High-wear-resistance aluminum alloy material treatment process

An aluminum alloy material and processing technology, applied in electrolytic coatings, anodizing, surface reaction electrolytic coatings, etc., can solve the problems of insufficient wear resistance of aluminum alloy materials, general surface hardness of aluminum alloy materials, and wear of aluminum alloy materials. , to improve the quality of the final product, reduce the amount of free N, and improve the tensile strength

Inactive Publication Date: 2021-02-09
江苏信轮美合金发展有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing aluminum alloy materials have good toughness and anti-corrosion properties. However, the surface hardness of aluminum alloy materials is average. For some long-term wear environments, the wear resistance of aluminum alloy materials is insufficient, which will cause damage to aluminum alloy materials. Rapid wear, resulting in damage, for this reason, we propose a high wear-resistant aluminum alloy material treatment process to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] It is a kind of high wear resistance aluminum alloy material treatment process in the preferred embodiment of the present invention, including

[0023] Step 1: First, preheat the heating furnace to 100°C, then put the pure aluminum block into the boiler to melt, keep the temperature at 480°C for 45 minutes, remove impurities and deoxidize, and then raise the furnace temperature to 500°C , add alloy material and rare earth, then heat to 630°C, keep warm for 2h;

[0024] Step 2: put the aluminum alloy material processed in step 1 into the refining furnace for refining, control the furnace temperature at 710°C, keep the time at 2 hours, blow nitrogen gas and stir throughout the process, ensure the nitrogen concentration at 40%, so that the chemical composition meets the component requirements, Carry out degassing with vacuum degassing furnace, degassing temperature is 730 DEG C, and pumping time is at 5h;

[0025] Step 3: adding alloys for modulation treatment, ensuring t...

Embodiment 2

[0033] It is a kind of high wear resistance aluminum alloy material treatment process in the preferred embodiment of the present invention, including

[0034] Step 1: First, preheat the heating furnace to 100°C, then put the pure aluminum block into the boiler to melt, keep the temperature at 500°C for 50 minutes, remove impurities and deoxidize, and then raise the furnace temperature to 580°C , adding alloy materials and rare earths, then heating to 650°C and keeping the temperature for 3h;

[0035]Step 2: put the aluminum alloy material processed in step 1 into the refining furnace for refining, control the furnace temperature at 730°C, keep the time at 4h, blow nitrogen gas and stir throughout the process, ensure the nitrogen concentration at 50%, so that the chemical composition meets the component requirements, Carry out degassing with vacuum degassing furnace, degassing temperature is 750 DEG C, and pumping time is at 6h;

[0036] Step 3: adding alloys for modulation tr...

Embodiment 3

[0044] It is a kind of high wear resistance aluminum alloy material treatment process in the preferred embodiment of the present invention, including

[0045] Step 1: First, preheat the heating furnace to 100°C, then put the pure aluminum block into the boiler to melt, keep the temperature at 490°C for 48 minutes, remove impurities and deoxidize, and then raise the furnace temperature to 550°C , adding alloy materials and rare earths, then heating to 640°C and keeping it warm for 2h;

[0046] Step 2: put the aluminum alloy material processed in step 1 into the refining furnace for refining, control the furnace temperature at 720°C, keep the time at 3 hours, blow nitrogen gas throughout the process and stir to ensure that the nitrogen concentration is at 45%, so that the chemical composition meets the component requirements. Carry out degassing with vacuum degassing furnace, degassing temperature is 740 ℃, and the time of pumping is at 5h;

[0047] Step 3: adding alloys for mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-wear-resistance aluminum alloy material treatment process which comprises the following operation steps that a pure aluminum block is added into a boiler for melting, and subjected to impurity removing and deoxidizing; an aluminum alloy material is put into a refining furnace for refining; alloy is added for modulation treatment, and an aluminum alloy melt X is obtained; the aluminum alloy melt X is subjected to argon shield die casting at the temperature of 600 DEG C, and finally subjected to air cooling to the room temperature; and the aluminum alloy melt X iscast through a semi-continuous casting method, water cooling is conducted after casting, and an aluminum alloy casting body Y is obtained. Through the heat treatment process, the cracking risk of thecasting can be greatly reduced on the premise that the mechanical property of the aluminum alloy casting is improved, and the quenching quality of parts is improved, so that the structural hardness ofthe aluminum alloy material can be greatly improved, and the wear resistance of the material is further improved. According to the high-wear-resistance aluminum alloy material treatment process, an aluminum alloy cylinder body is subjected to surface treatment through electrochemistry, and the surface hardness of the aluminum alloy after surface treatment is high.

Description

technical field [0001] The invention relates to the field of aluminum alloy processing, in particular to a process for processing aluminum alloy materials with high wear resistance. Background technique [0002] Aluminum alloy is an alloy based on aluminum with a certain amount of other alloying elements added, which is one of the light metal materials. In addition to the general characteristics of aluminum, aluminum alloys also have specific characteristics of some alloys due to the different types and quantities of alloying elements added. The density of aluminum alloy is 2.63-2.85g / cm, it has high strength (σb is 110-650MPa), the specific strength is close to high alloy steel, the specific stiffness exceeds steel, it has good casting performance and plastic processing performance, and good electrical conductivity , thermal conductivity, good corrosion resistance and weldability, can be used as structural materials, and has a wide range of applications in aerospace, aviat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/03B22D11/115C22F1/04C23F1/36C25D11/08C25D11/10B22D1/00
CPCB22D1/00B22D11/003B22D11/115C22C1/026C22C1/03C22F1/002C22F1/04C23F1/36C25D11/08C25D11/10
Inventor 阮继忠
Owner 江苏信轮美合金发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com