Thermal-melting welding flux igniting material and its constructred heat generation melt welding flux

A technology of hot-melt welding and raw materials, applied in the direction of welding medium, welding equipment, welding equipment, etc., can solve the problems of insufficient strength and chemical stability of welding joints, poor safety, and inconvenient use, etc., and achieve mechanical strength and chemical stability Improved performance, strong corrosion resistance, and long service life

Inactive Publication Date: 2007-01-17
成都桑莱特科技股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention aims to provide the hot-melt solder used for welding with the high-temperature hot-melt welding method in the wired signal transmission wire, the ignition agent and the exothermic fusion solder composed of the hot-melt solder and the ignition agent, so as to Overcome the defects of poor safety, inconvenient use, and insufficient strength and chemical stability of welding points in the existing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036]The composition of raw materials for the preparation of hot-melt solder:

[0037] Copper oxide (CuO) powder with a degree of oxidation of 58% and a particle size of 100 mesh 50%

[0038] Copper (Cu) powder with a copper passivation of 99% and a particle size of 60 mesh 30%

[0039] Metal aluminum (Al) powder with a particle size of 100 mesh 14%

[0040] Fluorspar (CaF 2 ) powder 5.0%

[0041] Zinc oxide (ZnO) powder with particle size of 100 mesh 1.0%

[0042] The preparation raw material component of igniter consists of:

[0043] Metallic copper (Cu) powder with a copper passivation of 99% and a particle size of 60 mesh 40%

[0044] Copper oxide (CuO) powder on the surface with an oxidation degree of 70% and a particle size of 100 mesh 25%

[0045] Metal aluminum (Al) powder with a particle size of 100 mesh 20%

[0046] Potassium permanganate (KMnO) with a particle size of 100 mesh 4 ) powder 8.0%

[0047] Red phosphorus (P) powder with particle size of 100 mes...

Embodiment 2

[0050] The raw material components for the preparation of hot-melt solder consist of:

[0051] Copper oxide (CuO) powder on the surface with an oxidation degree of 63% and a particle size of 200 mesh 60%

[0052] Copper passivation of 99%, particle size of 60 mesh metal copper (Cu) powder 30%

[0053] Metal aluminum (Al) powder with particle size of 100 mesh 12.5%

[0054] Fluorspar (CaF 2 ) powder 6.5%

[0055] Tin oxide (SnO) powder with particle size of 100 mesh 1.0%

[0056] The preparation raw material component of igniter consists of:

[0057] Copper (Cu) powder with a copper passivation of 99% and a particle size of 60 mesh 30%

[0058] Copper oxide (CuO) powder on the surface with an oxidation degree of 55% and a particle size of 100 mesh 40%

[0059] Metal aluminum (Al) powder with particle size of 100 mesh 15%

[0060] Potassium permanganate (KMnO) with a particle size of 100 mesh 4 ) powder 10%

[0061] Red phosphorus (P) powder with particle size of 100 me...

Embodiment 3

[0064] The raw material components for the preparation of hot-melt solder consist of:

[0065] Copper oxide (CuO) powder on the surface with an oxidation degree of 70% and a particle size of 100 mesh 59%

[0066] Copper (Cu) powder with a copper passivation of 99% and a particle size of 60 mesh 30%

[0067] Metal aluminum (Al) powder with particle size of 100 mesh 12%

[0068] Fluorspar (CaF 2 ) powder 5.5%

[0069] Zinc oxide (ZnO) powder with particle size of 100 mesh 2.0%

[0070] Tin oxide (SnO) powder with a particle size of 100 1.5%

[0071] The preparation raw material component of igniter consists of:

[0072] Copper (Cu) powder with a copper passivation of 99% and a particle size of 60 mesh 25%

[0073] Copper oxide (CuO) powder on the surface with an oxidation degree of 60% and a particle size of 100 mesh 37%

[0074] Metal aluminum (Al) powder with a particle size of 100 mesh 18%

[0075] Potassium permanganate (KMnO) with a particle size of 100 mesh 4 ) po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
oxidation stateaaaaaaaaaa
Login to View More

Abstract

A thermo-melting solder for the thermo-melting welding between copper wire and structural member is composed of the thermo-melting welding stock which contains less Zn and Sn for generating CuZnSn alloy at welded point and excessive Al for removing surficial oxide from welded point, and the igniting agent containing potassium permanganate instead of potassium bichromate (or chloride).

Description

1. Technical field [0001] The present invention relates to the welding material used in metal welding, more specifically, the present invention relates to the hot-melt solder used for welding metal by high-temperature hot-melt welding method, ignition agent and the composition of hot-melt solder and ignition agent hot melt solder. 2. Background technology [0002] There are a large number of connections between wires, between metal components, and between wires and components in wired signal transmission projects such as communication systems using railway guide rails or long-distance transportation pipelines as wires, lightning protection grounding projects for field buildings and structures, etc. solder joints. The traditional welding method is arc welding or gas welding. However, due to the wide distribution of these connection and welding points in the field, limited by the transportation of power supply and welding equipment, the construction is often inconvenient, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/362B23K28/00
Inventor 余旭东寇承平宋大余
Owner 成都桑莱特科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com