A table tennis table and composite material technology, applied in the field of composite materials, can solve the problems of non-corrosion resistance, easy aging, and the table tennis table surface is not suitable for outdoor use.

Pending Publication Date: 2022-05-10
QUANZHOU SHUNTONG CRAFTS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, in view of the above content, the present invention provides a composite material for outdoor table tennis tables, which solves the problems that the existing wooden table tennis table tops are not suitable for outdoor use, are not corrosion-resistant, and are easy to age.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A composite material for an outdoor table tennis table, comprising the following raw materials in parts by weight: 90 parts of Portland cement, 55 parts of river sand, 0.5 part of redispersible latex powder, 0.3 part of polypropylene fiber, 4 parts of fly ash, 3 parts of bagasse ash, 0.3 parts of lignocellulose, 0.2 parts of polycarboxylate reducer, 1 part of metakaolin loaded zirconia, 36 parts of water, 5 parts of bisphenol A epoxy resin, 1 part of T31 curing agent, disinfectant 0.06 parts of foaming agent, 0.08 parts of dispersant, 0.26 parts of fumed silica, and 1.5 parts of microcapsules.

[0026] Described metakaolin supported zirconia is prepared according to the following steps:

[0027] (1) Add metakaolin powder into sodium hydroxide solution, heat and stir for 5 hours, and the reaction temperature is 66° C. After the reaction is completed, filter, wash, and dry to obtain modified metakaolin;

[0028] (2) dissolving zirconium oxychloride in deionized water to ...

Embodiment 2

[0035] A composite material for an outdoor table tennis table, comprising the following raw materials in parts by weight: 100 parts of cement, 60 parts of river sand, 0.6 part of redispersible latex powder, 0.5 part of polypropylene fiber, 5 parts of fly ash, bagasse ash 4 parts, 0.5 parts of lignocellulose, 0.3 parts of polycarboxylate reducer, 2 parts of metakaolin loaded zirconia, 42 parts of water, 8 parts of epoxy resin, 1.5 parts of curing agent, 0.14 parts of defoamer, 0.17 parts of dispersant parts, 0.39 parts of fumed silica, and 2 parts of microcapsules.

[0036] Described metakaolin supported zirconia is prepared according to the following steps:

[0037] (1) Add metakaolin powder into sodium hydroxide solution, heat and stir for 4 hours, and the reaction temperature is 72°C. After the reaction is completed, filter, wash, and dry to obtain modified metakaolin;

[0038] (2) dissolving zirconium oxychloride in deionized water to prepare a zirconium oxychloride aqueou...

Embodiment 3

[0042] A composite material for an outdoor table tennis table, comprising the following raw materials in parts by weight: 110 parts of cement, 65 parts of river sand, 0.8 part of redispersible latex powder, 0.6 part of polypropylene fiber, 8 parts of fly ash, bagasse ash 6 parts, 0.8 parts of lignocellulose, 0.4 parts of polycarboxylate reducer, 3 parts of metakaolin loaded zirconia, 48 parts of water, 10 parts of epoxy resin, 2 parts of curing agent, 0.24 parts of defoaming agent, 0.16 parts of dispersant parts, 0.60 parts of fumed silica, and 2.5 parts of microcapsules.

[0043] Described metakaolin supported zirconia is prepared according to the following steps:

[0044] (1) Add metakaolin powder into sodium hydroxide solution, heat and stir for 3 hours, and the reaction temperature is 80° C. After the reaction is completed, filter, wash, and dry to obtain modified metakaolin;

[0045] (2) dissolving zirconium oxychloride in deionized water to prepare a zirconium oxychlori...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Flexural strengthaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite material for an outdoor table tennis table. The composite material comprises the following raw materials in parts by weight: 90-110 parts of cement, 55-65 parts of river sand, 0.5-0.8 part of redispersible latex powder, 0.3-0.6 part of polypropylene fiber, 4-8 parts of fly ash, 3-6 parts of bagasse ash, 0.3-0.8 part of lignocellulose, 0.2-0.4 part of a reducing agent, 1-3 parts of metakaolin loaded zirconium dioxide, 36-48 parts of water, 5-10 parts of epoxy resin, 1-2 parts of a curing agent and 0.4-1 part of an auxiliary agent. The problems that an existing wooden table tennis table top is not suitable for outdoor use, not resistant to corrosion and prone to aging are solved.

Description

technical field [0001] The invention relates to a composite material for an outdoor table tennis table. Background technique [0002] Table tennis is China's national ball game and is a popular ball game in the world. Ping-pong table is requisite facility when carrying out table tennis, and table tennis table generally comprises table top, support and block, and described support is located at the bottom of table top, and described block is perpendicular to table top and table top is divided into symmetrical two parts. Table tennis table tops can be made of any material, such as wood, fiberglass, marble, SMC boards, sawdust boards, etc. According to international regulations, table tennis table tops should be made of solid wood and must have certain elasticity. [0003] Table tennis is widely used in indoor or outdoor sports, and the outdoor table tennis table requires its table top to withstand the sun and rain, with the characteristics of not easy to age, long service lif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B111/20
CPCC04B28/04C04B2201/50C04B2111/20C04B14/06C04B16/0633C04B18/08C04B18/10C04B18/26C04B14/106C04B14/306C04B14/064C04B24/281C04B2103/50C04B2103/408C04B2103/0068C04B2103/302C04B2103/0057C04B2103/0001C04B24/38C04B24/16
Inventor 江志坚
Owner QUANZHOU SHUNTONG CRAFTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products