High-fluidity scratch-resistant spraying-free metallic-silvery-color modified polypropylene material for vehicles

A polypropylene material and high fluidity technology, applied in the field of polymer materials, can solve problems such as the compatibility difference between spray paint and polypropylene, the health risks of on-site employees, and the high requirements for injection molding processes, so as to improve gloss and overcome Inconsistent fluidity, the effect of simplifying the process flow

Pending Publication Date: 2020-09-22
NINGBO TAIYONG AUTOMOTIVE PARTS
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current spraying process also has limitations: 1. The on-site operation environment is not up to standard, which may easily cause the product to granulate; 2. There are differences in the compatibility between the spray paint and polypropylene, and there is a risk of bottoming; 3. The volatilization of spray paint will affect the on-site operation. employee health risk
The Chinese patent with the publication number CN108559178A added aluminum-silver paste and pearlescent powder in order to achieve a good metallic silver effect on the spray-free PP material, but the aluminum flake powder needs to be specially polished and surface-treated and formed with a lubricant as a carrier. The mixture needs to be fed separately during preparation. The talcum powder, aluminum silver bars, pearl powder, and coupling agent are added to the side feed first, and then the remaining raw materials are added to the main feed. The steps are cumbersome and have high requirements for the injection molding process. poor universality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-fluidity scratch-resistant spraying-free metallic-silvery-color modified polypropylene material for vehicles
  • High-fluidity scratch-resistant spraying-free metallic-silvery-color modified polypropylene material for vehicles
  • High-fluidity scratch-resistant spraying-free metallic-silvery-color modified polypropylene material for vehicles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-6

[0075] Examples 1-6 provide high-fluidity, scratch-resistant, spray-free metallic silver-colored modified polypropylene materials for vehicles, and the parts by weight of the raw material components are shown in Table 1. The PP resin used in Examples 1-6 is Formosa Plastics Copolymerized PP Resin 3500. Under the test conditions of 230°C and 2.16KG, the melt mass flow rate is 60g / 10min, which has high fluidity; ethylene-octene copolymerization is elastic The body is SK 875L, and the soft chain segment of octene makes its glass transition temperature lower than that of ethylene-butene copolymerized elastomers, endowing it with better toughness at room temperature and low temperature; The mesh number and purity of the same product above are extremely high; the aluminum powder is ECKARTDE MP 34-20C, the particle size is 34μm; the dispersant is Sinochem Plastics EBS P130; the antioxidant is BASF 1010, 168 and PS802 compound antioxidant; The ultraviolet absorber is Cytec 5411 and 77...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polymer materials, and particularly relates to a high-fluidity scratch-resistant spraying-free metallic-silvery-color modified polypropylene material for vehicles. Raw materials comprise the following components in parts by weight: 50 to 80 parts of PP resin, 5 to 20 parts of polyolefin elastomer, 10 to 40 parts of talcum powder, 0.5 to 5 parts of metal powder, 0.5 to 2 parts of a compatilizer, 0.5 to 2 parts of a dispersing agent, 1 to 3 parts of a scratch-resistant agent, 0.5 to 2 parts of a lubricant, 0.5 to 1 part of an antioxidant and 0.5 to1 part of an ultraviolet absorbent. On the basis of a common polypropylene formula, high-fluidity PP resin is used as a matrix; POE, small-particle-size talcum powder and medium-particle-size aluminum powder are added for modification and cooperate with a compatilizer, the dispersing agent, the scratch-resistant agent and the lubricant to prepare the spraying-free material with high fluidity andscratch resistance, so that the product meets the appearance requirements of high gloss and metallic silvery color and has the advantages of high quality, low cost, safety, environmental friendlinessand the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a modified polypropylene material, in particular to a metal silver-colored modified polypropylene material with high fluidity, scratch resistance and spray-free metal for vehicles. Background technique [0002] Modified polypropylene (PP resin) is one of the commonly used materials in the automotive field. Polypropylene with gorgeous and customizable appearance will be popular in the market when it is used in automobiles. Spraying technology is one of the common methods in the appearance processing of polypropylene plastics for vehicles. Spraying can make the material have a variety of colors and high-gloss appearance effects, and can realize customized processing. However, the current spraying process also has limitations: 1. The on-site operating environment is not up to standard, which may easily cause product pellets; 2. There are differences in the compatibility betw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L23/08C08L51/06C08L83/04C08K13/02C08K3/34C08K3/08C08K5/20
CPCC08L23/14C08K2201/005C08L2205/035C08K2003/0812C08L23/0815C08L51/06C08L83/04C08K13/02C08K3/34C08K3/08C08K5/20
Inventor 潘叶寒李文斌
Owner NINGBO TAIYONG AUTOMOTIVE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com