Migration-resistant environment-friendly plasticizer with micro-crosslinking structure and preparation method of same

An environmentally friendly plasticizer and micro-crosslinking technology, applied in the field of plasticizers, can solve the problems of no health problems, poor temperature resistance, low cost, etc., and achieve good migration resistance, not easy to move, and prevent migration.

Inactive Publication Date: 2021-09-17
SOUTH CHINA UNIV OF TECH
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims at the carcinogenicity of DOP, DOTP and other plasticizers used in the prior art in terms of human health, while biodiesel plasticizers not only have no health problems, but also have poor temperature resistance, and provide a Environment-friendly, good migration resistance at temperatures above 75°C, taking into account mechanical properties, low-cost environmental protection plasticizer with migration-resistant micro-crosslinked structure and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Migration-resistant environment-friendly plasticizer with micro-crosslinking structure and preparation method of same
  • Migration-resistant environment-friendly plasticizer with micro-crosslinking structure and preparation method of same
  • Migration-resistant environment-friendly plasticizer with micro-crosslinking structure and preparation method of same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A migration-resistant micro-crosslinked structure environment-friendly plasticizer, in parts by mass, its raw material formula components are as follows:

[0043]

[0044] A preparation method of a migration-resistant micro-crosslinked structure environment-friendly plasticizer, comprising the following steps:

[0045] 1) In terms of parts by mass, take 30 parts of epoxy soybean oil, 20 parts of polytrimethylene sebacate and adipate polyester 1:1 mixture, 6 parts of dipropylene glycol methyl ether acetate, use 120r / Stir at a speed of 1 min, heat to 90°C, add 8 parts of ternary chlorinated vinegar, cellulose acetate butyrate, chlorinated paraffin-70, antioxidant 168 mixture, keep warm for 1 hour and cool down to 70°C, add 2 parts of PEG -2000, 4 parts of isophorone diisocyanate, stirred for 0.5h;

[0046] 2) Add 30 parts of chlorinated fatty acid methyl esters to the reactor after the reaction in step 1), raise the temperature to 80° C., keep it warm for 1 hour, and...

Embodiment 2

[0054] A migration-resistant micro-crosslinked structure environment-friendly plasticizer, in parts by mass, its raw material formula components are as follows:

[0055]

[0056] A preparation method of a migration-resistant micro-crosslinked structure environment-friendly plasticizer, comprising the following steps:

[0057] (1) Take 25 parts of epoxy fatty acid methyl ester, 16 parts of polytrimethylene sebacate, 6 parts of dipropylene glycol methyl ether acetate, stir at a speed of 120r / min, heat to 90°C, and then add 8 parts The mixture of tribasic chlorinated vinegar, cellulose acetate butyrate, chlorinated paraffin-70, and antioxidant 168 was kept warm for 1 hour and then cooled to 65°C, and 4 parts of polyethylene glycol and 6 parts of toluene diisocyanate were added and stirred 0.5h;

[0058] (2) Add 35 parts of chlorinated fatty acid methyl esters to the reactor after the reaction in step (1), heat up to 70° C., keep warm for 1 hour, and distill under reduced pres...

Embodiment 3

[0061] A migration-resistant micro-crosslinked structure environment-friendly plasticizer, in parts by mass, its raw material formula components are as follows:

[0062]

[0063] The preparation method of this embodiment comprises the following steps:

[0064] (1) Take 50 parts of epoxy fatty acid methyl ester, 10 parts of adipic acid polyester, 6 parts of dipropylene glycol methyl ether acetate, stir at a speed of 120r / min, heat to 100°C, and then add 10 parts of The mixture of tribasic chlorinated vinegar, cellulose acetate butyrate, chlorinated paraffin-70, and antioxidant 168 was kept warm for 1 hour and then cooled to 70°C. 3 parts of polytetrahydrofuran diol and 6 parts of toluene diisocyanate were added and stirred for 0.5 h;

[0065] (2) Add chlorinated fatty acid methyl esters to the reaction kettle after the reaction in step (1), heat up to 80°C, keep warm for 1 hour, and distill under reduced pressure to obtain the final migration-resistant environmental protect...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
viscosityaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a migration-resistant environment-friendly plasticizer with a micro-crosslinking structure and a preparation method of same. The raw material formula mainly comprises the following components in parts by weight: 10-70 parts of epoxidized fatty acid ester, 5-40 parts of a polyester plasticizer, 3-5 parts of vinyl chloride-vinyl acetate, 1-3 parts of cellulose acetate butyrate, 3-5 parts of chlorinated paraffin, 0.1-2 parts of an antioxidant, 2-6 parts of polyether polyol, 3-10 parts of a polyurethane curing agent and 5-60 parts of chlorinated fatty acid methyl ester. By constructing a micro-crosslinking structure, the compatibility of epoxidized fatty acid ester and PVC resin is fully utilized, and an interpenetrating network structure can be formed after reactive hydrogen contained in the epoxidized fatty acid ester reacts with isocyanate. The micro-crosslinking structure has a more obvious effect on preventing the plasticizer from being separated out and is higher in heat-resistant stability, so that the problems that the plasticizer is prone to migration, poor in heat-resistant stability, short in service life, not environmentally friendly and the like are solved.

Description

technical field [0001] The invention relates to a plasticizer, in particular to a migration-resistant micro-crosslinked structure environment-friendly plasticizer and a preparation method thereof. The plasticizer is mainly used in the preparation of polyvinyl chloride film. Background technique [0002] The main component of polyvinyl chloride film is polyvinyl chloride, which is widely used in packaging and other fields. PVC film needs to add other components to enhance its performance, such as mechanical properties, heat resistance, toughness, and ductility. Wait. Plasticizer is a polymer material additive widely used in industrial production, also known as plasticizer. The use of plasticizers can improve the performance of polymer materials, reduce production costs, and increase production efficiency. It is an important class of chemical product additives, and its content can sometimes reach 50% of the product. Plasticizer molecules can be inserted between polymer mole...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/00C08L75/04C08L67/02C08L1/14C08L27/06
CPCC08L91/00C08L27/06C08L2205/035C08L75/04C08L67/02C08L1/14
Inventor 文秀芳王铭鄢远洋皮丕辉徐守萍程江
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com