Polypropylene composite material and preparation method and application thereof

A composite material and polypropylene technology, applied in the field of polypropylene composite materials and its preparation, can solve the problems of not suitable for instrument panels and low impact strength of notched cantilever beams, achieve good heat resistance, improve impact performance, and simple preparation process Effect

Pending Publication Date: 2020-09-29
GUANGDONG JUSHI CHEM CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CN109735005A adopts high-density polyethylene and polypropylene as the resin substrate to prepare a polypropylene composite material. The composite material has good fluidity and mechanical properties, and can be used for thinning the wall of automobiles, but its Izod notched impact strength Low, only 27 ~ 36KJ / m 2 , not suitable for making dashboards, especially seamless airbag dashboards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene composite material and preparation method and application thereof
  • Polypropylene composite material and preparation method and application thereof
  • Polypropylene composite material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This embodiment provides a polypropylene composite material, including the raw materials shown in Table 1.

[0045] Among them, the polypropylene is copolymerized polypropylene 7033E3, MI is 8g / 10min (230°C / 2.16kg), flexural modulus is 1140MPa, impact strength is 280J / m, ExxonMobil.

[0046] POE is ethylene elastomer ENGAGE TM 8842, MI is 1.0g / 10min (190°C / 2.16kg), Dow Chemical.

[0047] The nucleating agent is CS-9503, a nucleating agent for amide-type polypropylene beta crystal form, Hangzhou Jufeng New Materials.

[0048] The mineral filler is talc.

[0049] The coupling agent is KH-550.

[0050] The anti-thermal oxygen stabilizer is a compound composed of anti-thermal oxygen stabilizer 1010 and 168 with a mass ratio of 2:1.

[0051] The free radical scavenger is UV-3808; the extractant is BYK-P4200, BYK, Germany; the anti-scratch agent is silicone masterbatch MB50-001, Dow Corning; the lubricant is EBS.

[0052] The preparation method of the present embodiment...

Embodiment 2

[0056] This embodiment provides a polypropylene composite material, the raw material composition of which is shown in Table 1.

[0057] in,

[0058] The polypropylene is copolymerized polypropylene BH975MO, MI is 38g / 10min (230°C / 2.16kg), flexural modulus is 1420MPa, Borouge Chemicals.

[0059] POE is ethylene elastomer ENGAGE TM 8150, MI melt index is 1.0g / 10min (190℃ / 2.16kg), Dow Chemical.

[0060] Mineral fillers are whiskers.

[0061] Other raw materials are selected with embodiment 1.

[0062] The preparation method of the polypropylene of this embodiment is the same as that of Embodiment 1.

Embodiment 3

[0064] This embodiment provides a polypropylene composite material, the raw material composition of which is shown in Table 1.

[0065] in,

[0066] Polypropylene is copolymerized polypropylene BH3820, MI is 28g / 10min (230℃ / 2.16kg), flexural modulus is 981MPa, impact strength is 490J / m, Korea SK;

[0067] The mineral filler is mica.

[0068] Other raw materials are selected with embodiment 1.

[0069] The preparation method of the polypropylene of this embodiment is the same as that of Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Impact strengthaaaaaaaaaa
Melt fingeraaaaaaaaaa
Flexural modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polypropylene composite material as well as a preparation method and application thereof. The polypropylene composite material is prepared from the following raw materials: polypropylene, POE, a nucleating agent, a mineral filler, a coupling agent, a free radical capturing agent, a thermal oxidation resistant stabilizer, an extracting agent, a scratch resistant agent anda lubricating agent, and the melt flow rate of the POE under the test conditions of 190 DEG C and 2.16 kg is 0.5 g / 10 min to 5 g / 10 min. According to the invention, polypropylene is used as a matrix,POE with low melting performance is added, and the mineral filler, the nucleating agent and the extractant are scientifically matched so that the impact performance of the polypropylene composite material is improved, the composite material has good heat resistance and low odor, and the high-quality requirement of the seamless airbag instrument board is met.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a polypropylene composite material and its preparation method and application. Background technique [0002] The materials industry is the backbone of the automotive industry. With the continuous development and progress of society, the sales of automobiles are increasing year by year, and the requirements for materials of automobiles are getting higher and higher. [0003] As the most important interior part of a car, the instrument panel is a thin-walled, large-area, and complex-shaped auto part with many holes for installing instrument components. Interior parts that combine performance and decoration. Before the instrument panel is delivered for use, it is necessary to conduct high and low temperature airbag point explosion experiments to ensure that the airbag pops up safely and effectively. Therefore, there are extremely high requirements for the low...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/14C08L23/08C08L83/04C08K3/34C08K5/134C08K5/526C08K5/20C08K13/02C08K9/10C08K13/06
CPCC08L23/14C08L2201/08C08L2205/03C08L23/0815C08L83/04C08K3/34C08K5/1345C08K5/526C08K5/20C08K13/02C08K9/10C08K13/06
Inventor 熊金标林经萍蔡智勇刘鹏辉董启殿贾似海汪洋
Owner GUANGDONG JUSHI CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap