quantum dots have broad application prospects in optics and biology. Quantum dots are in great demand in life sciences and other fields, so people are constantly exploring quantum dots and their synthesis technology. A variety of core-shell nanoparticles have been synthesized, such as: CdS / Ag 2 S, CdS / Cd(OH) 2 , CdS / ZnS, CdSe / ZnS, CdHgTe / ZnS, ZnSe / CdSe, CdS / Hg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K11/84
Inventor 李岚张晓松安海萍
Owner TIANJIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com