A kind of casting aluminum-silicon alloy and preparation method thereof

A technology for casting aluminum-silicon alloys and intermediate alloys, which is applied in the field of metal materials, can solve the problems of poor heat dissipation and toughness of aluminum-silicon alloys, and cannot meet the needs of aluminum-silicon alloys, and achieve improved toughness, improved Fe phase morphology, and low thermal cracking effect of propensity

Active Publication Date: 2022-04-15
成都慧腾创智信息科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to solve the problems of poor heat dissipation and toughness of existing aluminum-silicon alloys, which cannot meet the needs of aluminum-silicon alloys in the photovoltaic field, and provide a cast aluminum-silicon alloy and its Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of casting aluminum-silicon alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A cast aluminum-silicon alloy, comprising the following components by mass percentage: Si: 8.5%; Fe: 0.1%; Co: 0.15%; Eu: 0.12%; B: 0.04%; La: 0.09%; Zn: 0.2% ; Unavoidable impurities Cr+Mn+V+Ti: less than 0.01%; the balance is Al.

[0039] The preparation method of the cast aluminum-silicon alloy is:

[0040] (1) According to the set chemical composition, weigh industrial pure aluminum, crystalline silicon, Al-20Fe master alloy, Al-10Co master alloy, Al-3B master alloy, Al-La master alloy, pure zinc, Al -Eu master alloy. Wash and dry the weighed raw materials for later use.

[0041] (2) Melt industrial pure aluminum preheated to 150°C in a smelting furnace at a melting temperature of 780°C. After melting, add 0.4% slag removal agent based on the mass of the aluminum ingot, stir for 20 minutes, and keep warm for 30 minutes after removing slag ;

[0042] (3) After cooling the melt in step (2) to 750°C, add crystalline silicon, Al-20Fe master alloy, and Al-10Co master...

Embodiment 2

[0046] A cast aluminum-silicon alloy, comprising the following components by mass percentage: Si: 9.0%; Fe: 0.1%; Co: 0.16%; Eu: 0.13%; B: 0.04%; La: 0.08%; Zn: 0.3% ; Unavoidable impurities Cr+Mn+V+Ti: less than 0.01%; the balance is Al.

[0047] The preparation method is the same as in Example 1.

Embodiment 3

[0049] A cast aluminum-silicon alloy, comprising the following components by mass percentage: Si: 9.5%; Fe: 0.15%; Co: 0.23%; Eu: 0.14%; B: 0.04%; La: 0.1%; Zn: 0.4% ; Unavoidable impurities Cr+Mn+V+Ti: less than 0.01%; the balance is Al.

[0050] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a casting aluminum-silicon alloy and a preparation method thereof. The cast aluminum-silicon alloy includes the following components in terms of mass percentage: Si: 8.5-10.5%; Fe: 0.1-0.2%; Co: 0.15-0.32%; B: 0.04-0.15%; mixed rare earth: 0.2-0.3% %; Zn: 0.1-0.5%; unavoidable impurities: less than 0.15%; the balance is Al. The aluminum-silicon alloy of the invention has high thermal conductivity and toughness, good fluidity and is easy to form complex thin-walled parts, and can meet the use requirements of the photovoltaic field.

Description

technical field [0001] The invention relates to the technical field of metal materials, in particular to a casting aluminum-silicon alloy and a preparation method thereof. Background technique [0002] The rapid promotion of photovoltaic power generation requires higher and higher heat dissipation capabilities of photovoltaic inverters. Photovoltaic inverters often need to be installed in harsh outdoor environments, and their product sealing must meet the level of IP67 or higher. This high sealing provides good protection for the electronic components inside the inverter, but it will also cause internal damage in extreme cases. The high heat and pressure are difficult to release. In order to avoid brittle bursting of the inverter in extreme cases, the die-casting aluminum-silicon alloy heat dissipation shell is also required to have good toughness, so that it can release the pressure through sufficient deformation under the impact load of the explosion, that is, ductile cra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/04C22C1/03C22C1/06B22D17/00
CPCC22C21/04C22C1/03C22C1/026C22C1/06B22D17/00
Inventor 孙自来
Owner 成都慧腾创智信息科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com