Construction method of water-based heavy-duty anti-corrosion fluorocarbon coating

A technology of anti-corrosion fluorocarbon coating and construction method, which is applied in the direction of anti-corrosion coatings, coatings, and devices for coating liquid on the surface, etc. It can solve the problems of affecting the service life of the product, uneven spraying effect, and poor adsorption effect. Achieve the effect of preventing oxidation, good chemical stability and enhancing wear resistance

Inactive Publication Date: 2020-12-25
葫芦岛渤船工贸通和防腐有限公司
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the existing anti-corrosion spraying process based on fluorocarbon coatings, the spraying effect of fluorocarbon coatings is not uniform, and the anti-corrosion time is short during use, and the phenomenon of shedding may occur, and the adsorption effect is not good at the same time, so that the coating and There are gaps between the metal substrates, resulting in corrosion, thus affecting the service life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A construction method of a water-based heavy-duty anti-corrosion fluorocarbon coating is carried out as follows:

[0025] Step 1. Surface cleaning treatment: Use alkaline degreasing agent to remove oil stains on the steel surface, use tank immersion method, and wash with water after cleaning. Alkaline degreasing agents include sodium phosphate, sodium carbonate and sodium hydroxide, and the treatment time is 10 minutes at 50°C.

[0026] Step 2. Rust removal: use pickling to remove rust, for example, use 12% HCl to remove rust on the surface of the steel, use tank immersion method, and then wash with water.

[0027] Step 3, phosphating: add zinc-based or iron-based phosphating agent for phosphating to form a phosphating film, the phosphating temperature is 45°C, and the phosphating time is 3 minutes.

[0028] Step 4: Spray primer coating: The primer coating is water-based heavy-duty anti-corrosion fluorocarbon coating with a spraying thickness of 10 μm. After spraying, ...

Embodiment 2

[0032] A construction method of a water-based heavy-duty anti-corrosion fluorocarbon coating is carried out as follows:

[0033] Step 1. Surface cleaning treatment: Use alkaline degreasing agent to remove oil stains on the steel surface, use tank immersion method, and wash with water after cleaning. Alkaline degreasing agents include sodium phosphate, sodium carbonate and sodium hydroxide, and the treatment time is 5 minutes at 55°C.

[0034] Step 2. Rust removal: use pickling to remove rust, for example, use 12% HCl to remove rust on the surface of the steel, use tank immersion method, and then wash with water.

[0035] Step 3, phosphating: add zinc-based or iron-based phosphating agent for phosphating to form a phosphating film, the phosphating temperature is 40°C, and the phosphating time is 3 minutes.

[0036] Step 4: Spray primer paint: The primer paint is a water-based heavy-duty fluorocarbon paint with a spray thickness of 15 μm. After spraying, it is cured, and the pr...

Embodiment 3

[0040] A construction method of a water-based heavy-duty anti-corrosion fluorocarbon coating is carried out as follows:

[0041] Step 1. Surface cleaning treatment: Use alkaline degreasing agent to remove oil stains on the steel surface, use tank immersion method, and wash with water after cleaning. Alkaline degreasing agents include sodium phosphate, sodium carbonate and sodium hydroxide, and the treatment time is 7 minutes at 60°C.

[0042] Step 2. Rust removal: use pickling to remove rust, for example, use 12% HCl to remove rust on the surface of the steel, use tank immersion method, and then wash with water.

[0043] Step 3, phosphating: add zinc-based or iron-based phosphating agents for phosphating to form a phosphating film, the phosphating temperature is 40°C, and the phosphating time is 10 minutes.

[0044] Step 4: Spraying the primer coating: the primer coating is a water-based heavy-duty anti-corrosion fluorocarbon coating, and the spraying thickness is 20 μm. Afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a construction method of a water-based heavy-duty anti-corrosion fluorocarbon coating. The construction method comprises the following steps of removing oil stains on the surface of steel by using an alkaline degreasing agent, and washing with water after cleaning; removing rust scale by using acid pickling, removing the rust scale on the surface of the steel, and then conducting water washing; adding a phosphating agent for phosphating to form a phosphating film; adopting water-based heavy-duty anti-corrosion fluorocarbon paint as primer paint to be sprayed, being thespraying thickness 10-20 microns, and forming a primer coating through maintenance; using the water-based heavy-duty anti-corrosion fluorocarbon coating as a finish paint coating to be sprayed, beingthe spraying thickness 10-30 microns, and forming a finish paint protective coating through maintenance. According to the construction method of the water-based heavy-duty anti-corrosion fluorocarboncoating, the combination degree of the primer, the finish paint and the surface of the steel is high, the adhesive force of the coating is improved, the wear resistance, salt water resistance, weatherresistance and other properties of the coating are enhanced, the corrosion resistance of the steel is improved, meanwhile, the obtained coating is flat and uniform, the coating is lighter and thinner, the less paint can be used, cost is reduced, and construction is convenient.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to a construction method of a water-based heavy-duty anti-corrosion fluorocarbon coating. Background technique [0002] With the development of the economy, the chemical industry, steel components, ships, power plants and other industries have increasingly urgent requirements for anti-corrosion of plates, pipes, pumps, etc., and the grades have been continuously improved. The anti-corrosion performance of materials has also put forward higher and higher requirements. Coatings with resin as the main film-forming substance are called fluorocarbon coatings. Such coatings have excellent chemical resistance, corrosion resistance, abrasion resistance, insulation, and stain resistance. The anti-corrosion spraying process refers to the Spray coating to achieve anti-corrosion effect and avoid items from being corroded. However, in the existing anti-corrosion spraying process...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B05D7/14B05D7/24B05D3/10B05D7/00C09D127/18C09D123/12C09D7/61C09D7/65C09D5/08
CPCB05D3/102B05D7/14B05D7/24B05D7/544B05D2202/10B05D2506/15B05D2507/02C08K2003/2241C08K2003/3009C08L2205/02C08L2205/035C09D5/08C09D127/18C09D7/61C09D7/65C08L23/12C08L23/28C08L83/12C08L77/00C08K3/30C08K3/22
Inventor 耿季平郑红伟
Owner 葫芦岛渤船工贸通和防腐有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com