A kind of covalent bond type alkali-free accelerator and preparation method thereof

A technology of covalent bond and accelerator, applied in the field of covalent bond type alkali-free accelerator and its preparation, can solve the problem of short service life of alkali-free accelerator, shorten the setting time, promote the consumption of gypsum, The effect of reducing the chance of collision

Active Publication Date: 2021-09-28
JIANGSU SOBUTE NEW MATERIALS +2
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the shortcomings of the existing non-alkali quick-setting agent such as short service life, the invention provides a covalent bond type non-alkali quick-setting agent and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of covalent bond type alkali-free accelerator and preparation method thereof
  • A kind of covalent bond type alkali-free accelerator and preparation method thereof
  • A kind of covalent bond type alkali-free accelerator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The preparation of covalent bond type non-alkali quick-setting agent comprises the following steps:

[0029] (1) Add 4g of 200-300 mesh polyaluminum sulfate and 1g of nanometer γ-alumina to 90g of 95wt% ethanol aqueous solution, and then ultrasonically disperse for 1h to obtain a uniformly dispersed suspension; then add 5g of 1wt% completely hydrolyzed γ-methacryloxypropyltrimethoxysilane ethanol solution; under the protection of nitrogen, stirred and reacted at 80°C for 24h, then centrifuged, washed with ethanol for 3 times, and finally dried in vacuum at 60°C to obtain the inorganic compound Point A.

[0030] (2) Mix 20 g of dimethyl diallyl ammonium chloride, 25 g of acrylic acid and 54.8 g of water uniformly, then add 0.2 g of ammonium persulfate and mix uniformly to obtain organic component B.

[0031] (3) Mix 40g of inorganic component A, 5g of diethanolamine, 3g of oxalic acid and 39.75g of water evenly, heat to 60°C, then add 12g of organic component B and 0.25...

Embodiment 2

[0033] The preparation of covalent bond type non-alkali quick-setting agent comprises the following steps:

[0034] (1) Add 4.9g of 200-300mesh polyaluminum sulfate and 0.1g of nanometer γ-alumina to 91g of 95wt% ethanol aqueous solution, and then ultrasonically disperse for 1 hour to obtain a uniformly dispersed suspension; then add 4g of 3wt% completely Hydrolyzed γ-methacryloxypropyltrimethoxysilane ethanol solution; under the protection of nitrogen, stirred and reacted at 80°C for 24h, then centrifuged, washed with ethanol for 3 times, and finally dried in vacuum at 60°C to obtain Unit A.

[0035] (2) Mix 25g dimethyl diallyl ammonium chloride, 20g acrylic acid and 53.8g water uniformly, then add 1.2g sodium persulfate and mix uniformly to obtain organic component B.

[0036] (3) Mix 50g of inorganic component A, 10g of triethanolamine, 1g of lactic acid and 23.65g of water evenly, heat to 80°C, then add 15g of organic component B and 0.35g of catechol respectively, keep ...

Embodiment 3

[0038] The preparation of covalent bond type non-alkali quick-setting agent comprises the following steps:

[0039] (1) Add 4g of 200-300 mesh polyaluminum sulfate and 1g of nanometer γ-alumina to 90.5g of 95wt% ethanol aqueous solution, and then ultrasonically disperse for 1 hour to obtain a uniformly dispersed suspension; then add 4.5g of 2wt% completely Hydrolyzed γ-methacryloxypropyltrimethoxysilane ethanol solution; under the protection of nitrogen, stirred and reacted at 80°C for 24h, then centrifuged, washed with ethanol for 3 times, and finally dried in vacuum at 60°C to obtain Unit A.

[0040] (2) Mix 22g of dimethyl diallyl ammonium chloride, 23g of acrylic acid and 54g of water uniformly, then add 1g of potassium persulfate and mix uniformly to obtain organic component B.

[0041] (3) Mix 50g of inorganic component A, 10g of triethanolamine, 1g of lactic acid and 23.65g of water evenly, heat to 80°C, then add 15g of organic component B and 0.35g of catechol respect...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a covalent bond type alkali-free quick-setting agent and a preparation method thereof. The alkali-free quick-setting agent of the present invention is composed of the following components by mass percentage: 40-50% inorganic component A, 5-10% alcohol amine, 1-3% organic acid, 12-15% organic component B , 0.25-0.35% catechol, the balance is water, and the inorganic component A is prepared in proportion by 200-300 mesh polyaluminum sulfate, nanometer γ-alumina, silane coupling agent solution, and 95wt% ethanol aqueous solution Formed; the organic component B is prepared in proportion from dimethyl diallyl ammonium chloride, acrylic acid, and initiator water. The invention has long service life and good construction performance; the introduced organic components have high charge density and suitable molecular weight, and can bond and precipitate with calcium ions in cement, thereby promoting the consumption of gypsum, increasing the hydration rate of C3A, shortening the The setting time of the product.

Description

technical field [0001] The invention belongs to the technical field of concrete admixtures, in particular to a covalent bond type alkali-free accelerator and a preparation method thereof. Background technique [0002] Accelerator is a concrete admixture that makes cement or concrete set and harden quickly. Its main function is to increase the thickness of the first spraying of shotcrete, shorten the interval between the second spraying, and improve the early strength of concrete at the same time, so as to provide support resistance in time. It has been widely used in modern underground engineering, mining engineering, plugging and emergency rescue Wait for the project. [0003] Alkali-free accelerators have little effect on the strength of concrete in the later stage, and are becoming the main direction of accelerator development. Alkali-free accelerators with aluminum sulfate as the main component are easy to obtain raw materials and simple preparation processes. The main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/42C04B103/12
CPCC04B40/0046C04B2103/12C04B22/148C04B22/06C04B24/42C04B24/026C04B24/122C04B24/06C04B24/2652C04B24/02
Inventor 洪锦祥张小磊王伟乔敏赵爽曾鲁平
Owner JIANGSU SOBUTE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com