Silicon-oxygen composite negative electrode material, preparation method thereof and lithium ion battery

A negative electrode material, silicon-oxygen technology, applied in battery electrodes, secondary batteries, circuits, etc., can solve the problems of complex coating process, no breakthrough in performance improvement, and high coating cost.

Active Publication Date: 2021-07-02
BTR NEW MATERIAL GRP CO LTD +1
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Titanium dioxide is also one of the common coating materials. The first effect and capacity have been improved to a certain extent. However, the high coating cost and complicated coating process limit its use, and at the same time, no breakthrough has been made in performance improvement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicon-oxygen composite negative electrode material, preparation method thereof and lithium ion battery
  • Silicon-oxygen composite negative electrode material, preparation method thereof and lithium ion battery
  • Silicon-oxygen composite negative electrode material, preparation method thereof and lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0077] Second aspect, such as figure 1 As shown, the application provides a method for preparing a silicon-oxygen composite negative electrode material, comprising the following steps:

[0078] S100, mixing the precursor with the pre-lithiated carbon-coated silicon-oxygen material, and performing a solid-state thermal reaction under a protective atmosphere to obtain a silicon-oxygen composite negative electrode material; the precursor includes a mixture of a phosphate ion-containing compound and a metal compound , metal phosphate, at least one of a mixture of a silicate ion compound and a metal compound, and a metal silicate; the silicon-oxygen composite negative electrode material includes a silicon-oxygen material and a composite coating layer formed on the surface of the silicon-oxygen material, The composite coating layer includes a carbon material and a lithium-containing compound, the carbon material has pores, and the lithium-containing compound is filled in the pores. ...

Embodiment 1

[0128] (1) react carbon-coated silicon-oxygen material SiO / C with metal lithium to obtain pre-lithiated carbon-coated silicon-oxygen material Li-SiO / C, wherein the lithium content is 10 wt%;

[0129] (2) Put V 2 o 5 Mix with phosphoric acid in a molar ratio of 1:3 to obtain a precursor;

[0130] (3) After high-speed dispersion of 5g precursor and 100g Li-SiO / C, under the protection of Ar gas, roast at 900°C for 6 hours, control the heating rate at 2°C / min, disperse and sieve after natural cooling to obtain silicon Oxygen composite anode material.

[0131] The average particle size (D 50 ) is 5.13μm, and the tap density is 0.98g / cm 3 , the specific surface area is 2.19m 2 / g, the porosity is 1.98%, and the carbon content is 5.0wt%. The composite coating layer of the silicon-oxygen composite negative electrode material is 100nm, and the lithium-containing compound is mainly Li 3 V 2 (PO 4 ) 3 , the lithium-containing compound is dispersed and filled in the pores of the...

Embodiment 2

[0133] (1) react carbon-coated silicon-oxygen material SiO / C with metal lithium to obtain pre-lithiated carbon-coated silicon-oxygen material Li-SiO / C, wherein the lithium content is 10 wt%;

[0134] (2) MgO and SiO 2 Mix according to the molar ratio of 1:1 to obtain the precursor;

[0135] (3) After high-speed dispersion of 5g precursor and 100g Li-SiO / C, under the protection of Ar gas, bake at 700°C for 6 hours, control the heating rate at 2°C / min, disperse and sieve after natural cooling to obtain silicon Oxygen composite anode material.

[0136] The average particle diameter (D 50 ) is 5.12μm, and the tap density is 0.98g / cm 3 , the specific surface area is 2.17m 2 / g, the porosity is 1.99%, and the carbon content is 5.0wt%. The composite coating layer of the silicon-oxygen composite negative electrode material is 100nm, wherein the lithium-containing compound includes Li 2 MgSiO 4 , the lithium-containing compound is dispersed and filled in the pores of the carbon ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a silicon-oxygen composite negative electrode material, a preparation method thereof and a lithium ion battery, the silicon-oxygen composite negative electrode material comprises a silicon-oxygen material and a composite coating layer coating the surface of the silicon-oxygen material, the composite coating layer comprises a carbon material and a lithium-containing compound, the carbon material has pores, and the pores are filled with the lithium-containing compound. The silicon-oxygen composite negative electrode material and the preparation method thereof are simple and low in cost, industrial production is easy to realize, the prepared silicon-oxygen composite negative electrode material has excellent electrochemical cycle and expansion inhibition performance, and the service life of a lithium ion battery can be prolonged.

Description

technical field [0001] The present application relates to the field of lithium-ion batteries, and relates to a silicon-oxygen composite negative electrode material, a preparation method thereof, and a lithium-ion battery. Background technique [0002] Silicon oxide material is an essential anode material in a new generation of ultra-large capacity lithium-ion batteries. The silicon oxide industry has been researching and laying out the development of silicon-based lithium-ion batteries for more than ten years. However, silicon-based materials represented by silicon oxide have not been used on a large scale. The main factor limiting the application of silicon oxide materials is caused by the natural disadvantages of silicon-based materials. High expansion and drastic volume change, low first effect, etc. are all problems that need to be solved urgently. [0003] Interfacial reaction regulation is one of the important directions to suppress the expansion of the pole piece an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/48H01M4/62H01M10/0525
CPCH01M4/366H01M4/483H01M4/62H01M4/624H01M4/625H01M4/628H01M10/0525Y02E60/10H01M4/36H01M4/5825H01M4/485H01M4/364H01M4/48H01M10/052H01M4/1395H01M4/38H01M4/131H01M2004/027H01M2004/021H01M4/382H01M4/587H01M4/386H01M4/134
Inventor 谢维庞春雷邓志强任建国贺雪琴
Owner BTR NEW MATERIAL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com