Adhesive for optical grating label and preparation method thereof

A modulation method and adhesive technology, applied in the direction of adhesives, adhesive types, polymer adhesive additives, etc., can solve the problems of easy powder agglomeration, signal transmission interference, etc., and achieve low cost, high bonding strength, The effect of high degree of acetalization

Inactive Publication Date: 2020-06-12
安徽点浩商标科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The inorganic adhesives and their preparation and application methods in the above patents have the following disadvantages: Usually, the method of adding powder to organic matter has the phenomenon that the powder is easy to agglomerate, which will seriously interfere with signal transmission

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An adhesive for grating marks, made of the following raw materials by weight: 20kg of polyvinyl butyral resin, 9kg of aldehyde and ketone resin, 80kg of ethanol, 18kg of n-butanol, 8kg of formaldehyde solution, 4kg of melamine and o-phthalic acid Dibutyl diformate 24kg.

[0027] Wherein, the mass fraction of the formaldehyde aqueous solution is 40%.

[0028] Wherein, the preparation method of the polyvinyl butyral resin is as follows: take 500 mass parts of polyvinyl alcohol-n-butyraldehyde aqueous emulsion and 100 mass parts of an organic acid aqueous solution with a concentration of 2.5% by mass, and feed them at 2950 The flow rate of parts by mass / h and 590 parts by weight / h is simultaneously and continuously added to the high-shear mixer, so that polyvinyl alcohol and n-butyraldehyde are mixed at a shear rate of 50S-1 to 150S-1 and a shear force of 50Pa to 150Pa , temperature 30°C-45°C, organic acid catalyzed conditions, mixed and reacted for 10min-20min; the react...

Embodiment 2

[0035] An adhesive for grating marks, made from the following raw materials by weight: 22kg of polyvinyl butyral resin, 9kg of aldehyde and ketone resin, 78kg of ethanol, 19kg of n-butanol, 10kg of formaldehyde solution, 5kg of melamine and o-phthalic acid Dibutyl diformate 22kg.

[0036] Wherein, the mass fraction of the formaldehyde aqueous solution is 42%.

[0037] A modulation method of grating marking adhesive, comprising the following steps:

[0038] S1: Quantitatively weighed according to the formula ratio, the raw materials include 22kg of polyvinyl butyral resin, 9kg of aldehyde and ketone resin, 78kg of ethanol, 19kg of n-butanol, 10kg of formaldehyde solution, 5kg of melamine and dibutyl phthalate 22kg, wherein the polyvinyl butyral resin has a rotational viscosity of 90mPa·s at 30°C in a 10% ethanol solution;

[0039] S2: Mix the formaldehyde aqueous solution and melamine, adjust the pH value to 8, then heat to 80°C for 60 minutes, then add dibutyl phthalate, and...

Embodiment 3

[0043] An adhesive for grating marks, made of the following raw materials by weight: 20kg of polyvinyl butyral resin, 8kg of aldehyde and ketone resin, 82kg of ethanol, 18kg of n-butanol, 8kg of formaldehyde solution, 5kg of melamine and o-phenyl Dibutyl diformate 22kg.

[0044] Wherein, the mass fraction of the formaldehyde aqueous solution is 43%.

[0045] A modulation method of grating marking adhesive, comprising the following steps:

[0046] S1: Quantitatively weighed according to the formula ratio, the raw materials include 20kg of polyvinyl butyral resin, 8kg of aldehyde and ketone resin, 82kg of ethanol, 18kg of n-butanol, 8kg of formaldehyde solution, 5kg of melamine and dibutyl phthalate 22kg, wherein the polyvinyl butyral resin has a rotational viscosity of 90mPa·s in a 10% ethanol solution with a mass fraction of 30°C;

[0047] S2: Mix the formaldehyde aqueous solution and melamine, adjust the pH value to 8, then heat to 80°C for 60 minutes, then add dibutyl phth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses an adhesive for an optical grating label and a preparation method of the adhesive, and relates to the technical field of adhesives. The adhesive is prepared from the followingraw materials in parts by weight. The adhesive is prepared from polyvinyl butyral resin, aldehyde ketone resin, ethanol, n-butyl alcohol, a formaldehyde aqueous solution, melamine and dibutyl phthalate. The preparation method of the adhesive comprises the following steps: weighing quantitative raw materials according to a formula ratio; uniformly mixing a formaldehyde aqueous solution with melamine, then heating, stirring and cooling the mixture to obtain a curing agent; uniformly mixing polyvinyl butyral resin, aldehyde ketone resin, ethanol and n-butyl alcohol until the components are completely dissolved to obtain an adhesive stock solution, and finally slowly mixing the obtained curing agent with the adhesive stock solution to obtain the adhesive. The invention has the advantages of low cost, moderate viscosity, high bonding strength, safety and environmental protection, simple and feasible preparation method, and is beneficial to simplifying the assembly process, improving the signal transmission efficiency and reducing the production cost.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an adhesive for grating marks and a preparation method thereof. Background technique [0002] The scale grating is a measurement feedback device that uses the optical principle of the grating. It can be widely used in equipment such as IC, electronic assembly, special machines, laser cutting, optical detection, PCB detection inspection, printing, scanning, cameras and scientific instruments. With the expansion of the scope of use, more and more people pay attention to adhesives with special properties, such as conductive glue that conducts electricity, and heat-conducting glue that conducts heat and so on. [0003] After searching, the Chinese patent application number is CN201811042099.6, which discloses an inorganic adhesive and its preparation and application method, including the following parts by mass: water glass: 100 parts; silicon phosphate: 1-15 parts, Sodium alumina...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J129/14C09J161/02C09J11/06C09J11/08C08G12/32C08F8/28C08F16/06
CPCC08F8/28C08G12/32C08L2205/02C08L2205/03C09J11/06C09J11/08C09J129/14C08L61/02C08L61/28C08K5/12C08F16/06
Inventor 袁以千
Owner 安徽点浩商标科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap