Alignment gold-transfer gold-coating printing coating film and preparation method thereof

A technology of lamination and raw materials, which is applied in the field of alignment-to-gold printing lamination and its preparation, can solve the problems of products that are not durable, difficult to clean, easy to weather, etc. Effect

Inactive Publication Date: 2021-04-23
DONGGUAN IUIU HOUSEHOLD PROD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently popular lace and NT tablecloths on the market are printed, plain and other styles of products, which are prone to problems such as undurable, easy to weather, tear, damage, and difficult to clean during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alignment gold-transfer gold-coating printing coating film and preparation method thereof
  • Alignment gold-transfer gold-coating printing coating film and preparation method thereof
  • Alignment gold-transfer gold-coating printing coating film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A gold-over-gold printing film for alignment transfer, comprising the following raw materials in parts by weight:

[0035]

[0036] The resin powder is PVC resin powder, the degree of polymerization of the PVC resin powder is 1000, the particle size is 0.1mm, and the density is 1.35g / cm 3 .

[0037] Each part of the ACR additive includes the raw materials of the following parts by weight:

[0038]

[0039] The silane coupling agent is a mixture composed of aminopropyltriethoxysilane, aminopropyltrimethoxysilane and triglycidyloxypropyltrimethoxysilane in a weight ratio of 0.6:0.8:0.4.

[0040] The ACR auxiliary agent is prepared through the following steps:

[0041] S1. According to parts by weight, add deionized water into the reaction device, then add butyl acrylate, silane coupling agent and o-phenylphenoxyethyl acrylate and stir for 20 minutes, add ammonium persulfate, pass through nitrogen, and heat React at 30°C for 30 minutes to obtain mixture A, which is ...

Embodiment 2

[0054] A gold-over-gold printing film for alignment transfer, comprising the following raw materials in parts by weight:

[0055]

[0056] The resin powder is PVC resin powder, the degree of polymerization of the PVC resin powder is 1050, the particle size is 0.13mm, and the density is 1.38g / cm 3 .

[0057] Each part of the ACR additive includes the raw materials of the following parts by weight:

[0058]

[0059] The silane coupling agent is a mixture composed of aminopropyltriethoxysilane, aminopropyltrimethoxysilane and triglycidyloxypropyltrimethoxysilane in a weight ratio of 0.7:0.9:0.5.

[0060] The ACR auxiliary agent is prepared through the following steps:

[0061] S1. According to parts by weight, add deionized water into the reaction device, then add butyl acrylate, silane coupling agent and o-phenylphenoxyethyl acrylate and stir for 25 minutes, add ammonium persulfate, pass through nitrogen, and heat Reaction at 35°C for 38 minutes to obtain mixture A, set...

Embodiment 3

[0074] A gold-over-gold printing film for alignment transfer, comprising the following raw materials in parts by weight:

[0075]

[0076] The resin powder is PVC resin powder, the degree of polymerization of the PVC resin powder is 1100, the particle size is 0.15mm, and the density is 1.4g / cm 3 .

[0077] Each part of the ACR additive includes the raw materials of the following parts by weight:

[0078]

[0079]

[0080] The silane coupling agent is a mixture composed of aminopropyltriethoxysilane, aminopropyltrimethoxysilane and triglycidyloxypropyltrimethoxysilane in a weight ratio of 0.8:1.0:0.6.

[0081] The ACR auxiliary agent is prepared through the following steps:

[0082] S1. According to parts by weight, add deionized water into the reaction device, then add butyl acrylate, silane coupling agent and o-phenylphenoxyethyl acrylate and stir for 30 minutes, add ammonium persulfate, pass through nitrogen, and heat Reaction at 40°C for 45 minutes to obtain mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of new materials, in particular to an alignment gold-transfer gold-overprinting coating film and a preparation method thereof. The film comprises the following raw materials by weight: 60-75 parts of filler, 45-55 parts of resin powder, 0.06-0.2 part of pigment powder, 0.01-0.15 part of titanium dioxide, 1.5-2.5 parts of an ACR assistant, 0.25-0.4 part of stearic acid, 5-10 parts of D80 solvent oil, 1.5-2.5 parts of a heat stabilizer and 25-35 parts of diisononyl phthalate. The film product disclosed by the invention has the characteristics of high cold resistance, skid resistance, flame retardance, humidity sensitivity, discoloration, rich printing pattern types and more bright and diverse colors, also has the characteristics of stable product quality, exquisite patterns, comfortable hand feeling, environmental protection and no toxicity, can bring consumers a novel and extra-value feeling, and realizes the combination of a gold film and three-dimensional printing.

Description

technical field [0001] The invention relates to the technical field of new materials, in particular to an alignment-transferred gold-coated gold printing film and a preparation method thereof. Background technique [0002] Tablecloth is an item that is covered on the table or tabletop to prevent dirt or increase the appearance. According to the production process, it is mainly divided into two categories: plastic and textile. Plastics include PVC tablecloths, EVA tablecloths, PEVA tablecloths, hot stamping tablecloths, cotton-based PVC tablecloths, PP tablecloths, polyethylene tablecloths, and cast film tablecloths. Wait. PVC tablecloth is widely used in daily life because of its easy cleaning, convenience and practicality. [0003] Therefore, tablecloth products play a pivotal role in home decoration. More and more people have a large demand and high requirements for tablecloths in order to pursue a perfect life. Currently popular lace and NT tablecloths on the market ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08L33/08C08K13/02C08K3/22C08K5/09C08K5/12C08K3/26C08J5/18B41M1/22B41M1/30B41M1/12B41M3/00
CPCC08J5/18B41M1/22B41M1/30B41M1/12B41M3/00C08J2327/06C08J2491/00C08J2433/08C08K13/02C08K2003/2241C08K5/09C08K5/12C08K2003/265C08K2201/011C08K2201/014
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com