A technology of polyvinylidene chloride and resin composition is applied in the fields of polyvinylidene chloride-based resin composition molding, new production of polyvinylidene chloride-based resin composition, and resin composition for coloring, which can solve the problem of It is difficult to adopt, the thermal stability of the composition is reduced, and it is difficult to use the master batch, and the effect of suppressing coarse foreign matter and excellent adhesion

Inactive Publication Date: 2006-02-08
KUREHA KAGAKU KOGYO KK
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is difficult to use the masterbatch, it is also difficult to increase the concentration of the pigment, and there is also the problem of polluting the inside of the mixer
[0015] In the final process of mixing, when a large amount of aggregated particles are removed by sieving, since the glycidyl-containing (meth)acrylic resin and a large amount of pigments are removed, the thermal stability of the composition decreases, or the desired product cannot be obtained. Disadvantages such as coloring degree
[0016] Due to the above-mentioned problems, although the proposal of a glycidyl-containing (meth)acrylic resin as a heat stabilizer for PVDC resins, the actual situation is that it is difficult to adopt industrially, or for industrialization, Further research is still needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0151] 1. Preparation of resin composition for coloring

[0152] As shown in Table 1, the glycidyl-containing (meth)acrylic resin [glycidyl methacrylate-methyl methacrylate-styrene-butyl acrylate (30 / 31 / 31 / 8% by weight) ] 41% by weight, methyl methacrylate-butyl methacrylate copolymer 23% by weight, pigment red mixture (pigment) 25% by weight, silica (inorganic lubricant; average particle diameter 5.2 μm) 5% by weight, 3% by weight of epoxidized soybean oil, 2% by weight of aliphatic hydrocarbon oligomer (Mw=2,100), and 1% by weight of calcium montanate were stirred with a Henschel mixer at normal temperature (23°C) for 5 minutes, A resin composition for coloring was prepared. The composition is shown in Table 1.

[0153]

Resin composition for coloring

composition

2 parts by weight

weight%

Details

Glycidyl-containing (meth)acrylic resin

Glycidyl Methacrylate-Methyl Methacrylate

- Styrene - Butyl Acrylate = 30 / 31 / 31 / ...

Embodiment 2

[0165] When the powder resin of PVDC (1) is polymerized, 0.3 parts by weight of epoxidized linseed oil (O-180) and 4.0 parts by weight of dibutyl sebacate are contained with respect to 100 parts by weight of PVDC-based resin. The ratio is adjusted. According to the order of powder resin, powder additive, liquid additive (acetyl tributyl citrate, epoxidized linseed oil and pigment) of PVDC (1), the glycidyl group-containing components in Table 2 Components other than (meth)acrylic resin are put into the paddle mixer, and the temperature is raised to about 80°C while mixing (heating mixing). After the temperature rises, it is cooled immediately, and when the temperature drops to about 65°C, it is put into the glycidyl-containing (methanol) Base) the powder of acrylic resin is mixed (mixing after heating). After cooling, obtain resin composition (mixture) after sieving with #50 mesh sieve. Except using this resin composition, other is the same as embodiment 1 A stretched film wa...

Embodiment 3

[0169] In the polymerization of each powder resin, 2.46 parts by weight of epoxidized linseed oil (O-180) and 3.5 parts by weight of dibutyl sebacate are contained with respect to 100 parts by weight of PVDC-based resin. modulation. Use these powder resins, and press powder resin. The order of powder additives and pigments is to put glycidyl group-containing (meth)acrylic resin and EVA components in the components shown in Table 2 into the paddle mixer, and heat up to about 80°C while mixing. (warm up to mix). After heating up, it was cooled immediately, and when the temperature dropped to about 65° C., powder of a glycidyl group-containing (meth)acrylic resin was thrown in and mixed (mixing at elevated temperature). Then, EVA was mixed at normal temperature (normal temperature mixing). Using the obtained resin composition, a stretched film was produced in the same manner as in Example 1. The results are shown in Table 2.

[0170]

Composition (parts by weigh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
melt flow indexaaaaaaaaaa
epoxy valueaaaaaaaaaa
Login to View More

Abstract

This polyvinylene chloride resin composition is obtained by including an epoxy compound and a glycidyl group-containing (meth)acrylic resin as a heat stabilizer in a polyvinylidene chloride resin. The polyvinylidene chloride resin composition has excellent processability, heat stability, color tone, dispersibility of the pigment, gas barrier properties. The method for producing the resin composition is provided. The film comprises the resin composition. The resin composition for coloring comprises the glycidyl group-containing (meth)acrylic resin and the pigment.

Description

technical field [0001] The present invention relates to a polyvinylidene chloride-based resin composition, and more specifically, to a polyvinylidene chloride-based resin composition having excellent processability, thermal stability, color tone, pigment dispersibility, gas barrier properties, and the like. The polyvinylidene chloride-based resin composition of the present invention can suppress the occurrence of coarse foreign matter, pigment agglomerates, stains, etc., has a high-end color tone, and can impart airtightness, strength, and good adhesion to food Films for packaging. [0002] The present invention also relates to a novel production method of the polyvinylidene chloride-based resin composition, and a film formed by molding the polyvinylidene chloride-based resin composition. The present invention also relates to a coloring resin composition suitable for coloring polyvinylidene chloride-based resins. Background technique [0003] Polyvi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08J3/20C08J5/18C08F2/44C08F220/32C08F283/10C08L23/08C08L27/08C08L33/04C08L33/12C08L63/00C09D133/12
CPCB29C55/12C08J5/18C08L23/0869C08L25/14C08L27/08C08L63/00C08L2203/16
Inventor 菅野胜彦饭均柴田修作
Owner KUREHA KAGAKU KOGYO KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com