Preparation of a porous graphene-loaded weak-light photocatalyst-nanosilver composite antiviral powder

A porous graphene, low-light technology, applied in disinfection, disinfectants, botanical equipment and methods, etc., can solve problems such as poor persistence and low data on the killing rate of infectious viruses, and expand the application field and scope. , the effect of high sterilization and antivirus efficiency, high sterilization rate and virus killing rate

Active Publication Date: 2022-02-08
聚治苏州纳米科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The domestic market basically uses organic antibacterial agents, and a small amount of silver-loaded zirconium phosphate is used as an additive to make products with antibacterial properties, but its killing rate for infectious viruses has the disadvantages of low data and poor persistence.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation of a porous graphene-loaded weak-light photocatalyst-nanosilver composite antiviral powder
  • Preparation of a porous graphene-loaded weak-light photocatalyst-nanosilver composite antiviral powder
  • Preparation of a porous graphene-loaded weak-light photocatalyst-nanosilver composite antiviral powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Preparation of highly dispersed nano-graphene microsheet slurry: 3g of expanded graphite was added to 992.4g of aqueous solution, and 3g of dispersant CTAB, 0.1g of defoamer DELTA-FC1501, 0.5g of wetting In the aqueous solution of agent TEGO245, stir and mix, emulsifier pre-disperse. Then grind and disperse in a sand mill, the filling rate of zirconium beads is 70%, the diameter of zirconium beads is 0.3mm, and the grinding line speed is 12m / s. Under the synergistic effect of 1g intercalation agent PVP, dispersant and grinding shear force, Prepare a nano-graphene microsheet slurry with a diameter of about 5 microns and a thickness of ≤10 layers.

[0027] Preparation of zinc oxide weak-light photocatalyst slurry: Add 20g of zinc nitrate to 72.8g of ethanol and stir, then add 0.2g of n-butyl titanate, 3g of acetylacetone, 3g of ethylenediaminetetraacetic acid, 1g of citric acid, and use ammonia water Adjust the pH to 8, quickly stir at 80°C to form a transparent sol, pre...

Embodiment 2

[0031] Preparation of highly dispersed nano-graphene microsheet slurry: 5g of expanded graphite was added to 992.4g of aqueous solution, and while stirring, 5g of dispersant CTAB, 0.15g of defoamer DELTA-FC1503, 0.6g of wetting In the aqueous solution of agent TEGOwet280, stir and mix well, and pre-disperse with an emulsifier. Carry out sand mill to grind and disperse then, zirconium bead filling rate is 75%, and the diameter of zirconium bead selection is 0.3mm, and grinding line speed 12m / s, in 2g intercalation agent dodecylbenzene sulfonic acid, dispersant and grinding shear Under the synergistic action of forces, a nano-graphene microsheet slurry with a diameter of about 3 microns and a thickness of ≤10 layers is made.

[0032] Preparation of zinc oxide weak-light photocatalyst slurry: Add 30g zinc oxalate to 60g ethanol and stir, then add 0.5g titanium tetrachloride, 4g acetylacetone, 4g ethylenediaminetetraacetic acid, 1.5g citric acid, adjust with ammonia water pH to 9...

Embodiment 3

[0036] Preparation of highly dispersed nanographene microsheet slurry: Add 8g of expanded graphite to 983g of aqueous solution, and add 8g of dispersant CTAB, 0.2g of defoamer DELTA-FC1522, and 0.8g of wetting agent while stirring In the aqueous solution of TEGO wet280, stir and mix well, and pre-disperse with an emulsifier. Carry out sand mill to grind and disperse then, zirconium bead filling rate is 80%, and zirconium bead is selected to be that diameter is 0.3mm, and grinding line speed 12m / s, in the synergy of 3g intercalation agent ferric chloride, dispersant and grinding shearing force Under the action, a nano-graphene microsheet slurry with a diameter of about 2 microns and a thickness of ≤10 layers is made.

[0037] Preparation of zinc oxide weak-light photocatalyst slurry: 40g zinc stearate was added to 47.2g ethanol and stirred, then 0.8g isopropyl titanate, 5g acetylacetone, 5g ethylenediaminetetraacetic acid, 2g citric acid were added successively, Adjust the pH ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

A method for preparing porous graphene-loaded weak-light photocatalyst-nano-silver composite antiviral powder, mixing a dispersant in an aqueous solution, prefabricating an expanded graphite premix, and then grinding with a sand mill, adding an intercalation agent and a dispersant , wetting agent, defoaming agent and grinding shear force to prepare a nano-graphene microsheet solution with less than 10 layers; use the sol-gel method to make titanium doped into the zinc oxide lattice while on its surface Form an amorphous titanium dioxide coating layer, prepare a low-light photocatalyst powder, and make a low-light photocatalyst dispersion with a particle size below 50 nanometers; then, use a high-efficiency complexing agent to prepare the silver compound into a metastable ultra-high Concentration nano-complex silver solution; finally, the above three solutions are mixed and ultrasonicated, and the composite slurry is irradiated under a constant power fluorescent lamp to reduce the remaining silver ions, and then dried to obtain a porous graphene-loaded weak light photocatalyst-nano-silver composite Antiviral powder has excellent bactericidal and virucidal capabilities.

Description

technical field [0001] The invention belongs to the technical field of preparation of antiviral materials, and in particular relates to the preparation of porous graphene-loaded weak-light photocatalyst-nano-silver composite antiviral powder. Background technique [0002] In recent years, studies have reported that silver nanoparticles can effectively inhibit human immunodeficiency virus, hepatitis B virus, respiratory syncytial virus, herpes simplex virus-1, monkeypox virus and influenza virus. With its extremely high antibacterial activity and no drug resistance, nano silver has incomparable advantages over traditional inorganic antibacterial agents. Although the antimicrobial activity of nanosilver is widely recognized, silver is a heavy metal, and even in nanometer form, excessive contact with the human body may produce mild toxicity. How to reduce the amount of silver while maintaining its high antibacterial activity is an important issue facing the development of nano...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A01N59/16A01N25/08A01N25/12A61L2/08A01P1/00A01P3/00
CPCA01N59/16A01N25/08A01N25/12A61L2/088A61L2/084
Inventor 张春明冉伟
Owner 聚治苏州纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap