Method for preparing composite material of silicon nitride-titanium carbide

A composite material, titanium carbide technology, applied in the field of material science, can solve problems such as strength reduction

Inactive Publication Date: 2006-04-19
SHANDONG UNIV
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these two toughening methods will lead to a decrease in strength while improving the fracture toughness of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Micron Si 3 N 4 (0.5μm)+nano-Si 3 N 4 (130nm) + nano TiC (50nm), the mass percentage of each component in the composite material is: 46% micron Si 3 N 4 , 20% nano-Si 3 N 4 , 25% Nano TiC, 3% Al 2 o 3 , 6%Y 2 o 3 . Nano-Si 3 N 4 (130nm) The concentration of the aqueous suspension is 2.0vol%, the pH value of the suspension is 9 to 9.5, polyethylene glycol is used as the dispersant, the molecular weight is 1540, and the addition amount is Si 3 N 4 0.4wt% of the powder mass; the concentration of nano-TiC (50nm) aqueous suspension is 2.0vol%, the pH value of the suspension is 9.5 to 10, polyethylene glycol is used as the dispersant, the molecular weight is 4000, and the addition amount is 1% of the TiC powder mass 0.5 wt%. Prepared Si 3 N 4 and TiC nanopowder suspension for 8 hours, and then with micron Si 3 N 4 Particles and sintering aid Al 2 o 3 and Y 2 o 3 Mix, dry and sieve to obtain a well-dispersed composite powder. Mix the materials with a pl...

Embodiment 2

[0020] Micron Si 3 N 4 (0.5μm)+nano-Si 3 N 4 (130nm) + nano TiC (130nm), the mass percentage of each component in the composite material is: 45% micron Si 3 N 4 , 18% nano-Si 3 N 4 , 28% Nano TiC, 3% Al 2 o 3 , 6%Y 2 o 3 . Nano-Si 3 N 4(130nm) dispersion process and parameters are the same as in Example 1; the concentration of nano-TiC (130nm) aqueous suspension is 2.0vol%, the pH value of the suspension is 9~9.5, with polyethylene glycol as the dispersant, the molecular weight is 1540, adding The amount is 0.35wt% of the mass of TiC powder. Nano-Si 3 N 4 (130nm) and nano-TiC (130nm) particle suspensions with micron-sized Si 3 N 4 Particles and sintering aid Al 2 o 3 and Y 2 o 3 Mixing, drying and sieving to obtain a well-dispersed composite powder. It adopts segmental temperature rise, segmental pressure hot pressing sintering process, and high-purity nitrogen protection. At 1200°C-1250°C, the heating rate is 80-100°C / min, and the pressure is 15MPa; at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
flexural strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

A process for preparing the nano-class composite silicon nitride-titanium carbide ceramic in which the granularities of silicon nitride are distributed by dual peaks includes such steps as mixing Si3N4 nanoparticles and TiC nanoparticles with Si3N4 micron-particles, and sintering by segmentally raising temp and pressurizing. Its advantages are high strength, toughness, heat shock resistance and antioxidizing performance.

Description

technical field [0001] The invention belongs to the technical field of material science, and in particular relates to a method for preparing a silicon nitride-titanium carbide composite material with a bimodal distribution of silicon nitride particle size. Background technique [0002] Silicon nitride ceramics are one of the most important structural ceramics due to their low coefficient of thermal expansion, high thermal conductivity, high strength and fracture toughness, and high thermal shock resistance. Silicon nitride ceramics are widely used in chemical, metallurgy, machinery, aerospace and automotive industries for high temperature resistance, oxidation resistance and wear resistance, such as turbine blades, turbochargers, ceramic bearings and metal cutting tools. However, the inherent brittleness and low chemical stability of silicon nitride ceramics limit its application range. [0003] By adding second phase particles (such as SiC, Al 2 o 3 , TiN), or whiskers (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/596C04B35/622
Inventor 赵军艾兴吕志杰
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com