Wall base paper and preparation method thereof

A base paper and wall technology, applied in pulp beating method, special paper, paper, etc., to achieve the effect of good non-hydrophobicity, good water resistance, and avoid wall mold

Pending Publication Date: 2020-09-08
ZIBO OU MU SPECIAL PAPER
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The technical problem to be solved by the present invention is to provide a wall base paper and its preparation method in view of the above-mentioned deficiencies in the prior art. The wall base paper is waterproof and breathable, has excellent stretchability, and adheres to wallpaper or latex paint Strong, not prone to the problem of wallpaper curling and falling off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiments 1 to 5 are specific embodiments of a method for preparing a wall base paper of the present invention, wherein embodiment 1 is the best embodiment.

[0034] Softwood pine pulp, Canadian Moon brand bleached softwood pulp;

[0035] Hardwood Acacia pulp, Indonesia Elephant brand bleached hardwood pulp;

[0036] Polyester fibers 2~4D (1~5mm, 10~14mm, 15~20mm, 21~30mm) are all produced by Linyi Jinjiang Industry and Trade Co., Ltd.;

[0037] Wet strength agent PAE, produced by Dongying Huaxing Chemical Plant;

[0038]Water repellant is TL204E-4 low-density polyethylene wax emulsion produced by Longkou Yijiu Chemical Technology Co., Ltd., light color translucent emulsion, solid content 35±1%, pH value 7.0~9.0, average particle size ≦0.1μm;

[0039] The sizing agent is an acrylate emulsion, which is a special emulsion for Mixstar 28#-1 special paper produced by Handan Restar Latex Technology Co., Ltd. Chemical properties: water-based acrylate copolymer emulsion wi...

Embodiment 2

[0048] The preparation method of the wall base paper of the present embodiment adopts the following steps:

[0049] 1) Bottom paper: Weigh coniferous pine pulp and hardwood acacia pulp by weight, disintegrate and beat; add polyester fiber, water repellent and wet strength agent PAE, mix, disintegrate, beat, and beat 30°SR; add water to adjust the slurry concentration to 3% by mass, spray from the paper machine headbox to the wire, press and dewater in the press section, and dry in the dryer section to obtain the bottom paper; among which, the speed of the paper machine headbox 80~100m / min, press section pressure 450KN / m, dryer section dryer temperature 95℃;

[0050] 2) Sizing: Immerse the backing paper in the acrylate emulsion on the sizing coating machine, and the immersion temperature is 23°C to obtain the backing paper after sizing;

[0051] 3) Post-treatment: drying the backing paper after sizing at 170°C in an oven, calendering, calendering pressure 195kN, calendering te...

Embodiment 3

[0053] The preparation method of the wall base paper of the present embodiment adopts the following steps:

[0054] 1) Bottom paper: Weigh coniferous pine pulp and hardwood acacia pulp by weight, disintegrate and beat; add polyester fiber, water repellent and wet strength agent PAE, mix, disintegrate, beat, and beat Degree 28°SR; add water to adjust the slurry concentration to 2.8% by mass, spray from the paper machine headbox to the wire, press and dewater in the press section, and dry in the dryer section to obtain the bottom paper; among which, the speed of the paper machine headbox 80~100m / min, press section pressure 400KN / m, dryer section dryer temperature 90℃;

[0055] 2) Sizing: Immerse the backing paper in the acrylate emulsion on the sizing coating machine, and the dipping temperature is 22°C to obtain the backing paper after sizing;

[0056] 3) Post-treatment: drying the backing paper in an oven at 160~180℃, calendering, calendering pressure 205kN, calendering tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses wall base paper and a preparation method thereof, and belongs to the field of special paper. The wall base paper is prepared from the following raw materials in parts by weight: 30-50 parts of softwood pulp, 40-60 parts of hardwood pulp, 10-15 parts of polyester fibers, 1-5 parts of a water repellent agent, 10-25 parts of a sizing agent and 1-4 parts of a wet strength agentPAE. The preparation method comprises the following steps: 1) preparing backing paper: weighing coniferous pine wood pulp and hardwood pulp in parts by weight; adding polyester fibers, a water repellent agent and a wet strength agent PAE, mixing, repulping and pulping with the pulping degree of 20-40 degrees SR, adding water to adjust the pulp concentration to be 2.5%-3% in percentage by mass, sparying the pulp to a net through a pulp flowing box of a paper machine, performing squeezing dehydration i through a squeezing part, drying through a drying part, and obtaining backing paper; 2) sizing; and 3) post-processing. The wall base paper has the advantages that the wall base paper is waterproof, breathable and excellent in flexibility, the wall base paper can be firmly adhered to wallpaper, and thus the problem of edge curling and falling of the wallpaper can be solved.

Description

technical field [0001] The invention belongs to the field of special paper, in particular to a wall base paper and a preparation method thereof. Background technique [0002] So far, the wall decoration materials used in the market are mostly latex paint and wallpaper. After half a year of use, ordinary latex paint will crack due to the brittle nature of the putty under the latex paint. The wallpaper only solves part of the problem in terms of appearance, and cannot play the role of crack resistance, and because the surface of the wallpaper is made of PVC, PVC is a special material of plastic products, which has completely airtight performance, so this kind of product is in the air humidity and humidity. If the difference is too obvious, it is easy to crack or even mold on the edge. Over time, defects such as yellowing, curling, and cracking of the wallpaper make the decoration effect poor and the service life insufficient. Since the main component of the paper base of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/20D21H21/16D21H21/20D21B1/34D21D1/02D21F11/00D21H23/22D21H25/06D21G1/00
CPCD21B1/345D21D1/02D21F11/00D21G1/00D21H21/16D21H21/20D21H23/22D21H25/06D21H27/20
Inventor 李安东李文海李建峰尚永强贾宝玉王强张志礼
Owner ZIBO OU MU SPECIAL PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap