Hydrogen-rich circulating annealing process for cold-rolled oil drum plate

An annealing process and hydrogen-rich cycle technology, applied in the direction of process efficiency improvement, manufacturing tools, furnaces, etc., can solve the problems of strip steel surface roughness reduction, etc., and achieve good surface quality, high energy utilization rate, and good mechanical properties Effect

Pending Publication Date: 2022-05-31
XINJIANG BAYI IRON & STEEL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Significantly reduce the surface roughness of the strip steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogen-rich circulating annealing process for cold-rolled oil drum plate
  • Hydrogen-rich circulating annealing process for cold-rolled oil drum plate
  • Hydrogen-rich circulating annealing process for cold-rolled oil drum plate

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0034]Use 4 coils of 1.0*920mm cold-rolled chilled coils for bell-type annealing process. The steel coils are annealed in 7 stages, and a large-flow hydrogen blowing process is applied. They are kept at 430°C for 3 hours, and press 30 m 3 / h hydrogen flow for 3 hours purging, 7 hours at 680 ° C, 3 hours by 25 m 3 / h hydrogen flow for purging. The hydrogen tail gas in the annealing process is filtered and separated, and then reused repeatedly.

[0035]

[0036] After the annealing is completed, the steel coil is carried out in a tempering machine, and is rolled at a tempering elongation of 1.1% to eliminate the yield platform. During the leveling process, 4% leveling liquid is used for cleaning, which can completely remove the residues on the surface of oil drum steel coils after annealing, obtain a surface quality with a reflectivity of 65%, and excellent mechanical properties.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydrogen-rich circulating annealing process for a cold-rolled oil drum plate, which is characterized in that a steel coil comprises the following chemical components: 0.04-0.08% of C, 0.02-0.03% of Si, 0.26-0.33% of Mn, less than 0.01% of P, less than 0.005% of S and the balance of Fe and residual elements, the oil drum plate cold-rolled steel coil subjected to hot rolling and cold rolling is placed on a furnace platform of a cover type annealing furnace, an inner cover is buckled firstly, then a heating cover is buckled, a medium pipeline is connected, nitrogen is used for purging air, hydrogen is used for purging nitrogen, and the steel coil is subjected to hot rolling and cold rolling; two heat preservation processes of 430 DEG C and 680 DEG C are adopted, heat preservation is conducted for 3 hours at the temperature of 430 DEG C, annealing and heat preservation are conducted for 7 hours at the temperature of 680 DEG C, recrystallization temperature annealing is conducted, hydrogen tail gas discharged in the annealing process is collected through a main pipeline, hydrogen with the hydrogen purity being 99.999%, the dew point being-65 DEG C or below and the oxygen content being 5 ppm or below is obtained, and hydrogen recycling is achieved. And the annealed steel coil is subjected to flattening treatment with the elongation of 1.1%, the surface of the steel coil is cleaned with flattening liquid with the concentration of 3%-5%, and the high-surface oil drum plate product is obtained.

Description

technical field [0001] The invention relates to a hydrogen-rich cycle annealing process for cold-rolled oil drum plates. Background technique [0002] The cold-rolling annealing furnace uses hydrogen as the protective atmosphere. Due to its good oxidation resistance, cold-rolled steel coils with no oxidation and high surface can be obtained by annealing and heating under the action of the protective atmosphere. At present, the hydrogen exhaust gas of the process is not recycled and recycled, and the consumption of hydrogen is relatively high. It consumes 2-2.3 cubic meters of hydrogen per ton of steel produced. The high-grade oil drum plate has very strict requirements on the surface quality of the cold-rolled steel plate due to the high purity and high value of the oil contained in it. [0003] In the state of the art: the hydrogen used once is discharged into the atmosphere with the exhaust gas after simple treatment, and is no longer recycled. The tail gas contains impu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/30C21D1/74C21D6/00C21D9/00C22C38/02C22C38/04
CPCC21D1/30C21D1/74C21D9/0081C21D6/005C21D6/008C22C38/02C22C38/04Y02P10/20
Inventor 向华张永钢徐建生
Owner XINJIANG BAYI IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com