Non-magnetic hard alloy for instrument shaft and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cemented carbide, non-magnetic technology, applied in the field of non-magnetic cemented carbide for instrument shafts and its preparation, can solve the problems of limited use range, interference of measurement accuracy, not durable, etc., and achieve a wide range of use and stable work. The effect of good sex and long working hours
Active Publication Date: 2020-07-10
江西中孚硬质合金股份有限公司
View PDF11 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The instrument transmission shaft is mainly made of steel, and its main defect is low hardness, not durable and because it is a magnetic material, its measurement accuracy is disturbed and affected in the widespread electromagnetic environment, and the scope of use is limited.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0038] This embodiment takes the total weight of 100kg as an example for illustration:
[0045] Mo powder requirements: Fsss particle size: 1-2u;
[0046] Step 2, mixing the above raw materials, and then adding a wet grinding agent for wet grinding (such as alcohol);
[0047] Step 3, sieving;
[0048] Step 4, after drying, sieve again;
[0049] Step 5, adding a molding agent for mixing;
[0050] Step 6, extrusion molding;
[0051] Step 7, get rid of forming agent;
[0052] Step 8, sintering;
[0053] Step 9, physical testing; check whether the magnetic force, void, density, strength, and hardness o...
Embodiment 2
[0062] This embodiment is basically the same as Embodiment 1, except that MoC powder is used instead of Mo powder.
Embodiment 3
[0064] The present embodiment is basically the same as embodiment 1, and the difference is that the raw materials taken are:
[0065]
[0066]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
density
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a non-magnetic hard alloy for instrument shaft and a preparation method thereof. The hard alloy is prepared from the raw materials in percentage by weight: 86.5 % of WC powder,1.6 % of W powder, 11 % of Ni powder, 0.4 % to 0.6 % of Cr3C2 powder and 0.3 % to 0.5 % of Mo powder or MoC powder. The preparation method comprises the steps of raw material weighing, wet grinding,sieving, screening after drying, mixing with a molding agent, extrusion molding, molding agent removing, sintering, physical detecting, shape inspection to obtain products and processing to obtain theinstrument shaft. According to the non-magnetic hard alloy, the requirements of hardness of the instrument shaft can be met, magnetism is further avoided, thus an instrument can resist electromagnetic interference, the working stability is good, and working can also be conducted normally without being affected in the presence environment of surrounding large electric magnetic field.
Description
technical field [0001] The invention relates to a hard alloy material, in particular to a nonmagnetic hard alloy for an instrument shaft and a preparation method thereof. Background technique [0002] The instrument transmission shaft is mainly made of steel, and its main defect is low hardness, not durable and because it is a magnetic material, its measurement accuracy is disturbed and affected in the widespread electromagnetic environment, and the scope of use is limited. . [0003] Cemented carbide material is an alloy material made of hard compound of refractory metal and bonding metal through powder metallurgy process. Cemented carbide has a series of excellent properties such as high hardness, wear resistance, good strength and toughness, heat resistance and corrosion resistance, especially its high hardness and wear resistance, which basically remain unchanged even at a temperature of 500°C , It still has high hardness at 1000 °C. Therefore, cemented carbide materi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more