Antibacterial and anti-adhesion nanofiber dressing free of bandage fixation and preparation method of antibacterial and anti-adhesion nanofiber dressing
A nanofiber and nanofiber membrane technology, applied in bandages, medical science, non-woven fabrics, etc., can solve the problems of waste of natural cotton fiber resources, difficult to maintain wound moisturization, and poor control of drug dosage, so as to reduce the pain of dressing changes. The effect of increasing the comfort of contact and reducing the frequency of replacement
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] S1, the preparation of nuclear layer spinning solution: firstly disperse the drug—silver sulfadiazine ultrasonically into an aqueous dispersion with a mass concentration of 10wt%, then mix cyclodextrin and ethyl cellulose in a mass ratio of 1:2 and use a volume ratio The mixed solution of 1:1 ethanol and water is used as a solvent to dissolve, and after sealing, it is fully mixed and stirred for 6 hours until uniform, and then the mixed solution with a mass concentration of 10wt% medicinal solution and 10wt% cyclodextrin-ethyl cellulose is mixed at a ratio of 1:5 The volume ratio is fully mixed and stirred until uniform, and used as the core layer spinning solution.
[0039] S2, preparation of shell spinning solution: dissolving chitosan powder and gelatin powder in acetic acid solution with the same mass concentration, then miscible with equal volume ratio of 1:1, sealed and fully stirred at room temperature, finally A chitosan-gelatin mixed solution with a solid mass ...
Embodiment 2
[0046] The difference from Example 1 is that the medicine is different, which is chloramphenicol, and the concentration of the drug solution dissolved in alcohol is 20wt%. The others are the same as in Example 1, and an antibacterial and anti-adhesion nanofiber dressing without bandage fixing is obtained.
[0047] The antibacterial and anti-adhesion nanofiber dressing prepared in this embodiment without bandage fixation has the following advantages: the diameter of a single fiber is 300-500 nm, the thickness is 800-1000 μm, it has a natural nanofiber and nanopore structure, and it is lighter, thinner and more breathable than cotton gauze. The combination with the skin is firm, and the contact comfort with the skin is increased, and 12 layers can be superimposed and covered. Suitable for wounds with exudate, PBS aqueous solution with a pH of 7.4 is used as a simulated body fluid, 2mL of PBS aqueous solution is completely absorbed in 6s, and quickly forms a gel in 15s. The dress...
Embodiment 3
[0049] The difference from Example 1 is that the medicine is different, it is ketoprofen, and the concentration of the drug solution dissolved in alcohol is 20wt%. Others are the same as in Example 1, and an antibacterial and anti-adhesion nanofiber dressing without bandage fixing is obtained.
[0050] The antibacterial and anti-adhesion nanofiber dressing prepared in this embodiment without bandage fixation has the following advantages: the diameter of a single fiber is 300-500 nm, the thickness is 800-1000 μm, it has a natural nanofiber and nanopore structure, and it is lighter, thinner and more breathable than cotton gauze. The combination with the skin is firm, and the contact comfort with the skin is increased, and 11 layers can be superimposed and covered. Suitable for wounds with exudate, PBS aqueous solution with a pH of 7.4 is used as the simulated body fluid, 2mL of PBS aqueous solution is completely absorbed in 8s, and quickly forms a gel in 13s. The dressing has a ...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com