Butyl pressure-sensitive adhesive as well as preparation method and application thereof

A pressure-sensitive adhesive, butyl technology, applied in the field of butyl pressure-sensitive adhesive and its preparation, can solve the problems of mildew resistance and poor noise reduction performance, and achieve good adhesion performance and cohesive strength, high mildew resistance and Antibacterial and antibacterial ability, the effect of raw material cost without pollution

Active Publication Date: 2022-03-29
KESHUN WATERPROOF TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to overcome the defects of mildew resistance and poor noise reduction performance in existing butyl pressure sensitive adhesives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Butyl pressure-sensitive adhesive as well as preparation method and application thereof
  • Butyl pressure-sensitive adhesive as well as preparation method and application thereof
  • Butyl pressure-sensitive adhesive as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0045] According to a particularly preferred embodiment, the method also includes preparing the silica airgel-silver-zinc composite by steps comprising the following operations:

[0046] (a) ball milling the silica airgel for 2-3 hours at a rotational speed of 100-150 rpm to obtain a powder;

[0047] (b) Put the powder and the mixed solution containing silver nitrate, zinc sulfate, glucose and ammonia water in a light-proof reactor, heat up to 60-80°C, and stir at a speed of 150-200rpm (for example, For mechanical stirring) 3-4h, obtain reaction product;

[0048] In the mixed solution, the concentration of silver nitrate is 0.1-0.2mol / L, the concentration of zinc sulfate is 0.2-0.4mol / L, the concentration of glucose is 0.5-1mol / L, and the concentration of ammonia water is 0.2-0.4mol / L L, the dosage ratio of the powder and the mixed solution is 1g: 100-150mL;

[0049] (c) filter the reaction product to obtain a filter cake, dry the filter cake for 24-28 hours, and then grind it...

preparation example 1

[0127] Silica Airgel-Silver Zinc Composite AA-1:

[0128] (a) 1 g of silica airgel was ball milled for 2 hours at a rotational speed of 150 rpm to obtain a powder;

[0129] (b) Put the powder and a mixed solution containing silver nitrate, zinc sulfate, glucose and ammonia water in a light-proof reaction kettle, heat up to 60° C., and mechanically stir for 3 hours at a rotation speed of 200 rpm to obtain a reaction product;

[0130] In the mixed solution, the concentration of silver nitrate is 0.1mol / L, the concentration of zinc sulfate is 0.2mol / L, the concentration of glucose is 1mol / L, and the concentration of ammonia water is 0.2mol / L. The powder and the The dosage ratio of the mixed solution is 1g: 150mL;

[0131] (c) Filter the reaction product to obtain a filter cake, freeze-dry the filter cake for 28 hours, and grind for 1 hour at a rotation speed of 100 rpm to obtain the silica airgel-silver-zinc composite AA-1.

Embodiment 1

[0133] This example is used to illustrate the method for preparing butyl pressure-sensitive adhesive according to the present invention. Specifically, according to the formula and process parameters in Table 1, butyl pressure-sensitive adhesive was prepared according to the following method.

[0134] The method for preparing butyl pressure-sensitive adhesive comprises the following steps:

[0135] (1) butyl rubber, silica airgel-silver-zinc composite, thermoplastic elastomer, antioxidant, light stabilizer and reinforcing agent accounting for 1 / 2 weight of the total amount are added in the vacuum kneader, Kneading for 2 hours at 120°C and vacuum <-0.096Mpa;

[0136] (2) sequentially add tackifier accounting for 1 / 3 weight of the total amount, plasticizer accounting for 1 / 2 weight of the total amount and remaining reinforcing agent, and knead for 1 hour at 120°C and vacuum <-0.096Mpa;

[0137] (3) Add the remaining tackifier, the remaining plasticizer and all the coupling agent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
softening pointaaaaaaaaaa
porosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of building waterproof materials, in particular to a butyl pressure-sensitive adhesive and a preparation method and application thereof.The method comprises the steps that 1, butyl rubber, a silicon dioxide aerogel-silver zinc compound, a thermoplastic elastomer, an antioxidant, a light stabilizer and a part of a reinforcing agent are subjected to a first contact reaction, and a product I is obtained; (2) carrying out a second contact reaction on the product I, a part of a tackifier, a part of a plasticizer and the rest of a reinforcing agent to obtain a product II; and (3) carrying out third contact reaction on the product II, a coupling agent, the rest tackifier and the rest plasticizer to obtain the butyl pressure-sensitive adhesive. The butyl pressure-sensitive adhesive provided by the invention has relatively high mildew-proof and noise-reducing properties, and meanwhile, can keep relatively good cohesive strength.

Description

technical field [0001] The invention relates to the field of building waterproof materials, in particular to a butyl pressure-sensitive adhesive and a preparation method and application thereof. Background technique [0002] Polymer waterproof membrane has gradually become one of the important materials in the construction field due to its good waterproof effect, simple construction method and excellent weather resistance. [0003] Self-adhesive polymer coils are usually composed of HDPE, PVC and other polymer sheets, adhesives, and isolation materials. The non-asphalt-based adhesives used mainly include hot-melt pressure-sensitive adhesives and butyl pressure-sensitive adhesives, of which butyl Pressure-sensitive adhesives have excellent sealing properties, water resistance, weather resistance, and are environmentally friendly and pollution-free, and have been widely used. [0004] With the expansion of city scale and the increase of building density, noise has become a ki...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/22C09J123/28C09J153/02C09J7/38C09J11/04
CPCC09J123/22C09J123/283C09J11/04C09J7/383C08K2003/0806C08K2003/0893C08L2207/04C09J2301/302C08L53/02C08K7/26C08K3/08C08L53/025Y02B80/10
Inventor 薛阳龚兴宇胡全超
Owner KESHUN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap