Manufacture of fine-type stainless steel plate heat exchanger

A technology of plate-fin heat exchangers and fin heat exchangers, which is applied in manufacturing tools, metal processing equipment, welding equipment, etc., and can solve the problems of heat exchangers that are not resistant to high temperature, corrosion, and high pressure

Inactive Publication Date: 2002-10-23
NANJING UNIV OF TECH
View PDF0 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the manufacture of stainless steel plate-fin heat exchangers, copper-based solder is mainly used for brazing at present. This type of heat exchanger is not resistant to high temperature, high pressure and corrosion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacture of fine-type stainless steel plate heat exchanger
  • Manufacture of fine-type stainless steel plate heat exchanger

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] Refer to attached figure 1 , the manufacturing process of stainless steel plate-fin heat exchanger is:

[0036] 1. Parts preparation

[0037] (1) Partition. It is produced by a special manufacturer, and the material is cut according to the required length when manufacturing the plate-fin heat exchanger.

[0038] The separator is generally a thin plate of 0.2 mm.

[0039] (2) Seals. It is a special profile, which can be obtained by cold drawing or hot extrusion, and is produced by a special factory

[0040] Home production, when manufacturing plate-fin heat exchangers, cut the material according to the required length.

[0041] (3) Fins. Its main forming methods are stamping and rolling, each with its own characteristics.

[0042] is carried out using automatic forming machine tools. The fins are made of stainless steel with a thickness of 0.1 to 0.4 mm

[0043] The thin plate is stamped into a blank shape with a forming punch on an automatic forming...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The production method of austenitic stainless steel plate fin heat exchanger includes the following steps: part preparation: partition, sealing strip, fin, sealing head and connecting pipe preparation; cleaning before welding; acid pickling to remove oil, dirt and oxide, and using high-pressure water to wash; element assembling and holding; vacuum braze welding, adopting argon arc welding to weldscaling head and connecting pipe, making general assembly; test and inspection, making x-ray inspection, helium leak detection, flow resistance test, pressure test, TUV, ASME and other test and inspection. Said invented process raise the production quality of said stainless steel plate fin heat exchanger, tensile-strength of connector and its service life.

Description

technical field [0001] The invention relates to a manufacturing method of an austenitic stainless steel plate-fin heat exchanger. Background technique [0002] In petrochemical, refrigeration, medicine, atomic energy, aerospace and other fields, aluminum plate-fin heat exchangers cannot meet the requirements of high temperature resistance, high pressure resistance, and corrosion resistance. With its excellent high temperature resistance, high pressure resistance, corrosion resistance, weldability, processability and ductility, austenitic stainless steel plate-fin heat exchanger has become one of the heat exchange equipment with broad development prospects in these fields. However, for the manufacture of stainless steel plate-fin heat exchangers, copper-based brazing filler metals are currently used for brazing. This type of heat exchanger is not resistant to high temperature, high pressure, and corrosion. Contents of the invention [0003] The object of the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K1/00B23K1/008
Inventor 凌祥周帼彦耿鲁阳涂善东
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com