Preparation method and application of bionic high-adhesion long-acting antibacterial antifogging agent

A technology of high adhesion and anti-fogging agent, which is applied in antibacterial goggles, preparation of bionic high-adhesion long-acting bacteriostatic anti-fogging agent, and anti-fog field. It can solve problems such as fogging, achieve moderate temperature, easy large-scale production, strong design effect

Pending Publication Date: 2021-11-02
HUAZHONG UNIV OF SCI & TECH +1
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Taking the lens as the surface to be treated as an example, applying the solution on goggles, face shields and other lenses can effectively inhibit the lens surface from fogging and bacterial growth, thus solving the technical problem of traditional goggles and other fogging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of bionic high-adhesion long-acting antibacterial antifogging agent
  • Preparation method and application of bionic high-adhesion long-acting antibacterial antifogging agent
  • Preparation method and application of bionic high-adhesion long-acting antibacterial antifogging agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A preparation method of a bionic high-adhesion long-acting antibacterial and antifogging agent is prepared according to the following method: first, polyacetamide-dopamine polymer is synthesized according to the mass ratio of dopamine and polyvinylamine at 1:100, and dialyzed with deionized water for three days, After freeze-drying, configure an aqueous solution with a mass fraction of 5%, spray it on the surface of the plastic petri dish and the right side of the goggles surface, and remove the solvent at room temperature to obtain a petri dish and goggles with a polymer coating. The coating film thickness of the anti-fogging agent on the goggles and other lenses is greater than or equal to the thickness of a single polymer layer, and it only needs to not affect the line of sight of the goggles and the like.

[0044] Effect verification:

[0045] Put the blank Petri dish, Petri dish with anti-fog antibacterial coating and goggles next to the humidifier, and after four ...

Embodiment 2

[0048] A preparation method of a bionic high-adhesion long-acting antibacterial and antifogging agent is prepared according to the following method: first, polyethyleneimine-dopamine polymer is synthesized according to the mass ratio of dopamine and polyethyleneimine at 1:10, and dialyzed with deionized water for three After three days and freeze-drying, configure an aqueous solution with a mass fraction of 20%, spray it on the surface of the plastic petri dish and the right side of the goggle surface, and remove the solvent at room temperature to obtain a petri dish and goggles with a polymer coating.

[0049] Effect verification:

[0050] Put the blank Petri dish, Petri dish with anti-fog antibacterial coating and goggles next to the humidifier, and after four hours, test the anti-fog effect.

[0051] By observation, the left side of the blank petri dish and goggles has a layer of water mist on the surface, while the petri dish and goggles coated with anti-fog and antibacter...

Embodiment 3

[0053] A preparation method of a bionic high-adhesion long-acting antibacterial and antifogging agent, which is prepared according to the following method: first, an aqueous solution with a mass fraction of 20% is prepared according to the mass ratio of tannic acid and gelatin at 1:2, and sprayed onto the surface of a plastic petri dish and On the right side of the goggle surface, the solvent was removed at room temperature to obtain a polymer-coated Petri dish and goggle.

[0054] Effect verification:

[0055] Put the blank petri dish, petri dish with anti-fog antibacterial coating and goggles next to the humidifier, and after six hours, test the anti-fog effect.

[0056] By observation, the left side of the blank petri dish and goggles has a layer of water mist on the surface, while the petri dish and goggles coated with anti-fog and antibacterial coating have no water mist on the surface.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of biomedical polymer materials, and discloses a preparation method and application of a bionic high-adhesion long-acting antibacterial antifogging agent. The antifogging agent is prepared by the steps that firstly, a hydrophilic bionic high-adhesion polymer is prepared, then the hydrophilic bionic high-adhesion polymer coats a surface to be treated through a solution of the hydrophilic bionic high-adhesion polymer, so as to inhibit surface fogging and bacterium breeding. A hydrophilic bionic high-adhesion polymer solution is prepared by controlling key raw materials, a flow process and the like of the antifogging agent, and the hydrophilic bionic high-adhesion polymer solution can be used as a long-acting antibacterial antifogging agent for antifogging and antibacterial treatment on the surfaces of medical goggles lenses and the like, has good biological safety, and can effectively inhibit fogging and bacterium breeding on the surfaces of the goggles.

Description

technical field [0001] The invention belongs to the field of biomedical polymer materials, and more specifically relates to the preparation and application of a bionic high-adhesion long-acting antibacterial and antifogging agent, and correspondingly can obtain antifogging and antibacterial goggles. Background technique [0002] As the temperature and humidity change, water vapor condenses into water droplets, making goggles, face shields and other protective equipment very easy to fog. Fog will strongly scatter visible light and reduce the light transmittance of goggles, face shields and other protective equipment. It not only affects the accuracy of medical staff's operation, but also increases the psychological pressure. [0003] Although some goggles and face shields are equipped with original anti-fog coatings, their anti-fog coatings are not wear-resistant, and a slight touch with your fingers will greatly reduce the anti-fog effect. Therefore, we often use some comm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/14C09D179/02C09D7/63C09D189/00C09D105/08C09D139/00C09D139/02G02B1/18A61F9/02
CPCC09D5/14C09D139/02C09D7/63C09D189/00C09D105/08C09D139/00C09D179/02G02B1/18A61F9/02C08K5/17C08K5/1545C08K5/13
Inventor 朱锦涛任敬丽张连斌姜伟闫南于佳玉
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com