A kind of black surface composite coating and preparation method thereof

A surface composite and black technology, which is applied in the field of black surface composite coating and its preparation, can solve problems such as easy to see, coating peeling off, easy to leave scratches on the top black chrome surface, etc.

Active Publication Date: 2022-01-04
JOMOO KITCHEN & BATHROOM
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Both baked black paint products and electroplated hexavalent black chrome can obtain a high-blackness appearance, but the existing high-blackness black products have poor scratch resistance. The plating layer falls off, resulting in the exposure of the underlying substrate; the black new material product made of water mist nickel + hexavalent black chrome encounters a sharp product, and the surface of the top layer of black chromium is easy to scratch, and the bottom water mist nickel material is easy to see. There is an obvious difference in the color contrast between the bottom water mist nickel layer and the surface black chrome layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of black surface composite coating and preparation method thereof
  • A kind of black surface composite coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0039] The preparation method is basically the same as that of Example 1, except that, when the black nickel layer is electroplated, the black nickel electroplating time is changed, and the black nickel electroplating time is 2700s.

Embodiment 3

[0041] The preparation method is basically the same as that of Example 1, except that, when the black nickel layer is electroplated, the black nickel electroplating time is changed, and the black nickel electroplating time is 3000s.

Embodiment 4

[0043] The preparation method is basically the same as that of Example 1, except that, when the black nickel layer is electroplated, the black nickel electroplating time is changed, and the black nickel electroplating time is 3300s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a black surface composite coating and a preparation method thereof. The black surface coating is sequentially plated with an electroplated copper layer, a black nickel layer and a hexavalent black chromium layer on the surface of a base material. The method includes the following steps: (i) electroplating pre-treatment, cleaning the surface of the metal substrate; (ii) electroplating a copper layer, electroplating a copper layer on the clean substrate obtained in (i); (iii) electroplating a black nickel layer, Black nickel electroplating is performed on the clean copper layer obtained in (ii); black chromium electroplating is performed on (iv) a black chromium layer, and black chromium electroplating is performed on the clean black nickel layer obtained in (iii). The black coating prepared by the method of the present invention not only has a matte black luster, but also has the advantages of corrosion resistance and high hardness.

Description

technical field [0001] The invention relates to a black surface composite coating and a preparation method thereof. Background technique [0002] In order to meet the anti-corrosion performance requirements of traditional kitchen and bathroom hardware products, the surface is basically coated with white chrome, showing a single metallic tone. Since 2018, with the development of kitchen and bathroom products in the direction of fashion, functionality, and intelligence, and the black post-modern industrial style has become popular all over the world, black kitchen and bathroom products have become more and more popular among consumers, and Kohler , Gaoyi, Hansgrohe and other well-known international sanitary ware companies are competing to develop one of the important directions. At present, black kitchen and bathroom hardware products are mainly realized through surface baking varnish technology, that is, a layer of black paint is sprayed on the surface of kitchen and bathro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D5/14C25D3/12C25D3/08C25D3/38
CPCC25D5/14C25D3/12C25D3/08C25D3/38
Inventor 林孝发林孝山刘小龙王汉春李日红
Owner JOMOO KITCHEN & BATHROOM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com