Polyphenyl ether composite material and preparation method thereof

A composite material and polyphenylene ether technology, applied in the field of polyphenylene ether composite materials and their preparation, can solve the problems that polyphenylene ether materials cannot satisfy fluidity, mechanical and mechanical properties, heat resistance, stability, etc. Large-scale industrial application, simple process, excellent thermodynamic performance

Pending Publication Date: 2020-04-28
江苏沃特特种材料制造有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a polyphenylene ether composite material, which aims to solve the technical problem that the existing polyphenylene ether materials cannot simultaneously satisfy excellent fluidity, mechanical properties, heat resistance, stability and other characteristics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphenyl ether composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] Correspondingly, an embodiment of the present invention also provides a method for preparing a polyphenylene ether composite material, comprising the following steps:

[0045] S10. Mixing the dried polyphenylene ether, liquid crystal polyester resin and filler to obtain a mixture;

[0046] S20. After the mixture is melt-kneaded, extruded and granulated to obtain a polyphenylene ether composite material.

[0047] The preparation method of the polyphenylene ether composite material provided in the embodiment of the present invention is to mix the dried polyphenylene ether, liquid crystal polyester resin and filler, melt and knead, and then extrude and granulate to obtain a polyphenylene ether composite material. Material. The embodiment of the present invention contains polyphenylene ether composite materials such as polyphenylene ether, liquid crystal polyester resin and fillers. Through the interaction between the components, the polyphenylene ether composite material ...

Embodiment 1

[0062] 65 parts of polyphenylene ether, 5 parts of wholly aromatic liquid crystal polyester resin (Jiangsu Water Special Material Manufacturing Co., Ltd.), and 30 parts of glass fiber were dried at 130° C. for 6 hours. Put the dried polyphenylene ether, liquid crystal polyester resin and glass fiber into an automatic mixer to mix evenly, then put them into a twin-screw extruder for melting and mixing, and then produce polyphenylene ether through extrusion, drawing, cooling, and granulation Composite material.

Embodiment 2

[0064] 60 parts of polyphenylene ether, 10 parts of wholly aromatic liquid crystal polyester resin (Jiangsu Water Special Material Manufacturing Co., Ltd.), and 30 parts of glass fiber were dried at 130° C. for 6 hours. Put the dried polyphenylene ether, liquid crystal polyester resin and glass fiber into an automatic mixer to mix evenly, then put them into a twin-screw extruder for melting and mixing, and then produce polyphenylene ether through extrusion, drawing, cooling, and granulation Composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of polymer composite materials, and particularly relates to a polyphenyl ether composite material. The polyphenyl ether composite material comprises 50-70parts of polyphenyl ether, 3-20 parts of liquid crystal polyester and 10-30 parts of filler. Through the combined action of the components of the polyphenyl ether, the liquid crystal polyester and thefiller, the flowability and the moldability of the polyphenyl ether composite material are improved, the mechanical property and the thermodynamic property are improved, and the polyphenyl ether composite material can be widely applied to the aspects of electronic appliances, automobiles, household appliances, office equipment, industrial machinery and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer composite materials, and in particular relates to a polyphenylene ether composite material and a preparation method thereof. Background technique [0002] Polyphenylene oxide (PPO) is one of the world's five general-purpose engineering plastics. It has the advantages of high rigidity, high heat resistance, flame retardant, high strength and excellent electrical properties. In addition, PPO also has the advantages of wear resistance, non-toxicity and pollution resistance. The dielectric constant and dielectric loss of PPO are one of the smallest varieties among engineering plastics, and they are hardly affected by temperature and humidity. However, polyphenylene ether is similar to Newtonian fluid, has poor fluidity, viscosity is sensitive to temperature, and is easy to decompose. Therefore, the processing and molding performance of polyphenylene ether is extremely poor, and pure polyphenylene e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L71/12C08L67/00C08K7/14
CPCC08L71/12C08L2201/08
Inventor 金东植周小宇刘彬孟华
Owner 江苏沃特特种材料制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap